THE EFFECTS OF SPECIMEN SIZE ON THE VERY HIGH CYCLE FATIGUE PROPERTIES OF FV520B-I

被引：0
|
作者：
Zhang, Ming [1 ]
Wang, Weiqiang [1 ]
Li, Aiju [2 ]
机构：
[1] Shandong Univ, Sch Mech Engn, Engn & Technol Res Ctr Special Equipment Safety S, Jinan 250100, Shandong, Peoples R China
[2] Shandong Univ, Sch Mat Sci & Engn, Jinan 250100, Shandong, Peoples R China
来源：
PROCEEDINGS OF THE ASME PRESSURE VESSELS AND PIPING CONFERENCE - 2015, VOL 5 | 2015年
关键词：
HIGH-STRENGTH STEELS; NON-METALLIC INCLUSIONS; QUANTITATIVE-EVALUATION; CRACK INITIATION; MECHANISM; PROPAGATION;
D O I：
暂无
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
The authors researched the effects of specimen size on the very high cycle fatigue properties of FV520B-I through ultrasonic fatigue testing. The test results showed that the very high cycle fatigue mechanism was not changed and the fatigue properties declined as the specimen size increased. The S-N curve moved downward and the fatigue life decreased under the same stress level maybe due to the heat effects of large specimens in tests. The fatigue strength and the fatigue life were predicted by relevant models. The prediction of fatigue strength was close to test result, and the prediction of fatigue life was less effective compared with the previous prediction of small size specimen test results.
引用
收藏
页数：6
相关论文
共 50 条
  • [41] Effects of specimen geometry and surface defect on high and very high cycle fatigue of TC17 alloy
    Wu, Han
    Chi, Weiqian
    Xu, Wei
    Wang, Wenjing
    Sun, Chengqi
    ENGINEERING FRACTURE MECHANICS, 2022, 276
  • [42] Fatigue life assessment of the centrifugal compressor impeller with cracks based on the properties of FV520B
    Liu, Chi
    Liu, Shujie
    Gao, Sibo
    Hu, Yawei
    Zhang, Shixin
    Zhang, Hongchao
    ENGINEERING FAILURE ANALYSIS, 2016, 66 : 177 - 186
  • [43] Effect of heat treatments on fatigue properties of FV520B steel using infrared thermography
    Guo, X. (xlguo@dlut.edu.cn), 1600, Chinese Journal of Materials Research (26):
  • [44] Size-effect in Very High Cycle Fatigue: A review
    Tridello, A.
    Niutta, C. Boursier
    Berto, F.
    Paolino, D. S.
    INTERNATIONAL JOURNAL OF FATIGUE, 2021, 153
  • [45] Effects of inclusion size and location on very-high-cycle fatigue behavior for high strength steels
    Lei, Zhengqiang
    Hong, Youshi
    Xie, Jijia
    Sun, Chengqi
    Zhao, Aiguo
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2012, 558 : 234 - 241
  • [46] Specimen size effects on gigacycle fatigue properties of high-strength steel under ultrasonic fatigue testing
    Furuya, Y.
    SCRIPTA MATERIALIA, 2008, 58 (11) : 1014 - 1017
  • [47] Effects of inclusions on the very high cycle fatigue behaviour of steels
    Pineau, Andre
    Forest, Samuel
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2017, 40 (11) : 1694 - 1707
  • [48] Effects of inclusion size and stress ratio on the very-high-cycle fatigue behavior of pearlitic steel
    Cong, Tao
    Qian, Guian
    Zhang, Guanzhen
    Wu, Si
    Pan, Xiangnan
    Du, Leiming
    Liu, Xiaolong
    INTERNATIONAL JOURNAL OF FATIGUE, 2021, 142
  • [49] Research on Fatigue Damage in High-Strength Steel (FV520B) Using Nonlinear Ultrasonic Testing
    Chen, Bingbing
    Wang, Chao
    Wang, Pengfei
    Zheng, Sanlong
    Sun, Weiming
    SHOCK AND VIBRATION, 2020, 2020
  • [50] Effect of surface residual stress and inclusion size on very high cycle fatigue properties of high speed tool steel
    Shimatani, Yuuji
    Shiozawa, Kazuaki
    Nakada, Takehiro
    Yoshimoto, Takashi
    Nihon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A, 2009, 75 (759): : 1598 - 1607
12345