Mechanical properties of copper-coated carbon foams

被引：28
|
作者：
Almajali, M. [1 ]
Lafdi, K. [1 ]
Prodhomme, P. H. [2 ]
Ochoa, Ozden [3 ]
机构：
[1] Univ Dayton, Dayton, OH 45469 USA
[2] Arts ET Metiers Paris Tech, F-51006 Chalons Sur Marne, France
[3] Texas A&M Univ, College Stn, TX 77843 USA
来源：
CARBON | 2010年 / 48卷 / 05期
关键词：
D O I：
10.1016/j.carbon.2009.12.060
中图分类号：
O64 [物理化学（理论化学）、化学物理学];
学科分类号：
070304 ; 081704 ;
摘要：
The mechanical properties of copper-coated carbon foam were investigated Reticulated vitreous carbon cell type foams, with 97% porosity and 10 ppi pore size, were electroplated with copper for different penods of time to obtain coatings with different thicknesses and foams with different porosities Compression tests were performed to determine the Young's modulus and the plateau stress The copper electroplating technique improved these two proper-ties, with the modulus increasing from 4 S to 8 6 MPa for the sample electroplated for 40 min and the plateau stress increasing from 54 to 171 kPa for the foam coated for 80 min The relationships between the measured proper-ties and the copper weight ratio were deter-mined (C) 2010 Elsevier Ltd All rights reserved
引用
收藏
页码：1604 / 1608
页数：5
相关论文
共 50 条
  • [41] Synergistic enhancing effect for mechanical and electrical properties of tungsten copper composites using spark plasma infiltrating sintering of copper-coated graphene
    Wenge Chen
    Longlong Dong
    Jiaojiao Wang
    Ying Zuo
    Shuxin Ren
    Yongqing Fu
    Scientific Reports, 7
  • [42] Reduction of nitrate by copper-coated ZVI nanoparticles
    Sparis, Dimitris
    Mystrioti, Christiana
    Xenidis, Anthimos
    Papassiopi, Nymphodora
    DESALINATION AND WATER TREATMENT, 2013, 51 (13-15) : 2926 - 2933
  • [43] HYDROGEN PERMEATION THROUGH COPPER-COATED PALLADIUM
    ANDREW, PL
    HAASZ, AA
    JOURNAL OF APPLIED PHYSICS, 1991, 70 (07) : 3600 - 3604
  • [44] PREPARATION OF COPPER-COATED TITANIA PARTICLES FOR COMPOSITES
    KUMAR, KG
    PAVITHRAN, C
    ROHATGI, PK
    JOURNAL OF MATERIALS SCIENCE, 1980, 15 (06) : 1588 - 1592
  • [45] Preparation and characterization of copper-coated alumina powders
    Zhao, G.
    Shi, Z. M.
    HIGH-PERFORMANCE CERAMICS IV, PTS 1-3, 2007, 336-338 : 1403 - 1405
  • [46] Photothermal Evidence of Laterally Inhomogeneous Interfacial Thermal Resistance in Copper-Coated Carbon Samples
    P. Kijamnajsuk
    J. Pelzl
    M. Chirtoc
    N. Horny
    D. Schäfer
    C. Eisenmenger-Sittner
    International Journal of Thermophysics, 2012, 33 : 2132 - 2138
  • [47] Study on Metallurgically Prepared Copper-Coated Carbon Fibers Reinforced Aluminum Matrix Composites
    Meilian Gao
    Pingping Gao
    Yu Wang
    Ting Lei
    Chun Ouyang
    Metals and Materials International, 2021, 27 : 5425 - 5435
  • [48] Enhanced electromagnetic shielding of lightweight copper-coated nonwoven laminate with carbon filament reinforcement
    Hu, Shi
    Wang, Dan
    Venkataraman, Mohanapriya
    Kremenakova, Dana
    Militky, Jiri
    Yang, Kai
    Wang, Yuanfeng
    Palanisamy, Sundaramoorthy
    JOURNAL OF ENGINEERED FIBERS AND FABRICS, 2023, 18
  • [49] Study on Metallurgically Prepared Copper-Coated Carbon Fibers Reinforced Aluminum Matrix Composites
    Gao, Meilian
    Gao, Pingping
    Wang, Yu
    Lei, Ting
    Ouyang, Chun
    METALS AND MATERIALS INTERNATIONAL, 2021, 27 (12) : 5425 - 5435
  • [50] Photothermal Evidence of Laterally Inhomogeneous Interfacial Thermal Resistance in Copper-Coated Carbon Samples
    Kijamnajsuk, P.
    Pelzl, J.
    Chirtoc, M.
    Horny, N.
    Schaefer, D.
    Eisenmenger-Sittner, C.
    INTERNATIONAL JOURNAL OF THERMOPHYSICS, 2012, 33 (10-11) : 2132 - 2138
12345