Development of Nb3Al superconducting wire for accelerator magnets

被引：14
|
作者：
Kobayashi, T [1 ]
Tsuchiya, K
Shintomi, T
Terashima, A
Banno, N
Nimori, S
Takeuchi, T
Tagawa, K
Iwaki, G
机构：
[1] KEK, High Energy Accelerator Res Org, Tsukuba, Ibaraki 3050801, Japan
[2] Natl Inst Mat Sci, Tsukuba, Ibaraki 3050003, Japan
[3] Hitachi Cable Ltd, Tsuchiura, Ibaraki 3000026, Japan
来源：
IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY | 2004年 / 14卷 / 02期
关键词：
accelerator magnets; critical current density; Nb3Al wire; rapid-heating/quenching process;
D O I：
10.1109/TASC.2004.830370
中图分类号：
TM [电工技术]; TN [电子技术、通信技术];
学科分类号：
0808 ; 0809 ;
摘要：
Nb3Al superconductors have shown promising performance compared to Nb3Sn conductors when processed by rapid heating/quenching process. Therefore we have started an R&D program of Nb3Al conductors for future accelerator magnets. Several test wires of around 0.8 mm diameter, which have relatively small filament (similar to50 micron diameter) and low matrix ratio (similar to1.0), were fabricated, and the heat treatment and area reduction conditions after the rapid quenching process were studied. The highest noncopper J(c) achieved during this study was 1734 A/mm(2) at 10 T and 4.2
引用
收藏
页码：1016 / 1019
页数：4
相关论文
共 50 条
  • [31] Development of Nb3Al superconductors for ITER
    Ayai, N
    Yamada, Y
    Mikumo, A
    Ito, M
    Ohmatsu, K
    Sato, K
    Koizumi, N
    Ando, T
    Matsui, K
    Sugimoto, M
    Tsuji, H
    Okuno, K
    IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 1999, 9 (02) : 2688 - 2691
  • [32] Development of Nb3Al multifilamentary superconductors
    Ayai, N.
    Yamada, Y.
    Mikumo, A.
    Takahashi, K.
    Sato, K.
    Koizumi, N.
    Sugimoto, M.
    Ando, T.
    Takahashi, Y.
    Nishi, M.
    Tsuji, H.
    IEEE Transactions on Applied Superconductivity, 1995, 5 (2 pt 1): : 893 - 896
  • [33] Effect of the layer thickness on Nb3Al superconducting wires
    Saito, S., 1600, (B7): : 1 - 2
  • [34] Superconducting Nb3Al by combustion synthesis: Structural characterization
    Hafs A.
    Benaldjia A.
    Hafs T.
    Hafs, A. (hafsali2006@yahoo.fr), 2016, Allerton Press Incorporation (25) : 159 - 165
  • [35] RELAXATION OF THE SPIN OF A POSITIVE MUON IN SUPERCONDUCTING NB3AL
    BARSOV, SG
    GETALOV, AL
    GREBINNIK, VG
    GORDEEV, VA
    GUREVICH, II
    ZHUKOV, VA
    KIRILLOV, BF
    KLIMOV, AI
    KRUGLOV, SP
    KUZMIN, LA
    LAZAREV, AB
    MIKIRTYCHYANTS, SM
    MIKHAILOV, BP
    NIKOLSKII, BA
    PIROGOV, AV
    PONOMAREV, AN
    SELIVANOV, VI
    SUETIN, VA
    KHLOPKIN, MN
    SHCHERBAKOV, GV
    JETP LETTERS, 1985, 41 (02) : 75 - 78
  • [36] Magnetization measurement for a nearly stoichiometric Nb3Al wire
    Mao, Dali
    Itoh, K.
    Kuroda, T.
    Yuyama, M.
    Wada, H.
    Murakami, Y.
    Physica C: Superconductivity and its Applications, 1998, 301 (3-4): : 272 - 276
  • [37] MICROSTRUCTURAL OBSERVATION OF NB3AL MULTIFILAMENTARY SUPERCONDUCTING WIRES
    HASEGAWA, A
    TAKEUCHI, T
    INOUE, K
    JOURNAL OF MATERIALS SCIENCE, 1993, 28 (04) : 942 - 948
  • [38] SUPERCONDUCTING TRANSITION TEMPERATURES OF Nb3Al and Nb3(Al,Ge) SUPERCONDUCTORS.
    Hiroyuki, Yoshida
    Hisao, Kodaka
    Yoshihiko, Hayashi
    Katsumi, Shoji
    Annual Reports of the Research Reactor Institute, Kyoto University, 1985, 18 : 154 - 158
  • [39] Development of Nb3Al Rutherford Cable for High-Field Accelerator Magnet Applications
    Tsuchiya, K.
    Kikuchi, A.
    Takeuchi, T.
    Banno, N.
    Iijima, Y.
    Nimori, S.
    Takigawa, H.
    Terashima, A.
    Nakamoto, T.
    Kuroda, Y.
    Maruyama, M.
    Yoshida, M.
    Takao, T.
    Nakagawa, K.
    Barzi, E.
    Yamada, R.
    Zlobin, A.
    IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 2012, 22 (03)
  • [40] METALLURGICAL CONSIDERATIONS FOR OPTIMIZING SUPERCONDUCTING PROPERTIES OF NB3AL
    KOHR, JG
    ROSE, RM
    EAGAR, TW
    METALLURGICAL TRANSACTIONS, 1972, 3 (05): : 1177 - &
12345