A method for testing pipe steels under the conditions of sulfide stress cracking

被引：0

作者：

Astaf'ev, VI ^{[1
]}

Narushev, VM ^{[1
]}

Tetyueva, TV ^{[1
]}

机构：

[1] Samara State Univ, Samara 443086, Russia

来源：

MATERIALS SCIENCE | 1999年 / 35卷 / 04期

关键词：

D O I：

暂无

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

We propose a testing method for the evaluation of the threshold crack resistance K-Issc of pipe steels under the conditions of sulfide stress corrosion cracking. The values of K-Issc are determined for various casing tubes mode of different types of steel after heat treatment.

引用

页码：587 / 591

页数：5

共 50 条

[1] A method for testing pipe steels under the conditions of sulfide stress cracking
Astaf'ev V.I.
Narushev V.M.
Tetyueva T.V.
Materials Science, 1999, 35 (4) : 587 - 591
[2] ON THE SULFIDE STRESS CRACKING OF LINE PIPE STEELS
TURN, JC
WILDE, BE
TROIANOS, CA
CORROSION, 1983, 39 (09) : 364 - 370
[3] ESTABLISHMENT OF EVALUATION METHOD OF SULFIDE STRESS CRACKING RESISTANCE .2. EFFECTS OF TESTING CONDITIONS ON KISCC FOR SULFIDE STRESS CRACKING
ASAHI, H
TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1986, 72 (13): : 1473 - 1473
[4] Effect of alloying elements on the susceptibility to sulfide stress cracking of line pipe steels
Koh, SU
Yang, BY
Kim, KY
CORROSION, 2004, 60 (03) : 262 - 274
[5] SULFIDE STRESS CRACKING OF NICKEL STEELS
CRAIG, BD
BROWNLEE, JK
BRUNO, TV
CORROSION, 1992, 48 (02) : 90 - 97
[6] EFFECT OF CATHODIC PROTECTION CONDITIONS ON THE STRESS CORROSION CRACKING OF LINE PIPE STEELS.
Kasahara, Komei
Adachi, Haruhiko
Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan, 1983, 69 (14): : 1630 - 1637
[7] Criteria for Accelerated Estimation of Susceptibility of Pipe Steels to Corrosion Cracking Under Oilfield Conditions
Kondrat'ev, S. Yu
Al'khimenko, A. A.
Khar'kov, A. A.
Shvetsov, O., V
Davydov, A. D.
METAL SCIENCE AND HEAT TREATMENT, 2022, 63 (9-10) : 533 - 539
[8] Criteria for Accelerated Estimation of Susceptibility of Pipe Steels to Corrosion Cracking Under Oilfield Conditions
S. Yu. Kondrat’ev
A. A. Al’khimenko
A. A. Khar’kov
O. V. Shvetsov
A. D. Davydov
Metal Science and Heat Treatment, 2022, 63 : 533 - 539
[9] SULFIDE STRESS-CORROSION CRACKING OF LINE PIPE
KIMURA, M
TOTSUKA, N
KURISU, T
AMANO, K
MATSUYAMA, J
NAKAI, Y
CORROSION, 1989, 45 (04) : 340 - 346
[10] Specified pipe fittings susceptible to sulfide stress cracking
Saudi Aramco, Dhahran, Saudi Arabia
Mater Perform, 1 (64-66):

← 1 2 3 4 5 →