Sintering of injection molded M2 high-speed steel

被引：53
|
作者：
Liu, ZY [1 ]
Loh, NH [1 ]
Khor, KA [1 ]
Tor, SB [1 ]
机构：
[1] Nanyang Technol Univ, Sch Mech & Prod Engn, Singapore 639798, Singapore
来源：
MATERIALS LETTERS | 2000年 / 45卷 / 01期
关键词：
powder injection molding; high speed steel; sintering; tool steel; supersolidus liquid phase sintering;
D O I：
10.1016/S0167-577X(00)00070-7
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The sintering of injection molded M2 high speed steel (HSS) was studied. The sintering parameters investigated were: sintering atmosphere, heating rate, sintering temperature and sintering time. Mechanical properties and SEM microstructures were used to determine an optimum sintering schedule. It was found that sintering in vacuum is better than in nitrogen as densification is faster in the former. In vacuum sintering, effective sintering took place in the range 1190-1210 degrees C, whereas in nitrogen atmosphere, effective sintering occurred form 1250 degrees C to 1270 degrees C. A heating rate of 10 degrees C/min is preferred since a higher heating rate of 30 degrees C/min resulted in distortion. Near full density was obtained within 10 min after reaching an optimum sintering temperature of 1210 degrees C. However, the maximum ultimate tensile strength of 752.6 MPa was obtained after 2 h of sintering in a vacuum. (C) 2000 Elsevier Science B.V. All rights reserved.
引用
收藏
页码：32 / 38
页数：7
相关论文
共 50 条
  • [1] Microstructure evolution during sintering of injection molded M2 high speed steel
    Liu, ZY
    Loh, NH
    Khor, KA
    Tor, SB
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2000, 293 (1-2): : 46 - 55
  • [2] Sintering and Mechanical Properties of AISI M2 High-Speed Steel Powder Molded at Low Pressures
    Eroglu, S.
    MATERIALS AND MANUFACTURING PROCESSES, 2010, 25 (09) : 1025 - 1029
  • [3] Supersolidus liquid phase sintering of injection molded M2 tool steel
    Myers, NS
    German, RM
    INTERNATIONAL JOURNAL OF POWDER METALLURGY, 1999, 35 (06): : 45 - 51
  • [4] Supersolidus liquid phase sintering of injection molded M2 tool steel
    Myers, Neal S.
    German, Randall M.
    International Journal of Powder Metallurgy (Princeton, New Jersey), 1999, 35 (06): : 45 - 51
  • [5] Computer model for the sintering densification of injection molded M2 tool steel
    German, RM
    INTERNATIONAL JOURNAL OF POWDER METALLURGY, 1999, 35 (04): : 57 - +
  • [6] CRACKING IN M2 HIGH-SPEED STEEL
    SHELTON, PW
    WRONSKI, AS
    METAL SCIENCE, 1983, 17 (11): : 533 - 539
  • [7] SOLIDIFICATION OF M2 HIGH-SPEED STEEL
    BARKALOW, RH
    GOLDSTEIN, JI
    KRAFT, RW
    METALLURGICAL TRANSACTIONS, 1972, 3 (04): : 919 - +
  • [8] THE INFLUENCE OF SINTERING ATMOSPHERE FOR METAL INJECTION MOULDING M2 HIGH SPEED STEEL
    Sauti, R.
    Wahab, N. A.
    Omar, M. A.
    Ahmad, I. N.
    ADVANCED MATERIALS CONFERENCE (AMC 2012), 2014, 879 : 169 - +
  • [9] Injection molding of M2 high speed steel
    RuizRoman, JM
    Candela, N
    Velasco, F
    REVISTA DE METALURGIA, 1996, 32 (06) : 369 - 374
  • [10] STABILITY OF CARBIDES IN M2 HIGH-SPEED STEEL
    VERSACI, RA
    JOURNAL OF MATERIALS SCIENCE LETTERS, 1988, 7 (03) : 273 - 275
12345