Evolution of transverse cracking in CF/epoxy cross-ply laminates under creep loading

被引：0

作者：

Takao, Y ^{[1
]}

Ogi, K ^{[1
]}

机构：

[1] Appl Mech Res Inst, Kasuga, Fukuoka 8168580, Japan

来源：

PROCEEDINGS OF THE EIGHTH JAPAN-U.S. CONFERENCE ON COMPOSITE MATERIALS | 1999年

关键词：

D O I：

暂无

中图分类号：

TB33 [复合材料];

学科分类号：

摘要：

The evolution of transverse cracking in a cross-ply laminate which deforms viscoelastically is investigated. A model predicting the strain under creep loading is established by a combination of the viseoelasticity theory, shear lag analysis and delayed failure concept. The creep strain and transverse crack density of the cross-ply laminates are measured during creep tests. Two stages of time for transverse cracking are observed in the creep tests. Predicted creep strains using the present model agree well with the experimental ones.

引用

页码：760 / 769

页数：10

共 50 条

[41] DELAMINATION CRACK ORIGINATING FROM TRANSVERSE CRACKING IN CROSS-PLY COMPOSITE LAMINATES UNDER EXTENSION
KIM, TW
KIM, HJ
IM, S
INTERNATIONAL JOURNAL OF SOLIDS AND STRUCTURES, 1991, 27 (15) : 1925 - 1941
[42] Transverse cracking of cross-ply laminates: Part 2. Progressive widthwise cracking
Universite du Maine, Le Mans, France
Compos Part A Appl Sci Manuf, 10 (1003-1010):
[43] DELAMINATION CRACKS ORIGINATING FROM TRANSVERSE CRACKING IN CROSS-PLY LAMINATES UNDER VARIOUS LOADINGS
KIM, YJ
IM, SY
INTERNATIONAL JOURNAL OF SOLIDS AND STRUCTURES, 1993, 30 (16) : 2143 - 2161
[44] Fatigue damage evolution in glass/epoxy cross-ply laminates under spectrum loadings
Carraro, Paolo Andrea
Simonetto, Mirko
Quaresimin, Marino
COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2023, 173
[45] Probabilistic energy based model for prediction of transverse cracking in cross-ply laminates
Vinogradov, V
Hashin, Z
INTERNATIONAL JOURNAL OF SOLIDS AND STRUCTURES, 2005, 42 (02) : 365 - 392
[46] Analysis of transverse cracking and stiffness loss in cross-ply laminates with hygrothermal conditions
Tounsi, A
Amara, KH
Adda-Bedia, EA
COMPUTATIONAL MATERIALS SCIENCE, 2005, 32 (02) : 167 - 174
[47] Effect of transverse cracking on stiffness reduction of hygrothermal aged cross-ply laminates
Bouazza, M.
Tounsi, A.
Benzair, A.
Adda-bedia, E. A.
MATERIALS & DESIGN, 2007, 28 (04) : 1116 - 1123
[48] Numerical simulation of interlaminar damage propagation in CFRP cross-ply laminates under transverse loading
Nishikawa, Masaaki
Okabe, Tomonaga
Takeda, Nobuo
INTERNATIONAL JOURNAL OF SOLIDS AND STRUCTURES, 2007, 44 (10) : 3101 - 3113
[49] On damage characteristics of cross-ply laminates under tensile loading
Wang, Rumin
Ma, Ruiran
Xibei Gongye Daxue Xuebao/Journal of Northwestern Polytechnical University, 1989, 7 (03): : 287 - 297
[50] ON CROSS-PLY CRACKING IN GLASS AND CARBON FIBER-REINFORCED EPOXY LAMINATES
PETERS, PWM
CHOU, TW
COMPOSITES, 1987, 18 (01): : 40 - 46

← 1 2 3 4 5 →