Tribological properties of a-C/Cr(N) coatings in micro-and nano-scales

被引：22
|
作者：
Zhang, P. [1 ]
Wang, L. [1 ]
Nie, X. [1 ]
机构：
[1] Univ Windsor, Windsor, ON N9B 3P4, Canada
来源：
SURFACE & COATINGS TECHNOLOGY | 2007年 / 201卷 / 9-11期
基金：
加拿大自然科学与工程研究理事会;
关键词：
coatings; tribology; nanoindentation; nanowear; nanotribology;
D O I：
10.1016/j.surfcoat.2006.07.220
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
This research was involved with comparison study of tribological properties of a-C/Cr(N) multilayered coatings in micro-and nano-scales. The aC/Cr(N) coatings were deposited on Si wafers and M2 steel substrates by unbalanced magnetron sputtering of one Cr and two C targets. Cross-section TEM analysis was used to determine the layer periodicity of the coatings. Nanoindentation was used to measure hardness (H) and elastic modulus (E), and also perform nanowear tests. Pin-on-disc tribological tests were conducted to evaluate tribological properties of the coatings in micro-scales. HI E, H-3 / E-2, and h(f)/h(max) values were calculated for predication of wear performance of the coatings. It was found that the ranking of coating wear resistance was consistent to the order of H / E, H-3 / E-2, and h(f)/h(max) values. The coating with a periodicity of 4 nm had the highest hardness and the best wear resistance in both nano-and micro-scales. (C) 2006 Elsevier B.V. All rights reserved.
引用
收藏
页码：5176 / 5181
页数：6
相关论文
共 50 条
  • [21] Optimized a-C coatings by doping with zirconium for tribological properties and machining performance
    Kao, W. H.
    DIAMOND AND RELATED MATERIALS, 2007, 16 (11) : 1896 - 1904
  • [22] Tribological properties of a-C : N and a-C films prepared by shielded arc ion plating
    Tajima, N
    Saze, H
    Sugimura, H
    Takai, O
    VACUUM, 2000, 59 (2-3) : 567 - 573
  • [23] The nature of the frictional force at the macro-, micro-, and nano-scales
    Esteban Broitman
    Friction, 2014, 2 : 40 - 46
  • [24] Micro- and Nano-Scales Three-Dimensional Characterisation of Softwood
    Patera, Alessandra
    Bonnin, Anne
    Mokso, Rajmund
    JOURNAL OF IMAGING, 2021, 7 (12)
  • [25] Influences of ceramic mating balls on the tribological properties of Cr/a-C coatings with low chromium content in water lubrication
    Wang, Qianzhi
    Zhou, Fei
    Ding, Xiangdong
    Zhou, Zhifeng
    Zhang, Wenjun
    Li, Lawrence Kwok-Yan
    Lee, Shuit-Tong
    WEAR, 2013, 303 (1-2) : 354 - 360
  • [26] Improving tribological properties and machining performance of a-C coatings by doping with titanium
    W. H. Kao
    Y. L. Su
    S. H. Yao
    Journal of Materials Engineering and Performance, 2006, 15 : 525 - 534
  • [27] Improving tribological properties and machining performance of a-C coatings by doping with titanium
    Kao, W. H.
    Su, Y. L.
    Yao, S. H.
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2006, 15 (05) : 525 - 534
  • [28] Structure, mechanical and tribological properties of Ti-doped and Cr-doped a-C:H:SiOx coatings
    Grenadyorov, A. S.
    Solovyev, A. A.
    Oskirko, V. O.
    Oskomov, K. V.
    Semenov, V. A.
    Sypchenko, V. S.
    Saraev, A. A.
    VACUUM, 2024, 219
  • [29] Mechanical properties and Raman spectra of a-C:H and a-C:H:N coatings
    Vyskocil, J
    Siroky, P
    Vorlicek, V
    Perina, V
    DIAMOND AND RELATED MATERIALS, 1996, 5 (3-5) : 466 - 470
  • [30] Tribological and electrochemical properties of Cr-Si-C-N coatings in artificial seawater
    Wu, Zhiwei
    Zhou, Fei
    Ma, Qiang
    Wang, Qianzhi
    Zhou, Zhifeng
    Li, Lawrence Kwok-Yan
    RSC ADVANCES, 2016, 6 (80): : 76724 - 76735
12345