Optimum Silane Treatment for the Adhesively Bonded Aluminum Adherends at the Cryogenic Temperature

被引：30

作者：

Kim, Jin Gyu ^{[1
]}

Park, Sang Wook ^{[1
]}

Yoon, Soon Ho ^{[1
]}

Lee, Dai Gil ^{[1
]}

机构：

[1] Korea Adv Inst Sci & Technol, Dept Mech Engn, Taejon 305701, South Korea

来源：

JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY | 2010年 / 24卷 / 04期

关键词：

Silane treatment; aluminum joint; single-lap joint; LNG; cryogenic temperature; SURFACE; STRENGTH; IMPROVEMENT; GLASS;

D O I：

10.1163/016942409X12579497420843

中图分类号：

TQ [化学工业];

学科分类号：

0817 ;

摘要：

Aluminum adherends for the adhesive joints at cryogenic application such as LNG (Liquefied Natural Gas) containment tanks were silane treated to improve bond strength of the aluminum joints. The bond strengths of the single-lap joints composed of aluminum adherends and epoxy adhesive were measured with respect to the condition of the silane solution and surface roughness obtained with grit blast. The chemical composition of the silane treated aluminum surface was analyzed by XPS (X-ray photoelectron spectroscopy). Also, contact angles of appropriate liquids on the silane treated aluminum surface were measured with respect to treatment conditions. From the experiments, the optimum treatment conditions for the aluminum adherends were obtained for the adhesive joints at the cryogenic temperature. (C) Koninklijke Brill NV, Leiden, 2010

引用

页码：775 / 787

页数：13

共 50 条

[41] DURABILITY IN ALUMINUM-SMC ADHESIVELY BONDED SYSTEMS
DILLARD, JG
SPINU, I
GRANT, JW
DESIGN AND MANUFACTURING OF ADVANCED COMPOSITES, 1989, : 97 - 109
[42] Adhesively bonded assemblies with identical nondeformable adherends and nonhomogeneous adhesive layer: Predicted thermal stresses in the adhesive
Suhir, E
JOURNAL OF REINFORCED PLASTICS AND COMPOSITES, 1998, 17 (18) : 1588 - 1606
[43] Cryogenic Performance of Adhesively Bonded Metal Joints for LNG Containment System
Bang, Chang Seon
Kim, Jin Gyu
Lee, Dai Gil
JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY, 2012, 26 (07) : 969 - 986
[44] Plasma treatment using nitrogen gas to improve bonding strength of adhesively bonded aluminum foam/aluminum composite
Chung, H. J.
Rhee, K. Y.
Han, B. S.
Ryu, Y. M.
JOURNAL OF ALLOYS AND COMPOUNDS, 2008, 459 (1-2) : 196 - 202
[45] Plasma treatment using nitrogen gas to improve bonding strength of adhesively bonded aluminum foam/aluminum composite
Chung, H.J.
Rhee, K.Y.
Han, B.S.
Ryu, Y.M.
Journal of Alloys and Compounds, 2008, 459 (1-2): : 196 - 202
[46] Influence of stress-reduction methods on the strength of adhesively bonded joints composed of orthotropic brittle adherends
Vallee, Till
Tannert, Thomas
Murcia-Delso, Juan
Quinn, David J.
INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES, 2010, 30 (07) : 583 - 594
[47] Adhesively bonded joints composed of pultruded adherends: Considerations at the upper tail of the material strength statistical distribution
Vallee, Till
Keller, Thomas
Fourestey, Gilles
Fournier, Benjamin
Correia, Joao R.
PROBABILISTIC ENGINEERING MECHANICS, 2009, 24 (03) : 358 - 366
[48] STRENGTH EVALUATION OF ADHESIVELY BONDED JOINTS OF ALUMINUM-ALLOY
KYOGOKU, H
SUGIBAYASHI, T
IKEGAMI, K
TRANSACTIONS OF THE JAPAN INSTITUTE OF METALS, 1986, 27 (02): : 115 - 121
[49] Interface strength and degradation of adhesively bonded porous aluminum oxides
Shoshan T. Abrahami
John M. M. de Kok
Visweswara C. Gudla
Rajan Ambat
Herman Terryn
Johannes M. C. Mol
npj Materials Degradation, 1
[50] THE FAILURE MODE OF ADHESIVELY BONDED ALUMINUM FOLLOWING AQUEOUS EXPOSURE
WATTS, JF
BLUNDEN, RA
HALL, TJ
SURFACE AND INTERFACE ANALYSIS, 1990, 16 (1-12) : 227 - 235

← 1 2 3 4 5 →