Sintering of injection molded M2 high-speed steel

被引：53
|
作者：
Liu, ZY [1 ]
Loh, NH [1 ]
Khor, KA [1 ]
Tor, SB [1 ]
机构：
[1] Nanyang Technol Univ, Sch Mech & Prod Engn, Singapore 639798, Singapore
来源：
MATERIALS LETTERS | 2000年 / 45卷 / 01期
关键词：
powder injection molding; high speed steel; sintering; tool steel; supersolidus liquid phase sintering;
D O I：
10.1016/S0167-577X(00)00070-7
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The sintering of injection molded M2 high speed steel (HSS) was studied. The sintering parameters investigated were: sintering atmosphere, heating rate, sintering temperature and sintering time. Mechanical properties and SEM microstructures were used to determine an optimum sintering schedule. It was found that sintering in vacuum is better than in nitrogen as densification is faster in the former. In vacuum sintering, effective sintering took place in the range 1190-1210 degrees C, whereas in nitrogen atmosphere, effective sintering occurred form 1250 degrees C to 1270 degrees C. A heating rate of 10 degrees C/min is preferred since a higher heating rate of 30 degrees C/min resulted in distortion. Near full density was obtained within 10 min after reaching an optimum sintering temperature of 1210 degrees C. However, the maximum ultimate tensile strength of 752.6 MPa was obtained after 2 h of sintering in a vacuum. (C) 2000 Elsevier Science B.V. All rights reserved.
引用
收藏
页码：32 / 38
页数：7
相关论文
共 50 条
  • [21] High temperature deformation behavior of M2 high-speed tool steel
    Ha, Tae Kwon
    Jeong, Hyo Tae
    Jung, Jae Young
    ADVANCES IN NANOMATERIALS AND PROCESSING, PTS 1 AND 2, 2007, 124-126 : 1365 - +
  • [22] INVESTIGATION OF M2 HIGH-SPEED STEEL PRODUCED BY OSPREY PROCESS
    IGHARO, M
    WOOD, JV
    POWDER METALLURGY, 1989, 32 (02) : 124 - 131
  • [23] IMPROVED HEAT-TREATMENT FOR HIGH-SPEED STEEL M2
    CHILD, HC
    PLUMB, SA
    HORTON, SA
    HEAT TREATMENT OF METALS, 1983, 10 (02): : 33 - 38
  • [24] Rapid solidification of M2 high-speed steel by laser melting
    Benyounis, K. Y.
    Fakron, O. M.
    Abboud, J. H.
    MATERIALS & DESIGN, 2009, 30 (03): : 674 - 678
  • [25] FRACTURE BEHAVIOR AND FRACTURE TOUGHNESS OF M2 HIGH-SPEED STEEL
    JOHANSSON, H
    SANDSTROM, R
    MATERIALS SCIENCE AND ENGINEERING, 1978, 36 (02): : 175 - 180
  • [26] Deep cryogenic treatment of AISI M2 high-speed steel
    Pellizzari, M.
    Molinari, A.
    Girardini, L.
    Maldarelli, L.
    International Journal of Microstructure and Materials Properties, 2008, 3 (2-3) : 383 - 390
  • [27] MC complex carbide in AISI M2 high-speed steel
    Serna, M. M.
    Rossi, J. L.
    MATERIALS LETTERS, 2009, 63 (08) : 691 - 693
  • [28] Supersolidus liquid phase sintering of infection molded M2 tool steel
    Myers, N
    German, RM
    ADVANCES IN POWDER METALLURGY & PARTICULATE MATERIALS - 1997, 1997, : 1877 - 1890
  • [29] Selective laser sintering of gas atomized M2 high speed steel powder
    H. J. Niu
    I. T. H. Chang
    Journal of Materials Science, 2000, 35 : 31 - 38
  • [30] Selective laser sintering of gas atomized M2 high speed steel powder
    Niu, HJ
    Chang, ITH
    JOURNAL OF MATERIALS SCIENCE, 2000, 35 (01) : 31 - 38
12345