Evolution of transverse cracking in CF/epoxy cross-ply laminates under creep loading

被引：0
|
作者：
Takao, Y [1 ]
Ogi, K [1 ]
机构：
[1] Appl Mech Res Inst, Kasuga, Fukuoka 8168580, Japan
来源：
PROCEEDINGS OF THE EIGHTH JAPAN-U.S. CONFERENCE ON COMPOSITE MATERIALS | 1999年
关键词：
D O I：
暂无
中图分类号：
TB33 [复合材料];
学科分类号：
摘要：
The evolution of transverse cracking in a cross-ply laminate which deforms viscoelastically is investigated. A model predicting the strain under creep loading is established by a combination of the viseoelasticity theory, shear lag analysis and delayed failure concept. The creep strain and transverse crack density of the cross-ply laminates are measured during creep tests. Two stages of time for transverse cracking are observed in the creep tests. Predicted creep strains using the present model agree well with the experimental ones.
引用
下载
收藏
页码：760 / 769
页数：10
相关论文
共 50 条
  • [31] On transverse matrix cracking in cross-ply laminates loaded in simple bending
    Smith, PA
    Ogin, SL
    COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 1999, 30 (08) : 1003 - 1008
  • [32] Effect of ply thickness on transverse crack initiation in CFRP cross-ply laminates under fatigue loading
    Kurihara, Ken
    Hosoi, Atsushi
    Sato, Narumichi
    Kawada, Hiroyuki
    Nihon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A, 2013, 79 (799): : 249 - 265
  • [33] Transverse cracking in CFRP cross-ply laminates with interlaminar resin layers
    Ogihara, S
    Takeda, N
    Kobayashi, A
    ADVANCED COMPOSITE MATERIALS, 1998, 7 (04) : 347 - 363
  • [34] Statistical modeling for the accumulation of transverse matrix cracking in cross-ply laminates
    Wang, Fang
    Li, Lu
    Chen, Zhiqian
    Zeng, Xiangguo
    POLYMER COMPOSITES, 2012, 33 (06) : 912 - 917
  • [35] Statistical analysis of the progression of transverse cracking and delamination in cross-ply laminates
    Berthelot, JM
    Le Corre, JF
    COMPOSITES SCIENCE AND TECHNOLOGY, 2000, 60 (14) : 2659 - 2669
  • [36] Experimental and analytical characterization of transverse cracking behavior in carbon/bismaleimide cross-ply laminates under mechanical fatigue loading
    Kobayashi, S
    Takeda, N
    COMPOSITES PART B-ENGINEERING, 2002, 33 (06) : 471 - 478
  • [37] Matrix cracking and delamination evolution in composite cross-ply laminates
    Rebiere, Jean-Luc
    COGENT ENGINEERING, 2014, 1 (01):
  • [38] Development of transverse cracking in cross-ply laminates during fatigue tests
    Berthelot, JM
    El Mahi, A
    Le Corre, JF
    COMPOSITES SCIENCE AND TECHNOLOGY, 2001, 61 (12) : 1711 - 1721
  • [39] Stiffness degradation in cross-ply laminates damaged by transverse cracking and splitting
    Kashtalyan, M
    Soutis, C
    COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2000, 31 (04) : 335 - 351
  • [40] Saturation of transverse cracking with delamination in polymer cross-ply composite laminates
    Dharani, LR
    Wei, J
    Ji, FS
    INTERNATIONAL JOURNAL OF DAMAGE MECHANICS, 2003, 12 (02) : 89 - 114
12345