Effect of Pipe Steel Strength on Sulfide Stress Cracking Resistance

被引：1
|
作者：
Kholodnyi, A. A. [1 ]
Matrosov, Yu. I. [1 ]
Kuznechenko, Ya. S. [1 ]
机构：
[1] FGUP IP Bardin TsNIIchermet, Moscow, Russia
来源：
METALLURGIST | 2018年 / 62卷 / 5-6期
关键词：
low-alloy pipe steel; accelerated cooling; rolled plate; sulfide stress cracking; loading factor; yield strength; ultimate strength;
D O I：
10.1007/s11015-018-0691-1
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
Based on test results for low-alloy steel of strength categories X42-X70 the effect is established of loading and strength properties on sulfide stress corrosion (SSC) cracking resistance with uniaxial tension. A favorable effect is demonstrated for a reduction in loading factor and an increase in strength on an increase in steel SSC resistance. The level of steel yield and ultimate strengths providing good SSC resistance is determined.
引用
收藏
页码：541 / 548
页数：8
相关论文
共 50 条
  • [41] Strength effect in stress corrosion cracking of high-strength steel in aqueous solution
    Li, HL
    Gao, KW
    Qiao, LJ
    Wang, YB
    Chu, WY
    CORROSION, 2001, 57 (04) : 295 - 299
  • [42] Strength effect in stress corrosion cracking of high-strength steel in aqueous solution
    Li, HL
    Hui, WJ
    Wang, YB
    Dong, H
    Weng, YQ
    Chu, WY
    ACTA METALLURGICA SINICA, 2001, 37 (05) : 512 - 516
  • [43] Strength effect in stress corrosion cracking of high-strength steel in aqueous solution
    Li, H.
    Hui, W.
    Wang, Y.
    Dong, H.
    Weng, Y.
    Chu, W.
    Jinshu Xuebao/Acta Metallurgica Sinica, 2001, 37 (05): : 512 - 516
  • [44] EFFECT OF MOLYBDENUM ON SULFIDE STRESS CRACKING RESISTANCE OF LOW-ALLOY STEELS
    LIAO, CM
    LEE, JL
    CORROSION, 1994, 50 (09) : 695 - 704
  • [45] Enhancing sulfide stress cracking resistance of a Cu-bearing high strength low alloyed steel through decreasing austenitizing temperature
    Zeng, Tianyi
    Zhang, Qingzhan
    Zhang, Shuzhang
    Zhou, Yong
    Zhao, Yinghui
    Shi, Xianbo
    Yan, Wei
    JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2025, 35 : 2315 - 2327
  • [46] Seabed Temperature and Sulfide Stress Cracking Resistance of Weldable Martensitic 13% Chromium Stainless Steel
    Dent, Philip
    Fowler, Chris
    Walters, Matthew
    Connolly, Brian
    Ueda, Masakatsu
    Amaya, Hisashi
    Takabe, Hideki
    MATERIALS PERFORMANCE, 2014, 53 (05) : 66 - 72
  • [47] A MICROSTRUCTURAL STUDY OF THE SULFIDE STRESS CRACKING RESISTANCE OF A CR-MO-V-B STEEL
    SHEI, SA
    KIM, CD
    CORROSION, 1985, 41 (01) : 12 - 18
  • [48] Experimental investigation on sulfide stress corrosion cracking of 16Mn hydrogen-induced cracking resistance steel
    Li, Ming
    Li, Xiaogang
    Chen, Gang
    Liu, Zhiyong
    Beijing Keji Daxue Xuebao/Journal of University of Science and Technology Beijing, 2007, 29 (03): : 282 - 287
  • [49] EFFECT OF GRIT BLASTING ON THE STRESS-CORROSION CRACKING BEHAVIOR OF LINE PIPE STEEL
    KOCH, GH
    BARLO, TJ
    BERRY, WE
    MATERIALS PERFORMANCE, 1984, 23 (10) : 20 - 23
  • [50] A method for testing pipe steels under the conditions of sulfide stress cracking
    Astaf'ev, VI
    Narushev, VM
    Tetyueva, TV
    MATERIALS SCIENCE, 1999, 35 (04) : 587 - 591
12345