Mechanical properties of copper-coated carbon foams

被引：28
|
作者：
Almajali, M. [1 ]
Lafdi, K. [1 ]
Prodhomme, P. H. [2 ]
Ochoa, Ozden [3 ]
机构：
[1] Univ Dayton, Dayton, OH 45469 USA
[2] Arts ET Metiers Paris Tech, F-51006 Chalons Sur Marne, France
[3] Texas A&M Univ, College Stn, TX 77843 USA
来源：
CARBON | 2010年 / 48卷 / 05期
关键词：
D O I：
10.1016/j.carbon.2009.12.060
中图分类号：
O64 [物理化学（理论化学）、化学物理学];
学科分类号：
070304 ; 081704 ;
摘要：
The mechanical properties of copper-coated carbon foam were investigated Reticulated vitreous carbon cell type foams, with 97% porosity and 10 ppi pore size, were electroplated with copper for different penods of time to obtain coatings with different thicknesses and foams with different porosities Compression tests were performed to determine the Young's modulus and the plateau stress The copper electroplating technique improved these two proper-ties, with the modulus increasing from 4 S to 8 6 MPa for the sample electroplated for 40 min and the plateau stress increasing from 54 to 171 kPa for the foam coated for 80 min The relationships between the measured proper-ties and the copper weight ratio were deter-mined (C) 2010 Elsevier Ltd All rights reserved
引用
收藏
页码：1604 / 1608
页数：5
相关论文
共 50 条
  • [31] Enhancement in ageing and functional properties of copper-coated fabrics by subsequent electroplating
    Ali, Azam
    Baheti, Vijay
    Javaid, Muhammad Usman
    Militky, Jiri
    APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING, 2018, 124 (09):
  • [32] Enhancement in ageing and functional properties of copper-coated fabrics by subsequent electroplating
    Azam Ali
    Vijay Baheti
    Muhammad Usman Javaid
    Jiri Militky
    Applied Physics A, 2018, 124
  • [33] Interfacial Properties of Copper-coated Graphite Electrodes: Coating Thickness Dependence
    Nobili, F.
    Dsoke, S.
    Mancini, M.
    Marassi, R.
    FUEL CELLS, 2009, 9 (03) : 264 - 268
  • [34] Effect of copper-coated graphite on tribological properties of phenolic resin composites
    Zhang, En
    Fu, Rong
    Shen, Chang-Bin
    Gao, Fei
    Gao, Fei (gaofei@djtu.edu.cn), 1600, Chongqing Wujiu Periodicals Press (49): : 170 - 176
  • [35] Structure feature characterization of aluminum foam reinforced by copper-coated carbon fibers
    Du J.
    Wang B.
    Cao Z.
    Yao G.
    Liang L.
    Cailiao Daobao/Materials Review, 2016, 30 (03): : 82 - 85and115
  • [36] Facile preparation of nanostructured copper-coated carbon microelectrodes for amperometric sensing of carbohydrates
    Riman, D.
    Bartosova, Z.
    Halouzka, V.
    Vacek, J.
    Jirovsky, D.
    Hrbac, J.
    RSC ADVANCES, 2015, 5 (39) : 31245 - 31249
  • [37] Galvanic corrosion of copper-coated carbon steel for used nuclear fuel containers
    Standish, Thalia E.
    Zagidulin, Dmitrij
    Ramamurthy, Sridhar
    Keech, Peter G.
    Noel, James J.
    Shoesmith, David W.
    CORROSION ENGINEERING SCIENCE AND TECHNOLOGY, 2017, 52 : 65 - 69
  • [38] Effect of copper-coated carbon fiber on the electromechanical and chloride extraction properties of cement-based anode materials
    Wang, Penggang
    Li, Weichao
    Fu, Hua
    Zhao, Haitao
    Xiong, Chuansheng
    Liu, Tao
    Li, Chenglong
    CEMENT & CONCRETE COMPOSITES, 2025, 159
  • [39] Preparation of tin coating on the surface of copper-coated carbon fiber and its effect on the microstructures and properties of the composite coating
    Xu, Wendong
    Li, Guanglong
    Qu, Yingdong
    Zhang, Wei
    Zhou, Qiwen
    Zhou, Shan
    Su, Ruiming
    Li, Rongde
    MATERIALS RESEARCH EXPRESS, 2021, 8 (12)
  • [40] Synergistic enhancing effect for mechanical and electrical properties of tungsten copper composites using spark plasma infiltrating sintering of copper-coated graphene
    Chen, Wenge
    Dong, Longlong
    Wang, Jiaojiao
    Zuo, Ying
    Ren, Shuxin
    Fu, Yongqing
    SCIENTIFIC REPORTS, 2017, 7
12345