Effect of Ag Content on the Microstructure and Crystallization of Coupled Eutectic Growth in Directionally Solidified Al-Cu-Ag Alloys

被引:7
|
作者
Du, Dafan [1 ]
Fautrelle, Yves [2 ]
Dong, Anping [1 ]
Shu, Da [1 ]
Zhu, Guoliang [1 ]
Sun, Baode [1 ]
Li, Xi [2 ,3 ]
机构
[1] Shanghai Jiao Tong Univ, Shanghai Key Lab Adv High Temp Mat & Precis Formi, BP 75, Shanghai 200240, Peoples R China
[2] PHELMA, CNRS, G INP, SIMAP EPM Madylam, F-38402 St Martin Dheres, France
[3] Shanghai Univ, State Key Lab Adv Special Steel, Shanghai 200072, Peoples R China
基金
中国博士后科学基金; 中国国家自然科学基金;
关键词
PLANAR INTERFACE; STABILITY; SIMULATIONS; ENERGIES; LAMELLAR;
D O I
10.1007/s11661-018-4799-5
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
A series of coupled eutectic growths along the univariant eutectic groove in the ternary Al-Cu-Ag alloy was studied to investigate the effect of Ag on the microstructure and crystallization of directionally solidified Al-Cu-Ag alloys. The results indicated that the eutectic morphology and orientation relationship (OR) between eutectic phases were modified as the Ag content in the Al-Cu-Ag alloys increased. At a lower growth velocity (R <= 1 mu m/s), a banded structure formed and the interlamellar spacing decreased with the increasing Ag content. At a higher growth velocity (R >= 3 mu m/s), the eutectic cell spacing decreased with increasing Ag content. Increasing the Ag content in the Al-Cu-Ag alloys enhanced the enrichment of the Ag solute in the liquid ahead of the quenched liquid/solid interface. In addition, increasing the Ag content in the Al-Cu-Ag alloys promoted the transformation from a "Beta 6" OR to an "Alpha 4" OR between eutectic phases. Modifications of the eutectic morphology and the OR during directional solidification were attributed to the enrichment of Ag content at the solid/liquid interface and the changes in the interfacial energy due to the increase in Ag solubility in the alpha-Al phase. (C) The Minerals, Metals & Materials Society and ASM International 2018
引用
收藏
页码:4735 / 4747
页数:13
相关论文
共 50 条
  • [21] Density and viscosity of liquid ternary Al-Cu-Ag alloys
    Brillo, Juergen
    Brooks, Rob
    Egry, Ivan
    Quested, Peter
    HIGH TEMPERATURES-HIGH PRESSURES, 2008, 37 (04) : 371 - 381
  • [22] Influence of gravity on the microstructure of directionally solidified Ag-Si eutectic alloy
    Aoi, I
    Yoshida, M
    Fukunaga, H
    Nakae, H
    MATERIALS TRANSACTIONS JIM, 1999, 40 (01): : 27 - 33
  • [23] Precipitation of the θ′(Al2Cu) phase in Al-Cu-Ag alloys
    Rosalie, Julian M.
    Bourgeois, Laure
    Muddle, Barrington C.
    LIGHT METALS 2012, 2012, : 307 - 312
  • [24] THE MICROSTRUCTURE OF UNIDIRECTIONALLY SOLIDIFIED AG-GE EUTECTIC ALLOYS
    SUK, MJ
    AHN, IS
    MOON, IH
    JOURNAL OF MATERIALS SCIENCE, 1986, 21 (02) : 451 - 456
  • [25] Microstructure Evolution of Directionally Solidified Al-Cu Alloys
    Qu, Min
    Liu, Lin
    Zhao, Ming
    Liu, Fengbin
    He, Guangping
    ADVANCES IN SUPERALLOYS, PTS 1 AND 2, 2011, 146-147 : 729 - +
  • [26] Microstructure formation in directionally solidified Al-Cu alloys
    Liu, S
    Lee, JH
    Walker, H
    Trivedi, RK
    LIGHT METALS 2003, 2003, : 1017 - 1022
  • [27] Directionally Solidified Al–Cu–Si–Fe Quaternary Eutectic Alloys
    U. Büyük
    S. Engin
    H. Kaya
    E. Çadırlı
    N. Maraşlı
    Physics of Metals and Metallography, 2020, 121 : 78 - 83
  • [28] Effect of a high magnetic field on the growth of ternary Al-Cu-Ag alloys during directional solidification
    Du, Dafan
    Fautrelle, Yves
    Ren, Zhongming
    Moreau, Rene
    Li, Xi
    ACTA MATERIALIA, 2016, 121 : 240 - 256
  • [29] Surface tension of liquid Al-Cu-Ag ternary alloys
    Brillo, J.
    Plevachuk, Y.
    Egry, I.
    JOURNAL OF MATERIALS SCIENCE, 2010, 45 (19) : 5150 - 5157
  • [30] Effect of Heterophase Interfaces on Microstructure and Crystallographic Texture Evolution During Rolling of Directionally Solidified Ag-Cu Eutectic Alloy
    Li, Jiehua
    Li, Jun
    Renk, Oliver
    Pippan, Reinhard
    Ghosh, Pradipta
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2020, 51 (01): : 368 - 379