Sintering of injection molded M2 high-speed steel

被引：53
|
作者：
Liu, ZY [1 ]
Loh, NH [1 ]
Khor, KA [1 ]
Tor, SB [1 ]
机构：
[1] Nanyang Technol Univ, Sch Mech & Prod Engn, Singapore 639798, Singapore
来源：
MATERIALS LETTERS | 2000年 / 45卷 / 01期
关键词：
powder injection molding; high speed steel; sintering; tool steel; supersolidus liquid phase sintering;
D O I：
10.1016/S0167-577X(00)00070-7
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The sintering of injection molded M2 high speed steel (HSS) was studied. The sintering parameters investigated were: sintering atmosphere, heating rate, sintering temperature and sintering time. Mechanical properties and SEM microstructures were used to determine an optimum sintering schedule. It was found that sintering in vacuum is better than in nitrogen as densification is faster in the former. In vacuum sintering, effective sintering took place in the range 1190-1210 degrees C, whereas in nitrogen atmosphere, effective sintering occurred form 1250 degrees C to 1270 degrees C. A heating rate of 10 degrees C/min is preferred since a higher heating rate of 30 degrees C/min resulted in distortion. Near full density was obtained within 10 min after reaching an optimum sintering temperature of 1210 degrees C. However, the maximum ultimate tensile strength of 752.6 MPa was obtained after 2 h of sintering in a vacuum. (C) 2000 Elsevier Science B.V. All rights reserved.
引用
收藏
页码：32 / 38
页数：7
相关论文
共 50 条
  • [41] Effect of sintering atmosphere and carbon content on the densification and microstructure of laser-sintered M2 high-speed steel powder
    Asgharzadeh, H
    Simchi, A
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2005, 403 (1-2): : 290 - 298
  • [42] Surface modification of M2 high-speed steel by high intense pulsed ion beam
    Li, Yu-Hai
    Xing, Gui-He
    Li, Sheng-Zhi
    Lou, Chang-Sheng
    Yuan, Jin-Wei
    Shenyang Gongye Daxue Xuebao/Journal of Shenyang University of Technology, 2010, 32 (02): : 141 - 145
  • [43] Densification of AISI M2 high speed steel by means of capacitor discharge sintering (CDS)
    Fais, A.
    Maizza, G.
    JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2008, 202 (1-3) : 70 - 75
  • [44] Sintering behavior of NbC based cemented carbides bonded with M2 high speed steel
    Hadian, Amir
    Zamani, Cyrus
    Clemens, Frank Jorg
    CERAMICS INTERNATIONAL, 2019, 45 (07) : 8616 - 8625
  • [45] Processing of AISI M2 high speed steel reinforced with vanadium carbide by solar sintering
    Herranz, G.
    Romero, A.
    de Castro, V.
    Rodriguez, G. P.
    MATERIALS & DESIGN, 2014, 54 : 934 - 946
  • [46] Mechanical alloying of TiC/M2 high speed steel composite powders and sintering investigation
    Liu, ZY
    Loh, NH
    Khor, KA
    Tor, SB
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2001, 311 (1-2): : 13 - 21
  • [47] Densification and microstructural evaluation during laser sintering of M2 high speed steel powder
    Simchi, A
    Asgharzadeh, H
    MATERIALS SCIENCE AND TECHNOLOGY, 2004, 20 (11) : 1462 - 1468
  • [48] The evolution of eutectic carbide in M2 high-speed steel cast-strip
    Zhang, Cai-Dong
    Jiang, Bin
    Yang, Qin
    Ding, Pei-Dao
    Cailiao Rechuli Xuebao/Transactions of Materials and Heat Treatment, 2009, 30 (03): : 107 - 110
  • [49] Precipitation of Secondary Carbides in M2 High-Speed Steel Modified with Titanium diboride
    Chaus, Alexander S.
    Domankova, Maria
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2013, 22 (05) : 1412 - 1420
  • [50] THE STUDY OF CARBIDES IN LASER-SURFACE TREATED M2 HIGH-SPEED STEEL
    SHI, GQ
    DING, PD
    LIU, JL
    LASERS IN ENGINEERING, 1995, 4 (01) : 25 - 31
12345