Comparative Study on Thermal Fatigue Behavior of Two Hot Work Die Steels

被引：7
|
作者：
Hu, Zhiqiang [1 ,2 ]
Wang, Kaikun [2 ]
机构：
[1] Suqian Univ, Suqian 223800, Peoples R China
[2] Univ Sci & Technol Beijing, Beijing 100089, Peoples R China
来源：
METALLOGRAPHY MICROSTRUCTURE AND ANALYSIS | 2022年 / 11卷 / 03期
关键词：
Hot work die steel; Thermal fatigue behavior; Fatigue cack; Thermal fatigue life; TOOL STEELS; CARBIDE;
D O I：
10.1007/s13632-022-00854-x
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
The thermal fatigue behavior of 5CrNiMoV and 5CrNiMoVNb steel was compared. The results show that length of the main thermal fatigue crack for 5CrNiMoV and 5CrNiMoVNb steel are, respectively, 184.47 and 104.06 mu m after 2000 thermal fatigue cycles. The fatigue crack initiation and propagation rate in 5CrNiMoVNb steel are significantly lower than that in 5CrNiMoV steel. Besides, a mixed way of transgranular and intergranular crack propagation occurs in 5CrNiMoV steel, while only transgranular propagation occurs in 5CrNiMoVNb steel. Due to high content of small carbide particles and the strong inhibitory effect on dislocation movement and microstructure coarsening, 5CrNiMoVNb steel has better microstructure stability, hardness and toughness. Based on the simplified thermal fatigue life model, it indicates that the thermal fatigue life is dependent on the stresses corresponding to the limit temperatures of their cycles. Therefore, the 5CrNiMoVNb steel with higher room temperature and high temperature stress shows longer thermal fatigue life.
引用
收藏
页码：425 / 433
页数：9
相关论文
共 50 条
  • [11] Effect of mechanical vibration on the microstructure and thermal fatigue behavior of cast hot work die steel
    Y. H. Liang
    Y. G. Zhao
    Q. D. Qin
    E. Y. Shang
    Q. C. Jiang
    Journal of Materials Science, 2006, 41 : 2529 - 2532
  • [12] Simulation and evaluation of thermal fatigue cracking of hot work tool steels
    Persson, A
    Hogmark, S
    Bergström, J
    INTERNATIONAL JOURNAL OF FATIGUE, 2004, 26 (10) : 1095 - 1107
  • [13] Thermal fatigue cracking of surface engineered hot work tool steels
    Persson, A
    Hogmark, S
    Bergström, J
    SURFACE & COATINGS TECHNOLOGY, 2005, 191 (2-3): : 216 - 227
  • [14] Thermal fatigue characteristics of the hot die steels treated with PVD and CVD and their application
    Hihara, M
    JOURNAL OF JAPANESE SOCIETY OF TRIBOLOGISTS, 1996, 41 (11) : 917 - 922
  • [15] Thermal fatigue behavior of new type high-Cr cast hot work die steel
    Jiang, QC
    Sui, HL
    Guan, QF
    ISIJ INTERNATIONAL, 2004, 44 (06) : 1103 - 1107
  • [16] Comparative study on wear of hot-working die steels
    Zhang Qiu-yang
    Wang Shu-qi
    Wang Lan
    2013 INTERNATIONAL CONFERENCE ON PROCESS EQUIPMENT, MECHATRONICS ENGINEERING AND MATERIAL SCIENCE, 2013, 331 : 559 - 562
  • [17] Effect of aluminizing and oxidation on the thermal fatigue damage of hot work tool steels for high pressure die casting applications
    Salem, M.
    Le Roux, S.
    Dour, G.
    Lamesle, P.
    Choquet, K.
    Rezai-Aria, F.
    INTERNATIONAL JOURNAL OF FATIGUE, 2019, 119 : 126 - 138
  • [18] TEMPERATURE-DEPENDENCE OF FATIGUE CRACK-PROPAGATION IN HOT WORK DIE STEELS
    SCHUCHTAR, E
    THEORETICAL AND APPLIED FRACTURE MECHANICS, 1988, 9 (02) : 141 - 143
  • [19] Hot Deformation Behavior of Four Steels: A Comparative Study
    Menapace, C.
    Sartori, N.
    Pellizzari, M.
    Straffelini, G.
    JOURNAL OF ENGINEERING MATERIALS AND TECHNOLOGY-TRANSACTIONS OF THE ASME, 2018, 140 (02):
  • [20] INFLUENCE OF MICROSTRUCTURE ON THERMAL FATIGUE RESISTANCE OF HOT-WORK TOOL STEELS
    CAJNER, F
    STROJARSTVO, 1991, 33 (5-6): : 289 - 296
12345