Corrosion resistance of HVOF-sprayed Ni2Si intermetallic coatings in hot H2SO4 medium

被引：6

作者：

Verdian, M. M. ^{[1
]}

Raeissi, K. ^{[1
]}

Salehi, M. ^{[1
]}

机构：

[1] Isfahan Univ Technol, Dept Mat Engn, Esfahan 8415683111, Iran

来源：

SURFACE & COATINGS TECHNOLOGY | 2014年 / 240卷

关键词：

Corrosion; EIS; Mott-Schottky; H2SO4; Ni2Si; HVOF; STEEL;

D O I：

10.1016/j.surfcoat.2013.12.016

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Corrosion behavior of high velocity oxy-fuel (HVOF) Ni2Si intermetallic coatings was investigated by means of Tafel polarization tests and electrochemical impedance spectroscopy (EIS) measurements in 70% H2SO4 solutions at 75 degrees C. Mott-Schottky analysis was also carried out to investigate semiconductive properties of passive films. It was found that the corrosion rate of HVOF Ni2Si coating was much lower than that of stainless steel substrate. Both Ni2Si bulk and coating materials showed an active-passive behavior with a wide passive range during anodic polarization. EIS measurements at open circuit conditions revealed that the system showed one time constant at low frequencies which was attributed to charge transfer processes. Under passive conditions, one time constant was observed at high frequencies which was related to formation of passive films. Further investigation showed that passive film formed on Ni2Si materials in H2SO4 is a p-type semiconductor with acceptor density in the order of 1020 cm(-3). (C) 2013 Elsevier B.V. All rights reserved.

引用

页码：70 / 75

页数：6

共 50 条

[41] Wear, erosion and corrosion resistance of HVOF-sprayed WC and Cr3C2 based coatings for electrolytic hard chrome replacement
Wang, Qun
Luo, Sisi
Wang, Shaoyi
Wang, Hui
Ramachandran, Chidambaram Seshadri
INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2019, 81 : 242 - 252
[42] Hot corrosion behavior of HVOF-sprayed carbide based composite coatings for boiler steel in Na2SO4-60 % V2O5 environment at 900 °C under cyclic conditions
Singh, Gurmail
Bala, Niraj
Chawla, Vikas
Singla, Yogesh Kumar
CORROSION SCIENCE, 2021, 190
[43] Effect of Structure Density of Milled Powder on Hot Corrosion and Erosion Resistance of HVOF-Sprayed Cr3C2-NiCr Coating
Safitry Ramandhany
Djoko Triyono
Eni Sugiarti
Agus Sukarto Wismogroho
Hubby Izzuddin
Ahmad Afandi
Wahyu Bambang Widayatno
Resetiana Dwi Desiati
Risma Y. Sundawa
Journal of Thermal Spray Technology, 2024, 33 : 1075 - 1099
[44] Effect of Structure Density of Milled Powder on Hot Corrosion and Erosion Resistance of HVOF-Sprayed Cr3C2-NiCr Coating
Ramandhany, Safitry
Triyono, Djoko
Sugiarti, Eni
Wismogroho, Agus Sukarto
Izzuddin, Hubby
Afandi, Ahmad
Widayatno, Wahyu Bambang
Desiati, Resetiana Dwi
Sundawa, Risma Y.
JOURNAL OF THERMAL SPRAY TECHNOLOGY, 2024, 33 (04) : 1075 - 1099
[45] Microstructures and corrosion behavior of HVOF-sprayed WC-12%Cr3C2-6%Ni coatings before and after sealing
Liu, Yu-Wan
Sun, Wan-Chang
Tian, Sha-Sha
Xiao, Yan
Jia, Ya-Peng
INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY, 2022, 19 (01) : 383 - 396
[46] Corrosion behaviour of AISI 304 stainless steel with Cu coatings in H2SO4
Pardo, A.
Merino, M. C.
Coy, A. E.
Arrabal, R.
Viejo, F.
M'hich, A.
APPLIED SURFACE SCIENCE, 2007, 253 (23) : 9164 - 9176
[47] Microstructure and corrosion resistance of laser clad coating of Ni2Si/Ni3Si2 silicide alloy
Wang, CM
Cai, LX
Wang, HM
RARE METAL MATERIALS AND ENGINEERING, 2003, 32 (03) : 197 - 200
[48] Corrosion of Ni-Al and Ni-Al-Al2O3 Flame Sprayed Coatings of "CastoDyn 8000" System in 0.01 M H2SO4 and 3.5% NaCl Solutions
Starosta, Robert
ENVIRONMENTAL DEGRADATION OF ENGINEERING & MATERIALS ENGINEERING AND TECHNOLOGIES, 2012, 183 : 185 - 192
[49] Inhibitor for the Corrosion of Mild Steel in H2SO4
Patel, Niketan S.
Jauhari, Smita
Mehta, Girishkumar N.
SOUTH AFRICAN JOURNAL OF CHEMISTRY-SUID-AFRIKAANSE TYDSKRIF VIR CHEMIE, 2009, 62 : 200 - 204
[50] Inhibition of zinc corrosion in H2SO4 by hexamethylenetetramine
Jameel, AA
Elangovan, P
Balakrishnan, K
ASIAN JOURNAL OF CHEMISTRY, 1996, 8 (04) : 635 - 643

← 1 2 3 4 5 →