Corrosion behavior of pre-oxidized Ni-Ti alloys in eutectic (Li, K)2CO3 mixture at 650 °C

被引：0
|
作者：
Zeng, CL [1 ]
Zhou, T [1 ]
Wu, WT [1 ]
机构：
[1] Chinese Acad Sci, Met Res Inst, State Key Lab Corros & Protect, Shenyang 110016, Peoples R China
来源：
JOURNAL OF MATERIALS SCIENCE LETTERS | 2002年 / 21卷 / 12期
基金：
中国国家自然科学基金;
关键词：
D O I：
10.1023/A:1016053102137
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The corrosion behavior of pre-oxidized Ni-Ti alloys in eutectic (Li, K)2CO3 at 650°C was studied. It was found that NiO formed beneath the TiO2 layer. This was attributed to the presence of cracks across the TiO2 layer that formed during pre-oxidation treatment.
引用
收藏
页码：907 / 909
页数：3
相关论文
共 50 条
  • [31] The corrosion behaviour of iron and chromium in molten (Li0.62K0.38)2CO3
    Biedenkopf, P
    Spiegel, M
    Grabke, HJ
    ELECTROCHIMICA ACTA, 1998, 44 (04) : 683 - 692
  • [32] Alkali insertion within NiO/Ni electrode in contact with molten Li2CO3-K2CO3 and Li2CO3-Na2CO3-K2CO3 at 650 degrees C
    Malinowska, B
    Cassir, M
    Devynck, J
    JOURNAL OF POWER SOURCES, 1996, 63 (01) : 27 - 32
  • [33] Corrosion behavior of stainless steel in molten Li2CO3-Na2CO3 eutectic
    Matsumoto, K
    Matsuoka, A
    Nakagawa, K
    Takizawa, K
    DENKI KAGAKU, 1997, 65 (01): : 44 - 50
  • [34] Corrosion of steel alloys in eutectic NaCl + Na2CO3 at 700 οC and Li2CO3 + K2CO3 + Na2CO3 at 450 οC for thermal energy storage
    Sarvghad, Madjid
    Steinberg, Theodore A.
    Will, Geoffrey
    SOLAR ENERGY MATERIALS AND SOLAR CELLS, 2017, 170 : 48 - 59
  • [35] Kinetics of the hydrogen electrode of a fuel cell with eutectic molten electrolyte (Li, K)2CO3 at 923 K in a coulostatic experiment
    V. N. Nekrasov
    N. N. Batalov
    A. V. Sofinskii
    M. A. Zvezdkin
    Russian Journal of Electrochemistry, 2000, 36 : 965 - 969
  • [36] Kinetics of the hydrogen electrode of a fuel cell with eutectic molten electrolyte (Li, K)2CO3 at 923 K in a coulostatic experiment
    Nekrasov, VN
    Batalov, NN
    Sofinskii, AV
    Zvezdkin, MA
    RUSSIAN JOURNAL OF ELECTROCHEMISTRY, 2000, 36 (09) : 965 - 969
  • [37] Water vapour effects on corrosion of Ni-Cr alloys in CO2 gas at 650 °C
    Xie, Yun
    Zhang, Jianqiang
    Young, David J.
    CORROSION SCIENCE, 2018, 136 : 311 - 325
  • [38] Oxidation of powder and ceramic UO2 by KClO3 in molten (Li-Na-K)2CO3 eutectic
    Volkovich, VA
    Griffiths, TR
    Fray, DJ
    Fields, M
    Thied, RC
    JOURNAL OF THE CHEMICAL SOCIETY-FARADAY TRANSACTIONS, 1998, 94 (17): : 2623 - 2625
  • [39] Fe-Cr合金在650℃熔融（Li-K）2CO3中的腐蚀行为
    曾潮流
    王文
    吴维
    金属学报, 2000, (06) : 651 - 654
  • [40] THE EFFECT OF SULFUR ON THE ANODIC H-2 (NI) ELECTRODE IN FUSED LI2CO3-K2CO3 AT 650-DEGREES-C
    VOGEL, WM
    SMITH, SW
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1982, 129 (07) : 1441 - 1445
12345