THE EFFECTS OF SPECIMEN SIZE ON THE VERY HIGH CYCLE FATIGUE PROPERTIES OF FV520B-I

被引：0
|
作者：
Zhang, Ming [1 ]
Wang, Weiqiang [1 ]
Li, Aiju [2 ]
机构：
[1] Shandong Univ, Sch Mech Engn, Engn & Technol Res Ctr Special Equipment Safety S, Jinan 250100, Shandong, Peoples R China
[2] Shandong Univ, Sch Mat Sci & Engn, Jinan 250100, Shandong, Peoples R China
来源：
PROCEEDINGS OF THE ASME PRESSURE VESSELS AND PIPING CONFERENCE - 2015, VOL 5 | 2015年
关键词：
HIGH-STRENGTH STEELS; NON-METALLIC INCLUSIONS; QUANTITATIVE-EVALUATION; CRACK INITIATION; MECHANISM; PROPAGATION;
D O I：
暂无
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
The authors researched the effects of specimen size on the very high cycle fatigue properties of FV520B-I through ultrasonic fatigue testing. The test results showed that the very high cycle fatigue mechanism was not changed and the fatigue properties declined as the specimen size increased. The S-N curve moved downward and the fatigue life decreased under the same stress level maybe due to the heat effects of large specimens in tests. The fatigue strength and the fatigue life were predicted by relevant models. The prediction of fatigue strength was close to test result, and the prediction of fatigue life was less effective compared with the previous prediction of small size specimen test results.
引用
收藏
页数：6
相关论文
共 50 条
  • [1] Fatigue behavior and mechanism of FV520B-I welding seams in a very high cycle regime
    Zhang, Ming
    Wang, Weiqiang
    Wang, Pengfei
    Liu, Yan
    Li, Jianfeng
    INTERNATIONAL JOURNAL OF FATIGUE, 2016, 87 : 22 - 37
  • [2] The Fatigue Behavior and Mechanism of Large FV520B-I Specimens in a Very High Cycle Regime
    Zhang, Han
    Zhao, Ya-Fan
    Zhang, Ming
    Li, Meng-Li
    Liu, Long
    Cui, Yu-Liang
    Shang, Xian-Dong
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2024, 33 (02) : 950 - 960
  • [3] The Fatigue Behavior and Mechanism of Large FV520B-I Specimens in a Very High Cycle Regime
    Han Zhang
    Ya-Fan Zhao
    Ming Zhang
    Meng-Li Li
    Long Liu
    Yu-Liang Cui
    Xian-Dong Shang
    Journal of Materials Engineering and Performance, 2024, 33 : 950 - 960
  • [4] The fatigue behavior and mechanism of FV520B-I with large surface roughness in a very high cycle regime
    Zhang, Ming
    Wang, Weiqiang
    Wang, Pengfei
    Liu, Yan
    Li, Jianfeng
    ENGINEERING FAILURE ANALYSIS, 2016, 66 : 432 - 444
  • [5] Fatigue behavior and mechanism of FV520B-I in ultrahigh cycle regime
    Zhang Ming
    Wang Weiqiang
    Wang Pengfei
    Liu Yan
    Li Jianfeng
    20TH EUROPEAN CONFERENCE ON FRACTURE, 2014, 3 : 2035 - 2041
  • [6] Fatigue behavior and mechanism of dog-bone-shaped specimens of FV520B-I in a very high cycle regime
    Zhang, Ming
    Zhang, Han
    Li, Mengli
    Liu, Long
    Wang, Pengfei
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2022, 45 (12) : 3658 - 3676
  • [7] Super-high-cycle fatigue behavior of FV520B-I steel used in impellers
    Sun Q.
    Sun K.
    Shi B.
    Zhang Y.
    Harbin Gongcheng Daxue Xuebao/Journal of Harbin Engineering University, 2019, 40 (12): : 2057 - 2062
  • [8] Fatigue Behavior and Fatigue Life for FV520B-I at Different Loading Frequencies
    Zhao Q.
    Wang J.
    Zhang Y.
    Shen Y.
    Liu S.
    Cailiao Daobao/Materials Review, 2018, 32 (08): : 2837 - 2841and2846
  • [9] A Study of Fatigue Property for FV520B-I at Different Loading Frequencies
    Zhao, Q. C.
    Zhang, Y. L.
    Wang, J. L.
    Shen, Y. H.
    Liu, S. J.
    2017 4TH INTERNATIONAL CONFERENCE ON ADVANCED MATERIALS, MECHANICS AND STRUCTURAL ENGINEERING (4TH AMMSE 2017), 2017, 269
  • [10] Fatigue failure analysis of FV520B-I in different test media
    Wang J.
    Gao S.
    Yang Y.
    Bao Y.
    Peng W.
    Harbin Gongcheng Daxue Xuebao/Journal of Harbin Engineering University, 2022, 43 (08): : 1163 - 1168
12345