Low temperature spark plasma sintering of Al2O3-TiC composites

被引：19
|
作者：
Meir, S. [1 ]
Kalabukhov, S. [1 ]
Hayun, S. [1 ]
机构：
[1] Ben Gurion Univ Negev, Dept Mat Engn, IL-84105 Beer Sheva, Israel
来源：
CERAMICS INTERNATIONAL | 2014年 / 40卷 / 08期
关键词：
Aluminum oxide; Ceramic composite; Spark plasma sintering (SPS); Titanium carbide; MECHANICAL-PROPERTIES; MICROSTRUCTURE; TOOLS;
D O I：
10.1016/j.ceramint.2014.04.059
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
Al2O3-TiC composites were fabricated using spark plasma sintering (SPS) technology between 1300 degrees C and 1500 degrees C. The composite densification process starts at 950 degrees C, with a maximum densification rate at 1170 degrees C. After thirty minutes soaking at 1400 degrees C, a relative density of 99.5% was achieved. Microstructure analysis reveals a submicron Al2O3 grain size and homogenous distribution of titanium carbide in the matrix. The fully dense Al2O3-20 wt% TiC composite exhibits high values of fracture toughness (8.3 MPa m(1/2)), Young's modulus (406 GPa), flexural strength (850 MPa) and hardness (21 GPa). (C) 2014 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
引用
收藏
页码：12187 / 12192
页数：6
相关论文
共 50 条
  • [1] Synthesis and characterization of Al2O3-TiC nano-composite by spark plasma sintering
    Kumar, Rohit
    Chaubey, A. K.
    Bathula, Sivaiah
    Jha, B. B.
    Dhar, Ajay
    INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2016, 54 : 304 - 308
  • [2] Al2O3-TiC Composite Prepared by Spark Plasma Sintering Process: Evaluation of Mechanical and Tribological Properties
    Kumar, Rohit
    Chaubey, A. K.
    Bathula, Sivaiah
    Prashanth, K. G.
    Dhar, Ajay
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2018, 27 (03) : 997 - 1004
  • [3] Al2O3-TiC/Al in-situ composites prepared by high-temperature reaction sintering
    Cheng, Xiulan
    Pan, Fusheng
    Tang, Aitao
    Chen, Fengchu
    Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals, 1999, 9 (02): : 313 - 318
  • [4] Al2O3-TiC Composite Prepared by Spark Plasma Sintering Process: Evaluation of Mechanical and Tribological Properties
    Rohit Kumar
    A. K. Chaubey
    Sivaiah Bathula
    K. G. Prashanth
    Ajay Dhar
    Journal of Materials Engineering and Performance, 2018, 27 : 997 - 1004
  • [5] Microstructure and properties of Al2O3-TiC composites fabricated by combination of high-energy ball milling and spark plasma sintering (SPS)
    Zhang, YF
    Wang, LJ
    Jiang, W
    Chen, LD
    JOURNAL OF INORGANIC MATERIALS, 2005, 20 (06) : 1445 - 1449
  • [6] The Effect of TiC Content and Sintering Temperature on Mechanical Property of Al2O3-TiC Composite Ceramics
    柳军旺
    郭英奎
    石春艳
    哈尔滨理工大学学报, 2008, (06) : 114 - 116
  • [7] RAPID RATE SINTERING OF AL2O3-TIC COMPOSITES FOR CUTTING-TOOL APPLICATIONS
    LEE, MY
    BOROM, MP
    ADVANCED CERAMIC MATERIALS, 1988, 3 (01): : 38 - 44
  • [8] Preparation, microstructures and properties of Al2O3-TiC composites
    Cai, KF
    McLachlan, DS
    Axen, N
    Manyatsa, R
    CERAMICS INTERNATIONAL, 2002, 28 (02) : 217 - 222
  • [9] Sintering of Al2O3-TiC composite in the presence of liquid phase
    Chae, Ki-Woong, 1600, American Ceramic Soc, Westerville, OH, United States (78):
  • [10] PRESSURELESS-SINTERED AL2O3-TIC COMPOSITES
    CUTLER, RA
    HURFORD, AC
    VIRKAR, AV
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1988, 105 : 183 - 192
12345