Improved oxidation resistance of TiAlN coatings by doping with Si or B

被引:84
|
作者
Pfeiler, M. [1 ]
Zechner, J. [1 ]
Penoy, M. [2 ]
Michotte, C. [2 ]
Mitterer, C. [3 ]
Kathrein, M. [4 ]
机构
[1] Mat Ctr Leoben Forsch GmbH, Leoben, Austria
[2] Ceratizit Luxembourg Sarl, Mamer, Luxembourg
[3] Univ Leoben, Dept Phys Met & Mat Testing, Leoben, Austria
[4] Ceratizit Austria GmbH, Reutte, Austria
来源
SURFACE & COATINGS TECHNOLOGY | 2009年 / 203卷 / 20-21期
关键词
Ti-Al-Si-N; Ti-Al-B-N; Ti-Al-N; Cathodic arc evaporation; Oxidation; REACTIVE ARC EVAPORATION; N COATINGS; NANOCOMPOSITE COATINGS; HARD COATINGS; TRIBOLOGICAL PROPERTIES; TI1-XALXN COATINGS; PHASE-STABILITY; BIAS VOLTAGE; THIN-FILMS; TI;
D O I
10.1016/j.surfcoat.2009.03.036
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
The improved oxidation resistance of TiAlN-based hard coatings is based on the formation of protective oxide scales. Here we report on further improvement of the oxidation resistance of TiAlN coatings by doping with Si and B. An industrial-scale cathodic arc evaporation facility was used to deposit Ti-Al-Si-N and Ti-Al-B-N coatings, with doping contents in the target of up to 2 at% for Si and 0.5 at% for B. X-ray diffraction displayed an increased formation of a hexagonal nitride phase for Si and B doped coatings. Oxidation experiments in ambient air showed a decreased thickness of the oxide scale with increasing content of the doping element, where doping with Si was found to be more beneficial than with B. Energy-dispersive X-ray spectroscopy line scans indicated an oxide scale with an Al-rich top-layer and a Ti-rich sub-layer, while Si was homogeneously distributed in both layers. For both doping elements, a modified oxidation sequence of Ti was found, compared to the undoped TiAlN reference coating. In particular, Raman spectroscopy revealed a significantly higher content of the metastable anatase type TiO(2), at the expense of the stable rutile type TiO(2), in the formed oxide scale. This is explained by hindered grain growth of the anatase phase followed by a retarded anatase-rutile transformation. Consequently, the time for coarsening of rutile and the accompanied generation of compressive stresses in the Ti-rich sub-layer is reduced. This is responsible for the superior oxidation properties of Si and B doped TiAlN. (C) 2009 Elsevier B.V. All rights reserved.
引用
收藏
页码:3104 / 3110
页数:7
相关论文
共 50 条
  • [21] Structure, Mechanical Properties, and Oxidation Resistance of Mo–Hf–La–Si–B Coatings
    Ph. V. Kiryukhantsev-Korneev
    A. D. Sytchenko
    F. I. Chudarin
    E. A. Levashov
    Physics of Atomic Nuclei, 2023, 86 : 1993 - 1997
  • [22] Improved oxidation resistance of A5Si3 (A=transition metal) silicides by small atom doping
    Thom, AJ
    Meyer, MK
    Williams, JJ
    Akinc, M
    PROCESSING AND FABRICATION OF ADVANCED MATERIALS IV, 1996, : 139 - 149
  • [23] Oxidation Resistance of TiAlN Coatings Deposited by Dual High-Power Impulse Magnetron Sputtering
    Grenadyorov, A. S.
    Oskirko, V. O.
    Zakharov, A. N.
    Oskomov, K. V.
    Semenov, V. A.
    Solovyev, A. A.
    Shmakov, A. N.
    JOURNAL OF SURFACE INVESTIGATION, 2023, 17 (SUPPL 1): : S128 - S135
  • [24] Oxidation resistance of TiN, CrN, TiAlN and CrAlN coatings deposited by lateral rotating cathode arc
    Chim, Y. C.
    Ding, X. Z.
    Zeng, X. T.
    Zhang, S.
    THIN SOLID FILMS, 2009, 517 (17) : 4845 - 4849
  • [25] Comparative study on crack resistance of TiAlN monolithic and Ti/TiAlN multilayer coatings
    Shuai, Jintao
    Zuo, Xiao
    Wang, Zhenyu
    Guo, Peng
    Xu, Beibei
    Zhou, Jia
    Wang, Aiying
    Ke, Peiling
    CERAMICS INTERNATIONAL, 2020, 46 (05) : 6672 - 6681
  • [26] Oxidation Resistance of TiAlN Coatings Deposited by Dual High-Power Impulse Magnetron Sputtering
    A. S. Grenadyorov
    V. O. Oskirko
    A. N. Zakharov
    K. V. Oskomov
    V. A. Semenov
    A. A. Solovyev
    A. N. Shmakov
    Journal of Surface Investigation: X-ray, Synchrotron and Neutron Techniques, 2023, 17 : S128 - S135
  • [27] Structure, Mechanical Properties, and Oxidation Resistance of Mo-Hf-La-Si-B Coatings
    Kiryukhantsev-Korneev, Ph. V.
    Sytchenko, A. D.
    Chudarin, F. I.
    Levashov, E. A.
    PHYSICS OF ATOMIC NUCLEI, 2023, 86 (09) : 1993 - 1997
  • [28] Oxidation resistance coatings of Mo-Si-B alloys via a pack cementation process
    Park, J. S.
    Kim, J. M.
    Kim, H. Y.
    Yi, S.
    Perepezko, J. H.
    METALS AND MATERIALS INTERNATIONAL, 2008, 14 (01) : 1 - 7
  • [29] Resistance to high-temperature oxidation in B+Si implanted TiN coatings on steel
    Werner, Z
    Piekoszewski, J
    Grötzschel, R
    Richter, E
    Szymczyk, W
    VACUUM, 2003, 70 (2-3) : 93 - 96
  • [30] Oxidation behaviour of nanoscale TiAlN/VN multilayer coatings
    Zhou, Z
    Rainforth, WM
    Lewis, DB
    Creasy, S
    Forsyth, JJ
    Clegg, E
    Ehiasarian, AR
    Hovespian, PE
    Münz, WD
    SURFACE & COATINGS TECHNOLOGY, 2004, 177 : 198 - 203