FRACTURE ANALYSIS OF THERMAL BARRIER COATING SYSTEMS UNDER THERMAL SHOCK

被引：1
|
作者：
Zhang Yan-Yan [1 ,3 ]
Shen Ri-Lin [2 ]
Huang Kai [2 ]
Yue Xiao-Ning [1 ]
机构：
[1] Shenyang Univ, Dept Phys, Shenyang 110000, Peoples R China
[2] Harbin Inst Technol, Sch Astronaut, Harbin 150001, Peoples R China
[3] Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang 110000, Peoples R China
来源：
CERAMICS-SILIKATY | 2017年 / 61卷 / 01期
关键词：
Thermal barrier coatings (TBCs); Interaction energy integral method (IEIM); Transient thermal stress intensity factors (TSIFs); Crack growth law; STRESS INTENSITY FACTORS; INTERFACE CRACK;
D O I：
10.13168/cs.2016.0061
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
In order to understand the thermal fracture properties of thermal barrier coating (IBC) systems, transient thermal stress intensity factors (TSIFs) are calculated by using the transient interaction energy integral method (IEIM) when a thermal shock load is applied. In this study, continuous and weak interfaces are studied. considering different distributions of the material properties and their derivatives in the interface. The effect of the interface bonding strength on TSIFs at crack tip of TBC systems with multiple interfaces is analysed. This method provides an avenue to simulate interfacial properties subjected to thermal shock loads.
引用
收藏
页码：59 / 64
页数：6
相关论文
共 50 条
  • [31] Failure Mechanism for Thermal Fatigue of Thermal Barrier Coating Systems
    C. Giolli
    A. Scrivani
    G. Rizzi
    F. Borgioli
    G. Bolelli
    L. Lusvarghi
    Journal of Thermal Spray Technology, 2009, 18 : 223 - 230
  • [32] Investigation of thermal fatigue behavior of thermal barrier coating systems
    Zhu, DM
    Miller, RA
    SURFACE & COATINGS TECHNOLOGY, 1997, 94-5 (1-3): : 94 - 101
  • [33] Thermal shock testing of burner cans coated with a thick thermal barrier coating
    P. Bengtsson
    T. Ericsson
    J. Wigren
    Journal of Thermal Spray Technology, 1998, 7 : 340 - 348
  • [34] Long crack behavior in a thermal barrier coating upon thermal shock loading
    Liu, Y
    Persson, C
    Melin, S
    Wigren, J
    JOURNAL OF THERMAL SPRAY TECHNOLOGY, 2005, 14 (02) : 258 - 263
  • [35] Thermal shock experiment and simulation of ceramic/metal gradient thermal barrier coating
    Xiao, Jinsheng
    Liu, Kun
    Zhao, Wenhua
    Fu, Weibiao
    High-Performance Ceramics IV, Pts 1-3, 2007, 336-338 : 1818 - 1821
  • [36] Long crack behavior in a thermal barrier coating upon thermal shock loading
    Y. Liu
    C. Persson
    S. Melin
    J. Wigren
    Journal of Thermal Spray Technology, 2005, 14 : 258 - 263
  • [37] Thermal shock testing of burner cans coated with a thick thermal barrier coating
    Bengtsson, P
    Ericsson, T
    Wigren, J
    JOURNAL OF THERMAL SPRAY TECHNOLOGY, 1998, 7 (03) : 340 - 348
  • [38] Thermal shock testing of burner cans coated with a thick thermal barrier coating
    Bengtsson, P.
    Ericsson, T.
    Wigren, J.
    1998, ASM International, Materials Park, OH, United States (07)
  • [39] Laser Thermal Gradient Testing and Fracture Mechanics Study of a Thermal Barrier Coating
    Yingsang Wu
    Pei-feng Hsu
    Yao Wang
    Mary Helen McCay
    D. Edward Croy
    David Moreno
    Lei He
    Chao Wang
    Hongqi Zhang
    Journal of Thermal Spray Technology, 2019, 28 : 1239 - 1251
  • [40] Laser Thermal Gradient Testing and Fracture Mechanics Study of a Thermal Barrier Coating
    Wu, Yingsang
    Hsu, Pei-feng
    Wang, Yao
    McCay, Mary Helen
    Croy, D. Edward
    Moreno, David
    He, Lei
    Wang, Chao
    Zhang, Hongqi
    JOURNAL OF THERMAL SPRAY TECHNOLOGY, 2019, 28 (06) : 1239 - 1251
12345