Outdoor exposure test on prepainted 55%Al-Zn coated steel sheet subjected in 15-year

被引：2

作者：

Nomura, H ^{[1
]}

Kanai, H ^{[1
]}

Takasugi, M ^{[1
]}

机构：

[1] Nippon Steel Corp Ltd, Steel Res Labs, Futtsu 2938511, Japan

来源：

TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN | 2003年 / 89卷 / 01期

关键词：

55%Al-Zn coated steel sheet; prepainted steel sheet; corrosion; edge creep; outdoor exposure;

D O I：

10.2355/tetsutohagane1955.89.1_196

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

We carried out a 15-year outdoor exposure test to investigate the corrosion behavior of prepainted 55%Al-Zn coated steel sheet in comparison with prepainted galvanized steel sheet. The edge creep of prepainted 55%Al-Zn coated steel sheet is larger than that of prepainted galvanized steel sheet in the early stages of the exposure test. However, the progress of edge creep of prepainted 55%Al-Zn coated steel sheet slows down year,after year then stopps, while that of prepainted galvanized steel sheet remains almost constant. The edge creep widths of both sheets were almost the same at 6 to 8 years. After that point, the edge creep width of prepainted 55%Al-Zn coated steel sheet was smaller than that of prepainted galvanized steel sheet. Also, the scribed part and T-bend part of prepainted 55%Al-Zn coated steel sheet shows better corrosion resistance than those of prepainted galvanized steel sheet. The effect of pretreatment and primer on the corrosion of prepainted 55%Al-Zn coated steel sheet was not clearly noticed.

引用

页码：196 / 203

页数：8

共 49 条

[41] Effect of Environmental Conditions on the Corrosion near Shear Cut Edge of 55 mass% Al-Zn Alloy Coated Steel Sheets
Matsumoto, Masamitsu
Okada, Nobuhiro
Nishihara, Katsuhiro
Kimoto, Masanari
Kudo, Takeo
Fujimoto, Shinji
ISIJ INTERNATIONAL, 2011, 51 (03) : 462 - 470
[42] EXPERIMENT ON HOT DIPPING OF Al-Zn EUTECTOID-BASE SUPERPLASTIC ALLOY ONTO SHEET STEEL AND SOME PROPERTIES OF THE COATED STEEL.
Motohashi, Yoshinobu
Shibata, Takao
1600, (26):
[43] Investigation of corrosion resistance of pre-painted Zn-11%Al-3%Mg-0.2%Si alloy coated steel sheet through outdoor exposure test in Okinawa
Ueda, K.
Takahashi, A.
Kubo, Y.
METALLURGIA ITALIANA, 2012, (03): : 13 - 19
[44] Tribological performance of thin organic permanent coatings deposited on 55% Al-Zn coated steel - Influence of coating composition and thickness on friction and wear
Carlsson, P.
Bexell, U.
Olsson, M.
Wear, 2001, 250-251 (PART 2) : 1075 - 1084
[45] THE EFFECT OF A Cr-FREE FINGERPRINT-RESISTANT PASSIVATION FILM ON THE PERFORMANCE OF HOT-DIP 55 % Al-Zn COATED STEEL
Li, Jian
Zhao, Zhanbiao
Tang, Xingchang
Wang, Yi
Cao, Youzhi
Li, Yang
Yuan, Xiaofeng
Zhang, Deyi
MATERIALI IN TEHNOLOGIJE, 2024, 58 (04): : 511 - 520
[46] Tribological performance of thin organic permanent coatings deposited on 55%Al-Zn coated steel - influence of coating composition and thickness on friction and wear
Carlsson, P
Bexell, U
Olsson, M
WEAR, 2001, 251 : 1075 - 1084
[47] COMPARISON OF THE KESTERNICH SULFUR-DIOXIDE TEST WITH INDUSTRIAL ATMOSPHERIC CORROSION TESTS OF ZINC-COATED, ALUMINUM-COATED, AND AL-ZN-COATED STEEL SHEET
BERKE, NS
TOWNSEND, HE
JOURNAL OF TESTING AND EVALUATION, 1985, 13 (01) : 74 - 76
[48] Influence of Treatment Time on Performance of Cr(III)-Based Conversion Coatings on Hot Dip Zn-55Al-1.6Si Coated Steel Sheet
Pan, Jie
Tang, Xiao
Li, Yan
COATINGS, 2019, 9 (05):
[49] Perspective on "Atmospheric Corrosion Resistance of Skyward- and Groundward-Exposed Surfaces of Zinc- and 55% Al-Zn Alloy-Coated Steel Sheet,"HE Townsend, Corrosion 54, 7 (1998): p.561-565
Dean, Sheldon W., Jr.
CORROSION, 2019, 75 (04) : 328 - 329

← 1 2 3 4 5 →