Outdoor exposure test on prepainted 55%Al-Zn coated steel sheet subjected in 15-year

被引：2
|
作者：
Nomura, H [1 ]
Kanai, H [1 ]
Takasugi, M [1 ]
机构：
[1] Nippon Steel Corp Ltd, Steel Res Labs, Futtsu 2938511, Japan
来源：
TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN | 2003年 / 89卷 / 01期
关键词：
55%Al-Zn coated steel sheet; prepainted steel sheet; corrosion; edge creep; outdoor exposure;
D O I：
10.2355/tetsutohagane1955.89.1_196
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
We carried out a 15-year outdoor exposure test to investigate the corrosion behavior of prepainted 55%Al-Zn coated steel sheet in comparison with prepainted galvanized steel sheet. The edge creep of prepainted 55%Al-Zn coated steel sheet is larger than that of prepainted galvanized steel sheet in the early stages of the exposure test. However, the progress of edge creep of prepainted 55%Al-Zn coated steel sheet slows down year,after year then stopps, while that of prepainted galvanized steel sheet remains almost constant. The edge creep widths of both sheets were almost the same at 6 to 8 years. After that point, the edge creep width of prepainted 55%Al-Zn coated steel sheet was smaller than that of prepainted galvanized steel sheet. Also, the scribed part and T-bend part of prepainted 55%Al-Zn coated steel sheet shows better corrosion resistance than those of prepainted galvanized steel sheet. The effect of pretreatment and primer on the corrosion of prepainted 55%Al-Zn coated steel sheet was not clearly noticed.
引用
收藏
页码：196 / 203
页数：8
相关论文
共 49 条
  • [21] Effect of Environmental Cation Species on Corrosion near Shear Cut Edge of 55%Al-Zn Alloy Coated Steel Sheet
    Matsumoto, Masamitsu
    Okada, Nobuhiro
    Nishihara, Katsuhiro
    Kimoto, Masanari
    Kudo, Takeo
    ISIJ INTERNATIONAL, 2009, 49 (04) : 574 - 581
  • [22] Cut-Edge Corrosion Behavior of Prepainted 55% Al-Zn Steel with Chromate -free Primers in Various Atmospheric Environments
    Tsujita, Takahiro
    Ooi, Azusa
    Tada, Eiji
    Nishikata, Atsushi
    ISIJ INTERNATIONAL, 2021, 61 (10) : 2620 - 2628
  • [23] High temperature deformation behaviors of hot dip 55 wt% Al-Zn coated steel
    Chang, Jun-Kai
    Lin, Chao-Sung
    Wang, Woei-Ren
    Jian, Shun-Yi
    APPLIED SURFACE SCIENCE, 2020, 511
  • [24] SIMS ANALYSIS OF THE ATMOSPHERIC CORROSION OF A 55-PERCENT AL-ZN COATED STEEL WIRE
    VANCRAEN, M
    HAEMERS, G
    ADAMS, F
    INTERNATIONAL JOURNAL OF MASS SPECTROMETRY AND ION PROCESSES, 1983, 46 (JAN): : 531 - 534
  • [25] Influence of an annealing heat treatment on the microstructure, ductility, and corrosion resistance of a chromated 55 wt.% Al-Zn coated steel sheet
    Nogueira, TMC
    Cruz, MAS
    Rios, PR
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2001, 10 (03) : 314 - 319
  • [26] Influence of an annealing heat treatment on the microstructure, ductility, and corrosion resistance of a chromated 55 wt.% Al-Zn coated steel sheet
    T. M. C. Nogueira
    M. A. S. Cruz
    P. R. Rios
    Journal of Materials Engineering and Performance, 2001, 10 : 314 - 319
  • [27] Corrosion behavior of 55%Al-Zn coated steel under wet-dry cycling conditions
    El-Mahdy, GA
    Nishikata, A
    Tsuru, T
    CORROSION AND CORROSION CONTROL IN SALTWATER ENVIRONMENTS, 2000, 99 (26): : 97 - 106
  • [28] Atmospheric Corrosion of Painted Galvanized and 55%Al-Zn Steel Sheets: Results of 12 Years of Exposure
    Elsner, C. I.
    Sere, P. R.
    Di Sarli, A. R.
    INTERNATIONAL JOURNAL OF CORROSION, 2012, 2012
  • [29] Atmospheric corrosion resistance of skyward- and groundward-exposed surfaces of zinc- and 55% Al-Zn alloy-coated steel sheet
    Townsend, HE
    CORROSION, 1998, 54 (07) : 561 - 565
  • [30] Application of a direct current anodic voltammetric technique to a 55mass%Al-Zn coated steel sheet before and after an annealing heat treatment
    Nogueira, TMC
    Cruz, MAS
    Rios, PR
    ISIJ INTERNATIONAL, 1999, 39 (03) : 295 - 297
12345