Tribological properties of a-C/Cr(N) coatings in micro-and nano-scales

被引：22
|
作者：
Zhang, P. [1 ]
Wang, L. [1 ]
Nie, X. [1 ]
机构：
[1] Univ Windsor, Windsor, ON N9B 3P4, Canada
来源：
SURFACE & COATINGS TECHNOLOGY | 2007年 / 201卷 / 9-11期
基金：
加拿大自然科学与工程研究理事会;
关键词：
coatings; tribology; nanoindentation; nanowear; nanotribology;
D O I：
10.1016/j.surfcoat.2006.07.220
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
This research was involved with comparison study of tribological properties of a-C/Cr(N) multilayered coatings in micro-and nano-scales. The aC/Cr(N) coatings were deposited on Si wafers and M2 steel substrates by unbalanced magnetron sputtering of one Cr and two C targets. Cross-section TEM analysis was used to determine the layer periodicity of the coatings. Nanoindentation was used to measure hardness (H) and elastic modulus (E), and also perform nanowear tests. Pin-on-disc tribological tests were conducted to evaluate tribological properties of the coatings in micro-scales. HI E, H-3 / E-2, and h(f)/h(max) values were calculated for predication of wear performance of the coatings. It was found that the ranking of coating wear resistance was consistent to the order of H / E, H-3 / E-2, and h(f)/h(max) values. The coating with a periodicity of 4 nm had the highest hardness and the best wear resistance in both nano-and micro-scales. (C) 2006 Elsevier B.V. All rights reserved.
引用
收藏
页码：5176 / 5181
页数：6
相关论文
共 50 条
  • [1] Electric current-assisted manipulation of liquid metals using a stylus at micro-and nano-scales
    Shastri, Vijayendra
    Majumder, Sukanya
    Ashok, Anuj
    Roy, Kaustav
    Pratap, Rudra
    Kumar, Praveen
    NANOTECHNOLOGY, 2023, 34 (10)
  • [2] Electroanalysis in micro- and nano-scales
    Li, Chang Ming
    Hu, Weihua
    JOURNAL OF ELECTROANALYTICAL CHEMISTRY, 2013, 688 : 20 - 31
  • [3] Diamondlike nanocomposite a-C:H:Cr Coatings: Structure, mechanical, and tribological properties
    Khrushchov M.M.
    Atamanov M.V.
    Marchenko E.A.
    Petrzhik M.I.
    Levin I.S.
    Bulletin of the Russian Academy of Sciences: Physics, 2014, 78 (10) : 1007 - 1014
  • [4] Structure and water-lubricated tribological properties of Cr/a-C coatings with different Cr contents
    Wang, Qianzhi
    Zhou, Fei
    Ding, Xiangdong
    Zhou, Zhifeng
    Wang, Chundong
    Zhang, Wenjun
    Li, Lawrence Kwok-Yan
    Lee, Shuit-Tong
    TRIBOLOGY INTERNATIONAL, 2013, 67 : 104 - 115
  • [5] Recent development on vibration and stability of pipes conveying fluid: from macro-scale to micro-and nano-scales
    Wang, Lin
    Kuang, Youdi
    Huang, Yuying
    Ni, Qiao
    Guti Lixue Xuebao/Acta Mechanica Solida Sinica, 2010, 31 (05): : 481 - 495
  • [6] Tribological properties of hard a-C:H:F coatings
    Jaoul, C.
    Dublanche-Tixier, C.
    Jarry, O.
    Tristant, P.
    Lavoute, J. P.
    Kilman, L.
    Colas, M.
    Laborde, E.
    Ageorges, H.
    SURFACE & COATINGS TECHNOLOGY, 2013, 237 : 328 - 332
  • [7] Effect of tribological media on tribological properties of multilayer Cr(N)/C(DLC) coatings
    Wang, L.
    Nie, X.
    Lukitsch, M. J.
    Jiang, J. C.
    Cheng, Y. T.
    SURFACE & COATINGS TECHNOLOGY, 2006, 201 (07): : 4341 - 4347
  • [8] Tribological behavior and frictional fatigue damage peculiarities in thin a-C and a-C:N coatings
    Albagachiev, A. Yu
    Tokarev, D. A.
    Khrushchov, M. M.
    Marchenko, E. A.
    Antonova, O. S.
    24TH INTERNATIONAL CONFERENCE ON VACUUM TECHNIQUE AND TECHNOLOGY, 2017, 872
  • [9] Tribological behavior of aluminum micro-and nano-composites
    Rohatgi P.
    Menezes P.
    Mazzei T.
    Lovell M.
    International Journal of Aerospace Innovations, 2011, 3 (03) : 153 - 162
  • [10] Optimized a-C:Wx% coatings with enhanced tribological properties and improved micro-drilling performance
    Kao, W. H.
    SURFACE & COATINGS TECHNOLOGY, 2007, 201 (16-17): : 7392 - 7400
12345