Wear of TiCN coated sintered Fe-1.5Cr-0.2Mo-0.7C steels

被引：3
|
作者：
Bidulsky, Robert [1 ]
Actis-Grande, Marco [1 ]
机构：
[1] Politecn Torino Sede Alessandria, I-15100 Turin, Italy
来源：
FRACTOGRAPHY OF ADVANCED CERAMICS III | 2009年 / 409卷
关键词：
sintered steel; wear behaviour; PVD coating; BEHAVIOR; ALLOYS;
D O I：
10.4028/www.scientific.net/KEM.409.390
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
The wear behaviour on prealloyed sintered steel parts TiCN PVD coating was analysed. Cylindrical specimens (phi 40x30 mm(3)) were compacted to the green density of similar to 7.0 g.cm(-3). The specimens were sintered in pusher furnace at the temperature of 1180 degrees C for 40 minutes in an atmosphere of 25H(2)+75N(2). Part of sintered specimens was then coated by Physical Vapour Deposition. Wear tests were carried out by means of a pin-on-disk tribometer. The results of profilograms (the values of surface roughness) and the wear curves (mass loss versus sliding distance) showed positive effect of coating on the wear resistance of the tested specimens.
引用
收藏
页码：390 / 393
页数：4
相关论文
共 50 条
  • [21] FRACTURE STATISTICS USING THREE-PARAMETER AND TWO-PARAMETER WEIBULL DISTRIBUTIONS FOR Fe-0.4C-1.5Cr-1.5Ni-0.8Mn-0.2Mo STRUCTURAL SINTERED STEEL
    Fial, Ch.
    Cias, A.
    Czarski, A.
    Sulowski, M.
    ARCHIVES OF METALLURGY AND MATERIALS, 2016, 61 (03) : 1201 - 1208
  • [22] Simultaneous improvement of corrosion and wear resistance of Fe-Mn-Al-C lightweight steels: The role of Cr/Mo
    Tang, Yihao
    Li, Bo
    Shi, Heyang
    Guo, Yuxing
    Zhang, Shuzhi
    Zhang, Junsong
    Zhang, Xinyu
    Liu, Riping
    MATERIALS CHARACTERIZATION, 2023, 205
  • [23] Non classical eutectoid decomposition products morphologies in Fe-Cr-C and Fe-Cr-Mo-C steels
    Goldenstein, Helio
    Cifuentes, John Alexander Bustos
    Sinatora, Amilton
    SOLID-SOLID PHASE TRANSFORMATIONS IN INORGANIC MATERIALS 2005, VOL 1, 2005, : 673 - 686
  • [24] LOW-TEMPERATURE ION-NITRIDING OF FE-MO-C SINTERED STEELS
    MOLINARI, A
    TESI, B
    BACCI, T
    PRADELLI, G
    JOURNAL DE PHYSIQUE IV, 1993, 3 (C7): : 949 - 954
  • [25] FRACTURE BEHAVIOR OF HIGH-STRENGTH-STEEL SINTERED STEELS FE-MO-C
    Ionici, Cristina
    NANO, BIO AND GREEN - TECHNOLOGIES FOR A SUSTAINABLE FUTURE, VOL I (SGEM 2015), 2015, : 69 - 74
  • [26] Effect of quenching medium on microstructure and hardness of as sintered Fe-Cr-Mo-0.6C and Fe-Mo-0.6C alloy steel
    Sandeep
    Verma, Vikas
    Prakash, Ujjwal
    Tewari, P. C.
    Khanduja, Dinesh
    MATERIALS TODAY-PROCEEDINGS, 2017, 4 (02) : 459 - 464
  • [27] Surface rolling properties and load bearing capacity of 1.5Cr-0.2Mo sintered alloy steel gears for automotive transmission
    Takemasu T.
    Koide T.
    Ishimaru R.
    Takeda Y.
    Shinbutsu T.
    Kamimura D.
    Saito K.
    Nakamura S.
    Funtai Oyobi Fummatsu Yakin/Journal of the Japan Society of Powder and Powder Metallurgy, 2010, 57 (06): : 442 - 448
  • [28] Industrial processing, microstructures and mechanical properties of Fe-(2-4)Mn (-0.85Mo)-(0.3-0.7)C sintered steels
    Dudrová, E
    Kabátová, M
    Bidulsky, R
    Wronski, AS
    POWDER METALLURGY, 2004, 47 (02) : 181 - 190
  • [29] CO2 WELDING Fe-Ni-Mo-C-Cu SINTERED STEELS.
    Thornley, J.C.
    Welding and Metal Fabrication, 1973, 41 (11): : 399 - 402
  • [30] Microstructure and mechanical property of sintered Fe-Cr-Mo steels due to phase transformations with fast cooling rates
    Srijampan, Wananurat
    Wiengmoon, Amporn
    Morakotjinda, Monnapas
    Krataitong, Rungtip
    Yotkaew, Thanyaporn
    Tosangthum, Nattaya
    Tongsri, Ruangdaj
    MATERIALS & DESIGN, 2015, 88 : 693 - 701
12345