Study of the corrosion behavior of Aspergillus niger on 7075-T6 aluminum alloy in a high salinity environment

被引：42

作者：

Wang, Junlei ^{[1
]}

Xiong, Fuping ^{[1
]}

Liu, Hongwei ^{[1
]}

Zhang, Tiansui ^{[1
]}

Li, Yanyan ^{[1
]}

Li, Chenjing ^{[1
]}

Xia, Wu ^{[1
]}

Wang, Haitao ^{[2
]}

Liu, Hongfang ^{[1
]}

机构：

[1] Huazhong Univ Sci & Technol, Sch Chem & Chem Engn, Key Lab Mat Chem Energy Convers & Storage, Minist Educ,Hubei Key Lab Mat Chem & Serv Failure, Wuhan 430074, Hubei, Peoples R China

[2] Wuhan Inst Technol, Sch Chem & Environm Engn, Minist Educ, Key Lab Green Chem Proc, Wuhan 430073, Hubei, Peoples R China

来源：

BIOELECTROCHEMISTRY | 2019年 / 129卷

关键词：

Aluminum alloy; Aspergillus Niger; Microbiology; Corrosion; Electrochemistry; SULFATE-REDUCING BACTERIA; MICROBIOLOGICALLY INFLUENCED CORROSION; IRON-OXIDIZING BACTERIA; CARBON-STEEL; PIPELINE STEEL; ACID; INHIBITION; PROTECTION; ADAPTATION; PYRITHIONE;

D O I：

10.1016/j.bioelechem.2019.04.020

中图分类号：

Q5 [生物化学]; Q7 [分子生物学];

学科分类号：

071010 ; 081704 ;

摘要：

In this study, the corrosion behavior of 7075-T6 aluminum alloy in a high salinity environment containing Aspergillus niger was investigated using high-performance liquid chromatography tandem mass spectrometry, gas chromatography, surface analysis and electrochemical measurement. Results demonstrated that uniform and localized corrosion rates of the alloy in the presence of A. niger were approximately 3.7 and 22.4 times, respectively, of that in the absence A niger. This higher corrosion rate was attributed to accelerated anode and cathode reactions from the actions of A. niger biofilm. Additionally, organic acid corrosion caused by the presence of A. niger was confirmed to be the main cause for the corrosion of aluminum alloy. (C) 2019 Elsevier B.V. All rights reserved.

引用

页码：10 / 17

页数：8

共 50 条

[41] Corrosion mechanism and machinability of 7075-T6 aluminum alloy in high-speed cutting: With and without cryogenic treatment
Zhang, Ping
Wang, Shunxiang
Lin, Zhenyong
Liu, Zehua
Liu, Junling
Mai, Qingqun
Yue, Xiujie
MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2023, 74 (06): : 872 - 886
[42] Study of Vibration-Ultrasonic Combined Fatigue on 7075-T6 Aluminum Alloy
Zhao, Ziyu
Tang, Sen
Chen, Mingsan
Liu, Yongjie
He, Chao
Xu, Bo
Wang, Chong
Wang, Qingyuan
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2025, 48 (01) : 231 - 243
[43] STRESS-CORROSION PREVENTIVE COATING FOR 7075-T6 ALUMINUM
MILLER, RN
SEELIGER, GC
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1973, 120 (08) : C230 - C230
[44] STUDY OF FRETTING FATIGUE CRACK NUCLEATION IN 7075-T6 ALUMINUM-ALLOY
ADIBNAZARI, S
HOEPPNER, DW
WEAR, 1992, 159 (02) : 257 - 264
[45] WORKABILITY OF ALUMINUM-ALLOY 7075-T6 IN UPSETTING AND ROLLING
OH, SI
KOBAYASHI, S
JOURNAL OF ENGINEERING FOR INDUSTRY-TRANSACTIONS OF THE ASME, 1976, 98 (03): : 800 - 806
[46] THE EFFECTS OF CORROSION ON THE MECHANICAL PROPERTIES OF ALUMINIUM ALLOY 7075-T6
Necsulescu, Daniela Alina
UNIVERSITY POLITEHNICA OF BUCHAREST SCIENTIFIC BULLETIN SERIES B-CHEMISTRY AND MATERIALS SCIENCE, 2011, 73 (01): : 223 - 229
[47] Feasibility study on contact heating warm forming of 7075-T6 aluminum alloy
Sun, Lu
Zhang, Zhiqiang
Song, Zhenkun
Ren, Mingwen
Jia, Hongjie
ARCHIVES OF CIVIL AND MECHANICAL ENGINEERING, 2023, 23 (03)
[48] Effect of alkaline cleaning and activation on aluminum alloy 7075-T6
Joshi, Simon
Fahrenholtz, William G.
O'Keefe, Matthew J.
APPLIED SURFACE SCIENCE, 2011, 257 (06) : 1859 - 1863
[49] Influence of Applied Load and Sliding Velocity on Tribocorrosion Behavior of 7075-T6 Aluminum Alloy
Li, Zhengyi
Yu, Hongying
Wen, Lei
Sun, Dongbai
METALS, 2022, 12 (10)
[50] Fracture behavior of 7075-T6 aluminum alloy under electromagnetic forming and traditional stamping
Yan, Ziqin
Xiao, Ang
Cui, Xiaohui
Lin, Yuhong
Yu, Hailiang
Chen, Baoguo
ARCHIVES OF CIVIL AND MECHANICAL ENGINEERING, 2021, 21 (03)

← 1 2 3 4 5 →