Improvement of oxidation resistance of Ti-47Al-2W-0.5Si alloy modified by aluminizing method

被引：21

作者：

Szkliniarz, Agnieszka ^{[1
]}

Moskal, Grzegorz ^{[1
]}

Szkliniarz, Wojciech ^{[1
]}

Swadzba, Radoslaw ^{[2
]}

机构：

[1] Silesian Tech Univ, Dept Mat Sci & Met, PL-40019 Katowice, Poland

[2] Inst Ferrous Met, PL-44100 Gliwice, Poland

来源：

SURFACE & COATINGS TECHNOLOGY | 2015年 / 277卷

关键词：

Titanium aluminides; TiAl based alloy; Protective coatings; Oxidation; Out-of-pack method; CYCLIC OXIDATION; COATINGS; MICROSTRUCTURE; BEHAVIOR;

D O I：

10.1016/j.surfcoat.2015.07.072

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

The presented study defines the impact of aluminizing process by out-of-pack method on the oxidation resistance of cast Ti-47Al-2W-0.5Si alloy after homogenising and hot isostatic pressing. The surface condition was characterized, as well as chemical and phase composition of scale formed on examined alloy with and without protective coating, when subjected to cyclic oxidation at 950 degrees C. It was established that the generated hermetic and compact aluminium diffusion coating with a thickness of about 7.5 mu m, consisting mainly of TiAl2 phase, has a significant effect on the improvement of cyclic oxidation resistance in the case of investigated alloy. It was confirmed that the scale formed after the oxidation process on the surface of alloy with protective coating was composed mainly of Al2O3 oxide, contrary to the scale formed on the alloy without protective coating, which was mainly consisting of TiO2 oxide. (C) 2015 Elsevier B.V. All rights reserved.

引用

页码：270 / 277

页数：8

共 50 条

[31] Microstructure evolution of directionally solidified Ti-46Al-0.5W-0.5Si alloy
Fan, Jianglei
Li, Xinzhong
Su, Yanqing
Chen, Ruirun
Guo, Jingjie
Fu, Hengzhi
JOURNAL OF CRYSTAL GROWTH, 2011, 337 (01) : 52 - 59
[32] High temperature oxidation of Ti-46Al-6Nb-0.5W-0.5Cr-0.3Si-0.1C alloy
Park, Soon Yong
Seo, D. Y.
Kim, Seong Woong
Kim, Seung Eon
Hong, Jae Keun
Lee, Dong Bok
INTERMETALLICS, 2016, 74 : 8 - 14
[33] Precipitation hardening of the fully lamellar structure of investment cast Ti-47Al-2Nb-1Mn-0.5Mo-0.5W-0.2Si alloy
Chen, WR
Zhao, L
Beddoes, J
SCRIPTA MATERIALIA, 1999, 41 (06) : 597 - 603
[34] Comparison of microstructures and mechanical properties of as-cast and directionally solidified Ti-47Al-1W-0.5Si alloy
Liu, T.
Luo, L. S.
Zhang, D. H.
Wang, L.
Li, X. Z.
Chen, R. R.
Su, Y. Q.
Guo, J. J.
Fu, H. Z.
JOURNAL OF ALLOYS AND COMPOUNDS, 2016, 682 : 663 - 671
[35] Directional solidification of intermetallic Ti-46Al-2W-0.5Si alloy in alumina moulds
Lapin, J
Ondrús, L
Nazmy, M
INTERMETALLICS, 2002, 10 (10) : 1019 - 1031
[36] Softening produced by the microstructural instability of the intermetallic alloy Ti-46.5Al-2W-0.5Si
Muñoz-Morris, MA
Fernández, IG
Morris, DG
SCRIPTA MATERIALIA, 2002, 46 (08) : 617 - 622
[37] Influence of silicide on fracture behavior of a fully lamellar Ti-46Al-0.5W-0.5Si alloy
Chen Hui1
2.College of Electromechanical Engineering
China Foundry, 2012, (02) : 108 - 113
[38] Influence of silicide on fracture behavior of a fully lamellar Ti-46Al-0.5W-0.5Si alloy
Chen HuiSu YanqingLuo LiangshunLi XinzhongWang ZhantaoGuo Jingjieand Fu Hengzhi School of Materials Science and EngineeringHarbin Institute of TechnologyHarbin ChinaCollege of Electromechanical EngineeringNortheast Forestry UniversityHarbin China
China Foundry, 2012, 9 (02) : 108 - 113
[39] Influence of silicide on fracture behavior of a fully lamellar Ti-46Al-0.5W-0.5Si alloy
Chen Hui
Su Yanqing
Luo Liangshun
Li Xinzhong
Wang Zhantao
Guo Jingjie
Fu Hengzhi
CHINA FOUNDRY, 2012, 9 (02) : 108 - 113
[40] On the orientation relationship between α2 precipitates and the B2 phase in a Ti-47 at. % Al-2 at. % W-0.5 at.% Si alloy
Yu, R
He, LL
Ye, HQ
Guo, JT
PHILOSOPHICAL MAGAZINE LETTERS, 2001, 81 (02) : 71 - 76

← 1 2 3 4 5 →