Comparative Study on Thermal Fatigue Behavior of Two Hot Work Die Steels

被引：7
|
作者：
Hu, Zhiqiang [1 ,2 ]
Wang, Kaikun [2 ]
机构：
[1] Suqian Univ, Suqian 223800, Peoples R China
[2] Univ Sci & Technol Beijing, Beijing 100089, Peoples R China
来源：
METALLOGRAPHY MICROSTRUCTURE AND ANALYSIS | 2022年 / 11卷 / 03期
关键词：
Hot work die steel; Thermal fatigue behavior; Fatigue cack; Thermal fatigue life; TOOL STEELS; CARBIDE;
D O I：
10.1007/s13632-022-00854-x
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
The thermal fatigue behavior of 5CrNiMoV and 5CrNiMoVNb steel was compared. The results show that length of the main thermal fatigue crack for 5CrNiMoV and 5CrNiMoVNb steel are, respectively, 184.47 and 104.06 mu m after 2000 thermal fatigue cycles. The fatigue crack initiation and propagation rate in 5CrNiMoVNb steel are significantly lower than that in 5CrNiMoV steel. Besides, a mixed way of transgranular and intergranular crack propagation occurs in 5CrNiMoV steel, while only transgranular propagation occurs in 5CrNiMoVNb steel. Due to high content of small carbide particles and the strong inhibitory effect on dislocation movement and microstructure coarsening, 5CrNiMoVNb steel has better microstructure stability, hardness and toughness. Based on the simplified thermal fatigue life model, it indicates that the thermal fatigue life is dependent on the stresses corresponding to the limit temperatures of their cycles. Therefore, the 5CrNiMoVNb steel with higher room temperature and high temperature stress shows longer thermal fatigue life.
引用
收藏
页码：425 / 433
页数：9
相关论文
共 50 条
  • [21] WEAR TESTING OF HOT WORK DIE STEELS
    ASTON, JL
    HOPKINS, AD
    KIRKHAM, KE
    METALLURGIA AND METAL FORMING, 1972, 39 (02): : 46 - &
  • [22] High temperature friction and wear properties of two hot work die steels
    Bai Z.-X.
    Zuo P.-P.
    Ji J.
    Wu X.-C.
    Gongcheng Kexue Xuebao/Chinese Journal of Engineering, 2019, 41 (07): : 906 - 913
  • [23] THERMAL FATIGUE OF TOOL STEELS FOR HOT WORKING
    ROUSSEAU, D
    RIEGERT, JP
    SERAPHIN, L
    TRICOT, R
    REVUE DE METALLURGIE-CAHIERS D INFORMATIONS TECHNIQUES, 1975, 72 (12): : 875 - 889
  • [24] Effect of Y-Ce complex modification on thermal fatigue behavior of high Cr cast hot working die steels
    Jiang, QC
    Liang, HQ
    Sui, HL
    ISIJ INTERNATIONAL, 2004, 44 (10) : 1762 - 1766
  • [25] THE INFLUENCE OF LASER SURFACE ALLOYING ON THE THERMAL FATIGUE RESISTANCE OF HOT WORK TOOL STEELS
    Jonda, E.
    Brytan, Z.
    Labisz, K.
    Drygala, A.
    ARCHIVES OF METALLURGY AND MATERIALS, 2016, 61 (03) : 963 - 968
  • [26] Thermal fatigue behavior of HHD hot work tool steel with structures
    Ma, Y.
    Wang, H.
    Chai, X.
    Zhuang, J.
    Li, J.
    Tong, J.
    Bhushan, B.
    MATERIALWISSENSCHAFT UND WERKSTOFFTECHNIK, 2018, 49 (12) : 1494 - 1502
  • [27] Microstructures and thermal fatigue behavior of Cr-Ni-Mo hot work die steel modified by rare earth
    Guan, QF
    Jiang, QC
    Fang, JR
    Jiang, H
    ISIJ INTERNATIONAL, 2003, 43 (05) : 784 - 789
  • [28] CRACK RESISTANCE OF HOT-WORK DIE STEELS
    BARNBY, JT
    BAYLISS, RN
    METAL FORMING, 1969, 36 (06): : 157 - &
  • [29] Hot working of two AISI 304 steels: a comparative study
    El Wahabi, M
    Cabrera, JM
    Prado, JM
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2003, 343 (1-2): : 116 - 125
  • [30] Marked effect of die temperature on the thermal fatigue cracking of die steels
    Wallace, JF
    Schwam, D
    Birceanu, S
    DIE CASTING ENGINEER, 2002, 46 (03): : 36 - 39
12345