Low-temperature Sintering of Yttria-stabilized Zirconia Using Bismuth-Vanadium Oxide as a Sintering Aid at 800 °C

被引：4
|
作者：
Nagao, Masahiro [1 ]
Kobayashi, Kazuyo [1 ]
Hibino, Takashi [1 ]
机构：
[1] Nagoya Univ, Grad Sch Environm Studies, Chikusa Ku, Nagoya, Aichi 4648601, Japan
来源：
CHEMISTRY LETTERS | 2014年 / 43卷 / 12期
关键词：
DOPED ZIRCONIA; ION CONDUCTORS; ELECTROLYTE; CONDUCTIVITY; COPPER;
D O I：
10.1246/cl.140712
中图分类号：
O6 [化学];
学科分类号：
0703 ;
摘要：
The effect of the addition of copper-doped bismuth-vanadium oxide to yttria-stabilized zirconia (YSZ) on the sinterability and electrical conductivity, especially in reducing atmospheres, has been investigated. When Bi2Cu0.1V0.9O5.35 was used as a sintering aid, the sintering temperature could be reduced to 800 degrees C, whereas the conventional sintering process requires temperatures above 1300 degrees C. Although the conductivity of YSZ with 1.5 mol % Bi2Cu0.1V0.9O5.35 was slightly lower than that of pure YSZ sintered at 1300 degrees C, no Po-2 dependence was observed under reducing conditions (e.g., Po-2 = 10(-5)-10(-2)4 atm), which indicates that the electrolyte is applicable to solid-oxide fuel cells.
引用
收藏
页码：1887 / 1889
页数：3
相关论文
共 50 条
  • [11] Sintering kinetic window for yttria-stabilized cubic zirconia
    Pouchly, Vaclav
    Maca, Karel
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2016, 36 (12) : 2931 - 2936
  • [12] Molybdenum Oxide and Nickel Nitrate as Cooperative Sintering Aids for Yttria-Stabilized Zirconia
    Hunt, Clay
    Allemeier, John Kyle
    Driscoll, David
    Weisenstein, Adam
    Sofie, Stephen
    MATERIALS, 2020, 13 (12)
  • [13] Effect of sintering temperature on compressive strength of porous yttria-stabilized zirconia ceramics
    Hu, LiangFa
    Wang, Chang-An
    CERAMICS INTERNATIONAL, 2010, 36 (05) : 1697 - 1701
  • [14] Effect of Sintering Temperature on Crack Growth Resistance Characteristics of Yttria-Stabilized Zirconia
    Kulyk, V
    Duriagina, Z.
    Vasyliv, B.
    Kovbasiuk, T.
    Lyutyy, P.
    Vira, V.
    Vavrukh, V.
    ACTA PHYSICA POLONICA A, 2022, 141 (04) : 323 - 327
  • [15] Yttria-stabilized zirconia–alumina composite sintering temperature effect on thermal diffusivity
    Kamil Dychtoń
    Marcin Drajewicz
    Maciej Pytel
    Paweł Rokicki
    Andrzej Nowotnik
    Journal of Thermal Analysis and Calorimetry, 2016, 126 : 1 - 7
  • [16] Effect of yttria-stabilized zirconia sintering temperature on mixed potential sensor performance
    Sekhar, Praveen K.
    Brosha, Eric L.
    Mukundan, Rangachary
    Nelson, Mark A.
    Toracco, Dennis
    Garzon, Fernando H.
    SOLID STATE IONICS, 2010, 181 (19-20) : 947 - 953
  • [17] INFLUENCE OF SINTERING TEMPERATURE ON TRANSLUCENCY OF YTTRIA-STABILIZED ZIRCONIA FOR DENTAL CROWN APPLICATIONS
    Hao, Chin Chuin
    Muchtar, Andanastuti
    Azhari, Che Husna
    Razali, Masfueh
    Aboras, Mohamed
    JURNAL TEKNOLOGI, 2016, 78 (11-3): : 13 - 18
  • [18] Densification of 8 mol% yttria-stabilized zirconia at low temperature by flash sintering technique for solid oxide fuel cells
    Zhang, Jing
    Wang, Zhenhua
    Jiang, Taizhi
    Xie, Liqiang
    Sui, Chao
    Ren, Rongzheng
    Qiao, Jinshuo
    Sun, Kening
    CERAMICS INTERNATIONAL, 2017, 43 (16) : 14037 - 14043
  • [19] Tough Yttria-Stabilized Zirconia Ceramic by Low-Temperature Spark Plasma Sintering of Long-Term Stored Nanopowders
    Bezdorozhev, Oleksii
    Borodianska, Hanna
    Sakka, Yoshio
    Vasylkiv, Oleg
    JOURNAL OF NANOSCIENCE AND NANOTECHNOLOGY, 2011, 11 (09) : 7901 - 7909
  • [20] CHANGE IN PORE STRUCTURE OF YTTRIA-STABILIZED ZIRCONIA DURING SINTERING
    Gabelkov, S. V.
    Tarasov, R. V.
    Mironova, A. G.
    POWDER METALLURGY AND METAL CERAMICS, 2011, 50 (3-4) : 151 - 156
12345