Heavy ion irradiation-induced microstructural evolution in pyrochlore Lu2Ti2O7 at room temperature and 723 K

被引：10
|
作者：
Xie, Q. R. [1 ]
Zhang, J. [1 ]
Dong, X. N. [1 ]
Guo, Q. X. [1 ]
Li, N. [1 ]
机构：
[1] Xiamen Univ, Coll Energy, Xiamen 361005, Fujian, Peoples R China
来源：
JOURNAL OF SOLID STATE CHEMISTRY | 2015年 / 231卷
基金：
中国国家自然科学基金;
关键词：
Phase transformation; Nano-crystal; Ion irradiation; PHASE; AMORPHIZATION; CERAMICS; DAMAGE;
D O I：
10.1016/j.jssc.2015.08.005
中图分类号：
O61 [无机化学];
学科分类号：
070301 ; 081704 ;
摘要：
Polycrystalline pyrochlore Lu2Ti2O7 pellets were irradiated with 600 key Kr3+ at room temperature and 723 K to a fluence of 4 x 10(15) ions/cm(2), corresponding to an average ballistic damage dose of 10 displacements per atom in the peak damage region. Irradiation-induced microstructural evolution was examined by grazing incidence X-ray diffraction, and cross-sectional transmission electron microscopy. Incomplete amorphization was observed in the sample irradiated at room temperature due to the formation of nano-crystal which has the identical structure of pyrochlore, and the formation of nano-crystal is attributed to the mechanism of epitaxial recrystallization. However, an ordered pyrochlore phase to a swelling disordered fluorite phase transformation is occurred for the Lu2Ti2O7 sample irradiated at 723 K, which is due to the disordering of metal cations and anion vacancies. (C) 2015 Elsevier Inc. All rights reserved.
引用
收藏
页码：159 / 162
页数：4
相关论文
共 50 条
  • [11] Ionic conduction of a high-temperature modification of Lu2Ti2O7
    A. V. Shlyakhtina
    A. E. Ukshe
    L. G. Shcherbakova
    Russian Journal of Electrochemistry, 2005, 41 : 265 - 269
  • [12] Heat Capacity of the Gd2Ti2O7 and Lu2Ti2O7 Pyrochlores in the Range 350–1000 K
    L. T. Denisova
    L. G. Chumilina
    V. V. Ryabov
    Yu. F. Kargin
    N. V. Belousova
    V. M. Denisov
    Inorganic Materials, 2019, 55 : 477 - 481
  • [13] Pressure-induced phase transition of Lu2Ti2O7 and Lu1.5Ce0.5Ti2O7+x pyrochlores
    Xu, Min
    Niu, Jingjing
    Wu, Guanfeng
    Liao, Qian
    Tan, Xi
    Yang, Dongyan
    Liu, Longcheng
    Li, Yuhong
    Xia, Yue
    JOURNAL OF PHYSICS-CONDENSED MATTER, 2024, 36 (16)
  • [14] Synthesis of Lu2Ti2O7 powders by molten salt method
    Li, Bao-rang
    Chang, Hui-bin
    Liu, Dong-yu
    Yuan, Xiao-na
    MATERIALS CHEMISTRY AND PHYSICS, 2011, 130 (1-2) : 755 - 759
  • [15] Heat Capacity of the Gd2Ti2O7 and Lu2Ti2O7 Pyrochlores in the Range 350-1000 K
    Denisova, L. T.
    Chumilina, L. G.
    Ryabov, V. V.
    Kargin, Yu. F.
    Belousova, N. V.
    Denisov, V. M.
    INORGANIC MATERIALS, 2019, 55 (05) : 477 - 481
  • [16] Influences of calcining process on Lu2Ti2O7 powder morphology
    Gao, H. (gaohui880202@yahoo.com.cn), 2012, Chinese Ceramic Society, Baiwanzhuang, Beijing, 100831, China (41):
  • [17] Role of ion species in radiation effects of Lu2Ti2O7pyrochlore
    Li, Yuhong (liyuhong@lzu.edu.cn), 1600, Elsevier Ltd (693):
  • [18] Effects of Sintering and Annealing Temperature on Fabrication of Transparent Lu2Ti2O7 by Spark Plasma Sintering
    An, Liqiong
    Ito, Akihiko
    Goto, Takashi
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2011, 94 (11) : 3851 - 3855
  • [19] Heat Capacity and Thermodynamic Functions of Lutetium Titanate Lu2Ti2O7
    P. G. Gagarin
    A. V. Guskov
    V. N. Guskov
    A. V. Khoroshilov
    K. S. Gavrichev
    Russian Journal of Physical Chemistry A, 2025, 99 (3) : 409 - 419
  • [20] Synthesis and thermal properties of Lu2Ti2O7 nano-wires
    Li, Baorang
    Gao, Hui
    Guo, Yongquan
    Hou, Shixiang
    CRYSTENGCOMM, 2012, 14 (12): : 4168 - 4172
12345