Microstructure characterization and mechanical properties of Al-based coating on magnesium alloy prepared by Supersonic Particles Deposition

被引：3
|
作者：
Wang, X. M. [1 ]
Zhu, S. [1 ]
Han, G. F. [1 ]
Chang, Q. [1 ]
机构：
[1] Acad Armored Force Engn, Natl Key Lab Remfg, Beijing 100072, Peoples R China
来源：
INTERNATIONAL FEDERATION FOR HEAT TREATMENT AND SURFACE ENGINEERING (20TH CONGRESS) | 2013年 / 50卷
关键词：
Magnesium alloy; Supersonic particles deposition; Microstructure; Mechanical properties; Formation mechanism;
D O I：
10.1016/j.phpro.2013.11.042
中图分类号：
O414.1 [热力学];
学科分类号：
摘要：
Al-Si coating on the surface of AZ81E magnesium alloy was fabricated by Supersonic Particles Deposition, then microstructure observation, micro-hardness testing, bonding strength measurement and formation mechanism analysis of the deposited coating were accomplished by relative analytical technique, respectively. The results elucidated that Al-Si coating on magnesium alloy surface prepared by Supersonic Particles Deposition was formed via the integrated combination of mechanical bonding and metallurgical bonding. The coating was compacted and its hardness was about 1.8 times to that of the substrate. Average bonding strength of the interface was above 40MPa. (C) 2013 The Authors. Published by Elsevier B.V.
引用
收藏
页码：267 / 271
页数：5
相关论文
共 50 条
  • [41] Microstructure and Mechanical Properties of Cr-SiC Particles-Reinforced Fe-Based Alloy Coating
    Wang, Fu-cheng
    Du, Xiao-dong
    Zhan, Ma-ji
    Lang, Jing-wei
    Zhou, Dan
    Liu, Guang-fu
    Shen, Jian
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2015, 24 (12) : 4673 - 4680
  • [42] Tuning the microstructure and mechanical properties of Al-based amorphous/crystalline composites by addition of Pd
    Gonzalez, S.
    Sort, J.
    Louzguine-Luzgin, D. V.
    Perepezko, J. H.
    Baro, M. D.
    Inoue, A.
    INTERMETALLICS, 2010, 18 (12) : 2377 - 2384
  • [43] Microstructure and Wear Resistance of Graphite/Cu Composite Coating Prepared by Supersonic Laser Deposition
    Wang Jianjun
    Tian Kai
    Chen Zhijun
    Li Bo
    Zhang Gang
    Zhang Qunli
    Yao Jianhua
    CHINESE JOURNAL OF LASERS-ZHONGGUO JIGUANG, 2021, 48 (18):
  • [44] Effects of yttrium on microstructure and mechanical properties of Mg-6Al magnesium alloy
    Ren Wenliang
    Li Quan'an
    Li Jianhong
    Li Kejie
    Zhang Xingyuan
    CHINA FOUNDRY, 2010, 7 (04) : 362 - 366
  • [45] Microstructure and novel properties of nanocrystalline and nanocrystalline alloys prepared in Al-based systems by rapid solidification
    Inoue, A
    Kimura, HM
    Sasamori, K
    Masumoto, T
    SCIENCE REPORTS OF THE RESEARCH INSTITUTES TOHOKU UNIVERSITY SERIES A-PHYSICS CHEMISTRY AND METALLURGY, 1996, 42 (01): : 165 - 178
  • [46] Microstructure and mechanical properties of Mg-6Al magnesium alloy with yttrium and neodymium
    Chen Jun
    China Foundry, 2009, 6 (02) : 124 - 128
  • [47] Influence of Ca on microstructure and mechanical properties of Mg-8%Al magnesium alloy
    Sun, Jing
    Li, Hong
    Guo, Quan-Ying
    Mao, Ping-Li
    Liu, Zheng
    Shenyang Gongye Daxue Xuebao/Journal of Shenyang University of Technology, 2011, 33 (02): : 125 - 128
  • [48] Effects of yttrium on microstructure and mechanical properties of Mg-6Al magnesium alloy
    Ren Wenliang 1
    2. School of Material Science and Engineering
    China Foundry, 2010, 7 (04) : 362 - 366
  • [49] Investigation of Mechanical Properties and Microstructure of Non-Commercial Magnesium Alloy Prepared by Extrusion and ECAP
    Zemkova, M.
    Bohlen, J.
    Capek, J.
    Hadzima, B.
    Kral, R.
    Minarik, P.
    ACTA PHYSICA POLONICA A, 2018, 134 (03) : 905 - 908
  • [50] Fabrication, microstructure and mechanical properties of Al-Fe intermetallic particle reinforced Al-based composites
    Xue, Yang
    Shen, Rujuan
    Ni, Song
    Song, Min
    Xiao, Daihong
    JOURNAL OF ALLOYS AND COMPOUNDS, 2015, 618 : 537 - 544
12345