TRANSFORMATION KINETICS AND FERRITE-PEARLITE RATIOS IN A 65-45-12 DUCTILE IRON

被引：5
|
作者：
Samuel, C. [1 ]
Viswanathan, S. [1 ]
机构：
[1] Univ Alabama, Dept Met & Mat Engn, Tuscaloosa, AL 35487 USA
来源：
INTERNATIONAL JOURNAL OF METALCASTING | 2008年 / 2卷 / 04期
关键词：
dilatometry; transformation kinetics; ductile iron; pearlite; ferrite; austenite;
D O I：
10.1007/BF03355436
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
Dilatometry has been extensively used to study the transformation behavior of steels. This paper outlines the use of Gleeble dilatometry to characterize the transformation kinetics and ferrite-pearlite ratios it? a 65-45-12 ductile iron. Samples were heated to 900(sic)C (1650(sic)F) and cooled at constant cooling rates ranging from 2 to 2000(sic)C/min (3.6 to 3600(sic)F/min). The dilatometer results were analyzed and transformation temperatures and the ferrite-pearlite ratio in the final microstructure were determined. The information was also used to estimate the continuous-cooling-transformation (CCT) curve for 65-45-12 ductile iron. The agreement between the ferrite-pearlite ratio predicted from the dilatometry results and metallographic analysis of dilatometry specimens was excellent.
引用
收藏
页码：55 / +
页数：10
相关论文
共 50 条
  • [31] Refinement of ferrite-pearlite structures through transformation from heavily deformed austenite in a low carbon Si-Mn steel
    Torizuka, S
    Umezawa, O
    Tsuzaki, K
    Nagai, K
    PROCEEDINGS OF THE INTERNATIONAL CONFERENCE ON MICROALLOYING IN STEELS, 1998, 284-2 : 225 - 230
  • [32] Effect of silicon content on transformation kinetics of austempered ductile iron
    Mallia, J
    Grech, M
    Smallman, RE
    MATERIALS SCIENCE AND TECHNOLOGY, 1998, 14 (05) : 452 - 460
  • [33] Effect of Copper and Nickel on the Transformation Kinetics of Austempered Ductile Iron
    Gorny, Marcin
    Tyrala, Edward
    Lopez, Hugo
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2014, 23 (10) : 3505 - 3510
  • [34] Effect of Copper and Nickel on the Transformation Kinetics of Austempered Ductile Iron
    Marcin Górny
    Edward Tyrała
    Hugo Lopez
    Journal of Materials Engineering and Performance, 2014, 23 : 3505 - 3510
  • [35] Transformation kinetics of unalloyed and high Mn austempered ductile iron
    Ahmadabadi, MN
    Farjami, S
    MATERIALS SCIENCE AND TECHNOLOGY, 2003, 19 (05) : 645 - 649
  • [36] The Synergy Between Cement Spheroidization and Cu Alloying on the Corrosion Resistance of Ferrite-Pearlite Steel in Acid Chloride Solution (vol 84, pg 65, 2021)
    Dong, Junhua
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2021, 95 : 180 - 180
  • [37] In-situ measurement of phase transformation kinetics in austempered ductile iron
    Meier, Leopold
    Hofmann, Michael
    Saal, Patrick
    Volk, Wolfram
    Hoffmann, Hartmut
    MATERIALS CHARACTERIZATION, 2013, 85 : 124 - 133
  • [38] Solid state transformation kinetics of high nodule count ductile iron
    Massone, JM
    Boeri, RE
    Sikora, JA
    INTERNATIONAL JOURNAL OF CAST METALS RESEARCH, 2003, 16 (1-3) : 179 - 184
  • [39] Influence of magnetic field on the kinetics of proeutectoid ferrite transformation in iron alloys
    M. Enomoto
    H. Guo
    Y. Tazuke
    Y. R. Abe
    M. Shimotomai
    Metallurgical and Materials Transactions A, 2001, 32 : 445 - 453
  • [40] Influence of magnetic field on the kinetics of proeutectoid ferrite transformation in iron alloys
    Enomoto, M
    Guo, H
    Tazuke, Y
    Abe, YR
    Shimotomai, M
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2001, 32 (03): : 445 - 453
12345