Low-temperature Sintering of Yttria-stabilized Zirconia Using Bismuth-Vanadium Oxide as a Sintering Aid at 800 °C

被引：4
|
作者：
Nagao, Masahiro [1 ]
Kobayashi, Kazuyo [1 ]
Hibino, Takashi [1 ]
机构：
[1] Nagoya Univ, Grad Sch Environm Studies, Chikusa Ku, Nagoya, Aichi 4648601, Japan
来源：
CHEMISTRY LETTERS | 2014年 / 43卷 / 12期
关键词：
DOPED ZIRCONIA; ION CONDUCTORS; ELECTROLYTE; CONDUCTIVITY; COPPER;
D O I：
10.1246/cl.140712
中图分类号：
O6 [化学];
学科分类号：
0703 ;
摘要：
The effect of the addition of copper-doped bismuth-vanadium oxide to yttria-stabilized zirconia (YSZ) on the sinterability and electrical conductivity, especially in reducing atmospheres, has been investigated. When Bi2Cu0.1V0.9O5.35 was used as a sintering aid, the sintering temperature could be reduced to 800 degrees C, whereas the conventional sintering process requires temperatures above 1300 degrees C. Although the conductivity of YSZ with 1.5 mol % Bi2Cu0.1V0.9O5.35 was slightly lower than that of pure YSZ sintered at 1300 degrees C, no Po-2 dependence was observed under reducing conditions (e.g., Po-2 = 10(-5)-10(-2)4 atm), which indicates that the electrolyte is applicable to solid-oxide fuel cells.
引用
收藏
页码：1887 / 1889
页数：3
相关论文
共 50 条
  • [21] Flash sintering of yttria-stabilized zirconia: Fundamental understanding and applications
    Ren, Ke
    Liu, Jinling
    Wang, Yiguang
    SCRIPTA MATERIALIA, 2020, 187 : 371 - 378
  • [22] Change in pore structure of yttria-stabilized zirconia during sintering
    S. V. Gabelkov
    R. V. Tarasov
    A. G. Mironova
    Powder Metallurgy and Metal Ceramics, 2011, 50
  • [23] Direct microwave sintering of yttria-stabilized zirconia at 2.45 GHz
    Israel Ceramic and Silicate Inst, Haifa, Israel
    J Eur Ceram Soc, 12 (2067-2072):
  • [24] POWDER PROPERTIES AND SINTERING CHARACTERISTICS OF ULTRAFINE YTTRIA-STABILIZED ZIRCONIA
    HAAG, RM
    RHODES, WH
    AMERICAN CERAMIC SOCIETY BULLETIN, 1969, 48 (04): : 391 - &
  • [25] LOW-TEMPERATURE THERMOLUMINESCENCE STUDIES OF THE NANOCRYSTALLINE YTTRIA-STABILIZED ZIRCONIA
    Stanovyi, O.
    Kutovyy, S.
    Morozov, Yu.
    Naumenko, A.
    Dmitruk, I.
    Borodyanska, A.
    UKRAINIAN JOURNAL OF PHYSICS, 2016, 61 (06): : 489 - 494
  • [26] Low-Temperature Superionic Conductivity in Strained Yttria-Stabilized Zirconia
    Sillassen, Michael
    Eklund, Per
    Pryds, Nini
    Johnson, Erik
    Helmersson, Ulf
    Bottiger, Jorgen
    ADVANCED FUNCTIONAL MATERIALS, 2010, 20 (13) : 2071 - 2076
  • [27] Effect of iron oxide coloring agent on the sintering behavior of dental yttria-stabilized zirconia
    Kao, Ching-Ti
    Tuan, Wei-Hsing
    Liu, Che-Yuan
    Chen, Shih-Chieh
    CERAMICS INTERNATIONAL, 2018, 44 (05) : 4689 - 4693
  • [28] Electrospun yttria-stabilized zirconia nanofibers for low-temperature solid oxide fuel cells
    Koo, Ja Yang
    Lim, Yonghyun
    Kim, Young Beom
    Byun, Doyoung
    Lee, Wonyoung
    INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 2017, 42 (24) : 15903 - 15907
  • [29] Processing of porous yttria-stabilized zirconia tapes: Influence of starch content and sintering temperature
    Albano, Maria P.
    Garrido, Liliana B.
    Plucknett, Kevin
    Genova, Luis A.
    CERAMICS INTERNATIONAL, 2009, 35 (05) : 1783 - 1791
  • [30] Influence of starch content and sintering temperature on the microstructure of porous yttria-stabilized zirconia tapes
    Albano, Maria P.
    Garrido, Liliana B.
    Plucknett, Kevin
    Genova, Luis A.
    JOURNAL OF MATERIALS SCIENCE, 2009, 44 (10) : 2581 - 2589
12345