THE EFFECTS OF SPECIMEN SIZE ON THE VERY HIGH CYCLE FATIGUE PROPERTIES OF FV520B-I

被引：0
|
作者：
Zhang, Ming [1 ]
Wang, Weiqiang [1 ]
Li, Aiju [2 ]
机构：
[1] Shandong Univ, Sch Mech Engn, Engn & Technol Res Ctr Special Equipment Safety S, Jinan 250100, Shandong, Peoples R China
[2] Shandong Univ, Sch Mat Sci & Engn, Jinan 250100, Shandong, Peoples R China
来源：
PROCEEDINGS OF THE ASME PRESSURE VESSELS AND PIPING CONFERENCE - 2015, VOL 5 | 2015年
关键词：
HIGH-STRENGTH STEELS; NON-METALLIC INCLUSIONS; QUANTITATIVE-EVALUATION; CRACK INITIATION; MECHANISM; PROPAGATION;
D O I：
暂无
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
The authors researched the effects of specimen size on the very high cycle fatigue properties of FV520B-I through ultrasonic fatigue testing. The test results showed that the very high cycle fatigue mechanism was not changed and the fatigue properties declined as the specimen size increased. The S-N curve moved downward and the fatigue life decreased under the same stress level maybe due to the heat effects of large specimens in tests. The fatigue strength and the fatigue life were predicted by relevant models. The prediction of fatigue strength was close to test result, and the prediction of fatigue life was less effective compared with the previous prediction of small size specimen test results.
引用
收藏
页数：6
相关论文
共 50 条
  • [21] Very high cycle bending fatigue behaviors of FV520B steel under fretting wear
    Ya-nan Song
    Zhi-guo Xing
    Hai-dou Wang
    Peng-fei He
    Bin-shi Xu
    Journal of Materials Research, 2016, 31 : 1748 - 1754
  • [22] Very high cycle bending fatigue behaviors of FV520B steel under fretting wear
    Song, Ya-nan
    Xing, Zhi-guo
    Wang, Hai-dou
    He, Peng-fei
    Xu, Bin-shi
    JOURNAL OF MATERIALS RESEARCH, 2016, 31 (12) : 1748 - 1754
  • [23] Competitive giga-fatigue life analysis owing to surface defect and internal inclusion for FV520B-I
    Wang, Jinlong
    Zhang, Yuanliang
    Liu, Shujie
    Sun, Qingchao
    Lu, Huitian
    INTERNATIONAL JOURNAL OF FATIGUE, 2016, 87 : 203 - 209
  • [24] Effects of Specimen Size and Welded Joints on the Very High Cycle Fatigue Properties of Compressor Blade Steel KMN-I
    Wang, Pengfei
    Wang, Weiqiang
    Zhang, Ming
    Zhou, Qiwen
    Gao, Zengliang
    COATINGS, 2021, 11 (10)
  • [25] Study of the remanufacturing critical threshold and remanufacturability evaluation for FV520B-I blade based on fatigue life and FEA
    Wang Jinlong
    Yu Jing
    Yang Yuxing
    Du Fengming
    Wang Jingsi
    ENGINEERING FAILURE ANALYSIS, 2020, 112
  • [26] FV520B-I在不同介质的疲劳失效分析
    王金龙
    高斯博
    杨宇星
    鲍永杰
    彭文杰
    哈尔滨工程大学学报, 2022, 43 (08) : 1163 - 1168
  • [27] Effects of specimen size on fatigue life of metallic materials in high-cycle and very-high-cycle fatigue regimes
    Sun, C.
    Zhang, X.
    Liu, X.
    Hong, Y.
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2016, 39 (06) : 770 - 779
  • [28] Effect of aging temperature on energy dissipation and high-cycle fatigue properties of FV520B stainless steel
    Yang, Wenping
    Guo, Qiang
    Fan, Junling
    Guo, Xinglin
    Zhao, Yanguang
    ENGINEERING FRACTURE MECHANICS, 2021, 242
  • [29] Notable size effects on very high cycle fatigue properties of high-strength steel
    Furuya, Yoshiyuki
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2011, 528 (15): : 5234 - 5240
  • [30] RESEARCH ON HIGH-CYCLE FATIGUE BEHAVIOR OF FV520B STEEL BASED ON INTRINSIC DISSIPATION
    Guo Qiang
    Guo Xinglin
    Fan Junling
    Wu Chengwei
    ACTA METALLURGICA SINICA, 2015, 51 (04) : 400 - 406
12345