Corrosion behavior of pre-oxidized Ni-Ti alloys in eutectic (Li, K)2CO3 mixture at 650 °C

被引：0
|
作者：
Zeng, CL [1 ]
Zhou, T [1 ]
Wu, WT [1 ]
机构：
[1] Chinese Acad Sci, Met Res Inst, State Key Lab Corros & Protect, Shenyang 110016, Peoples R China
来源：
JOURNAL OF MATERIALS SCIENCE LETTERS | 2002年 / 21卷 / 12期
基金：
中国国家自然科学基金;
关键词：
D O I：
10.1023/A:1016053102137
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The corrosion behavior of pre-oxidized Ni-Ti alloys in eutectic (Li, K)2CO3 at 650°C was studied. It was found that NiO formed beneath the TiO2 layer. This was attributed to the presence of cracks across the TiO2 layer that formed during pre-oxidation treatment.
引用
收藏
页码：907 / 909
页数：3
相关论文
共 50 条
  • [1] Corrosion of Ni-Ti alloys in the molten (Li,K)2CO3 eutectic mixture
    Zeng, CL
    Wu, WT
    CORROSION SCIENCE, 2002, 44 (01) : 1 - 12
  • [2] Effect of pre-oxidation treatment on the corrosion behaviour of Ni-Ti alloys in eutectic (Li, K)2CO3 mixture at 650°C
    Zeng, CL
    Zhou, T
    Wu, WT
    CORROSION ENGINEERING SCIENCE AND TECHNOLOGY, 2004, 39 (02) : 152 - 156
  • [3] The corrosion behavior of two-phase Ni-Dy alloys in a eutectic (Li,K)2CO3 mixture at 650 ○C
    Zeng, CL
    Zhang, T
    Guo, PY
    Wu, WT
    CORROSION SCIENCE, 2004, 46 (09) : 2183 - 2189
  • [4] Electrochemical impedance of two-phase Ni-Ti alloys during corrosion in eutectic (0.62Li, 0.38K)2CO3 at 650 °C
    Zeng, CL
    Guo, PY
    Wu, WT
    ELECTROCHIMICA ACTA, 2004, 49 (14) : 2271 - 2277
  • [5] The Corrosion Behavior of Ni-Y Binary Alloys in Air and in Molten (0.62Li,0.38K)2CO3 Mixture at 650℃
    郭平义
    Journal of Wuhan University of Technology(Materials Science), 2009, (S1) : 115 - 118
  • [6] Study of the corrosion of Fe-Cr alloys in molten (Li-K)2CO3 at 650 °C
    Zeng, Chaoliu
    Wang, Wen
    Wu, Weitao
    Jinshu Xuebao/Acta Metallurgica Sinica, 2000, 36 (06): : 651 - 654
  • [7] Electrochemical impedance study of the corrosion of Fe-Cr alloys in molten (Li,K)2CO3 eutectic mixture
    Zeng, CL
    Wang, W
    Niu, Y
    Wu, WT
    HIGH TEMPERATURE CORROSION AND PROTECTION OF MATERIALS 5, PTS 1 AND 2, 2001, 369-3 : 809 - 816
  • [8] Galvanic corrosion in molten salts:: A discussion of the corrosion mechanism of two-phase Ni-20Cr-20/30Cu alloys in eutectic (Li,K)2CO3 at 650°C
    Zeng, CL
    Li, J
    Zhou, T
    OXIDATION OF METALS, 2005, 64 (3-4): : 207 - 218
  • [9] Galvanic Corrosion in Molten Salts: A Discussion of the Corrosion Mechanism of Two-Phase Ni–20Cr–20/30Cu Alloys in Eutectic (Li,K)2CO3 at 650°C
    C. L. Zeng
    J. Li
    T. Zhou
    Oxidation of Metals, 2005, 64 : 207 - 218
  • [10] CORROSION OF IRON IN (LI0.62K0.38)2CO3 AT 650-DEGREES-C
    HSU, HS
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1986, 133 (03) : C116 - C116
12345