The Oxide-Scale Growth and Failure on an Fe-16Cr Alloy in the Presence of Compressive Stress

被引：6
|
作者：
Zhou, C. H. [1 ]
Liu, A. L. [1 ]
Ma, H. T. [2 ]
Wang, L. [2 ]
机构：
[1] Heilongjiang Univ Sci & Technol, Sch Mat Sci & Engn, Harbin 150022, Peoples R China
[2] Dalian Univ Technol, Sch Mat Sci & Engn, Dalian 116085, Peoples R China
来源：
OXIDATION OF METALS | 2016年 / 85卷 / 5-6期
基金：
中国国家自然科学基金;
关键词：
High temperature oxidation; Compressive stress; Kinetics; Failure; Fe-Cr alloy; FE-CR ALLOYS; INITIAL OXIDATION; BEHAVIOR; STEEL; ADHERENCE; TENSILE; NI;
D O I：
10.1007/s11085-016-9611-6
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
The high temperature oxidation behavior of an Fe-16Cr binary alloy, oxidized under different compressive stresses in air at 900 degrees C, was investigated. Surface and cross-sectional micrographs, observed by scanning electron microscopy, indicated that the resulting morphology of the thermally grown oxide scale depended on the compressive stress. Results showed that oxide scales were infact below 5 MPa stress after 10 h of oxidation. Delamination developed at the outer/inner oxide scale interface in the case of compressive stress above 5 MPa. Growth kinetics measurements revealed that the rate of oxide-scale growth increased by the compressive stress.
引用
收藏
页码：537 / 546
页数：10
相关论文
共 50 条
  • [41] Oxide Scale Development in a Ni-16 Cr-4.5 Al Alloy for Short Exposure Times
    Ury, Nicholas
    Wagner, Annette
    Deodeshmukh, Vinay
    Hayashi, Shigenari
    Ravi, Vilupanur
    JOM, 2021, 73 (12) : 3974 - 3987
  • [42] Oxide Scale Development in a Ni-16 Cr-4.5 Al Alloy for Short Exposure Times
    Nicholas Ury
    Annette Wagner
    Vinay Deodeshmukh
    Shigenari Hayashi
    Vilupanur Ravi
    JOM, 2021, 73 : 3974 - 3987
  • [43] INITIAL FORMATION OF OXIDE NODULES DUE TO GRAIN-GROWTH OF AN FE-18CR ALLOY
    HORIBE, S
    NAKAYAMA, T
    CORROSION SCIENCE, 1975, 15 (09) : 589 - &
  • [44] Influence of Surface Oxide Scale of Fe-Cr Alloy on Tool Lubrication Characteristic during Hot Rolling
    Hidaka, Yasuyoshi
    Iida, Sumio
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 2010, 96 (04): : B16 - B21
  • [45] A KINETIC-STUDY OF THE RELAXATION OF GROWTH STRESS DURING OXIDATION OF A FE-CR-AL ALLOY
    NARDOU, F
    RANAIVONIARIVO, L
    RAYNAUD, P
    BILLY, M
    MATERIALS SCIENCE AND ENGINEERING, 1987, 88 : 241 - 246
  • [46] Deformation and fracture behavior of surface oxide scale on Fe-13Cr alloy in hot-rolling process
    Hidaka, Y.
    Anraku, T.
    Ohtsuka, N.
    HIGH-TEMPERATURE OXIDATION AND CORROSION 2005, 2006, 522-523 : 461 - 468
  • [47] Stress-induced roughness development during oxide scale growth on a metallic alloy for SOFC interconnects
    Saillard, Audric
    Cherkaoui, Mohammed
    El Kadiri, Haitham
    MODELLING AND SIMULATION IN MATERIALS SCIENCE AND ENGINEERING, 2011, 19 (01)
  • [48] Oxide scale formation and stability of Fe-Cr alloy interconnects under dual atmospheres and current flow conditions for SOFCs
    Horita, Teruhisa
    Kishimoto, Haruo
    Yamaji, Katsuhiko
    Xiong, Yueping
    Sakai, Natsuko
    Brito, Manuel E.
    Yokokawa, Harumi
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2006, 153 (11) : A2007 - A2012
  • [49] OBSERVATION ON VOID FORMED IN OXIDE SCALE OF Fe-Cr-Ni ALLOY AT 1073K IN DRY AND HUMID ENVIRONMENTS
    Kaderi, Akbar
    Zainal, Ahmad Zaki Mohd
    Ani, Hanafi
    Othman, Raihan
    IIUM ENGINEERING JOURNAL, 2011, 12 (05): : 69 - 78
  • [50] Growth of α-alumina oxide film in high temperature oxidation of Fe-20Cr-5Al alloy thin strip
    Kongju Natl Univ, Kongju, Korea, Republic of
    Scripta Mater, 8 (1151-1155):
12345