Field emission from nonaligned zinc oxide nanowires

被引：18
|
作者：
Zhang, GM [1 ]
Zhang, QF [1 ]
Pei, Y [1 ]
Chen, LA [1 ]
机构：
[1] Peking Univ, Sch Elect Engn & Comp Sci, Dept Elect, Beijing 100871, Peoples R China
来源：
VACUUM | 2004年 / 77卷 / 01期
基金：
中国国家自然科学基金;
关键词：
zinc oxide nanowire; vapor-phase transport process; field emission;
D O I：
10.1016/j.vacuum.2004.06.005
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Zinc oxide (ZnO) nanowires with an average diameter of 15 nm were grown using a vapor phase transport process. Field emission was achieved from these nanowires in spite of their random orientation. The electric field for the extraction of a 10 muA/cm(2) current density was measured to range from 4.4 to 5.0 V/mum, and that for a 1 mA/cm(2) current density from 7.6 to 8.7 V/mum, depending on whether the sample was submitted to a heat treatment. The results exhibit the potential application of ZnO nanowires as field emitters in future flat panel displays. (C) 2004 Elsevier Ltd. All rights reserved.
引用
收藏
页码：53 / 56
页数：4
相关论文
共 50 条
  • [41] From zinc nanowires to zinc oxide nanowires: a low substrate-temperature approach
    Liu, JG
    Zhang, ZJ
    Su, X
    Zhao, Y
    JOURNAL OF PHYSICS D-APPLIED PHYSICS, 2005, 38 (07) : 1068 - 1071
  • [42] Zinc oxide nanowires
    Cui, Jingbiao
    MATERIALS CHARACTERIZATION, 2012, 64 : 43 - 52
  • [43] Field emission properties of discretely synthesized tungsten oxide nanowires
    Furubayashi, Masaki
    Nagato, Keisuke
    Moritani, Hiroki
    Hamaguchi, Tetsuya
    Nakao, Masayuki
    MICROELECTRONIC ENGINEERING, 2010, 87 (5-8) : 1594 - 1596
  • [44] Synthesis, characterization and field emission properties of tin oxide nanowires
    Rikka, Vallabha Rao
    Sameera, I.
    Bhatia, Ravi
    Prasad, V.
    MATERIALS CHEMISTRY AND PHYSICS, 2015, 166 : 26 - 30
  • [45] Improving field emission properties of GaN nanowires by oxide coating
    Tang, Cen-Cun
    Xu, Xue-Wen
    Hu, Long
    Li, Yang-Xian
    APPLIED PHYSICS LETTERS, 2009, 94 (24)
  • [46] Field emission from zinc oxide nanowire arrays grown directly from brass
    Xiao, Jing
    Zhang, Gengmin
    Bai, Xin
    Wu, Yue
    Zhang, Wei
    Zhao, Xingyu
    Guo, Dengzhu
    PHYSICA E-LOW-DIMENSIONAL SYSTEMS & NANOSTRUCTURES, 2008, 41 (02): : 309 - 314
  • [47] Field-emission enhancement of molybdenum oxide nanowires with nanoprotrusions
    Khademi, Ali
    Azimirad, Rouhollah
    Nien, Yung-Tang
    Moshfegh, Alireza Z.
    JOURNAL OF NANOPARTICLE RESEARCH, 2011, 13 (01) : 115 - 125
  • [48] Field-emission enhancement of molybdenum oxide nanowires with nanoprotrusions
    Ali Khademi
    Rouhollah Azimirad
    Yung-Tang Nien
    Alireza Z. Moshfegh
    Journal of Nanoparticle Research, 2011, 13 : 115 - 125
  • [49] Flexible Field Emission Devices Based on Barium Oxide Nanowires
    Cui, Yunkang
    Chen, Jing
    Zhang, Xiaobing
    Lei, Wei
    Di, Yunsong
    Wang, Qilong
    JOURNAL OF DISPLAY TECHNOLOGY, 2016, 12 (05): : 466 - 471
  • [50] Efficient field emission from tetrapod-like zinc oxide nanoneedles
    Yu, K
    Zhang, YS
    Xu, RL
    Ouyang, SX
    Li, DM
    Luo, LQ
    Zhu, ZQ
    Ma, J
    Xie, SJ
    Han, SH
    Geng, HR
    MATERIALS LETTERS, 2005, 59 (14-15) : 1866 - 1870
12345