Fracture toughness of thick plates of Ti-6Al-4V weldments

被引：0
|
作者：
Eizaguirre, I [1 ]
Santamaria, F [1 ]
Irisarri, AM [1 ]
Plaza, LM [1 ]
机构：
[1] INASMET, San Sebastian 20009, Spain
来源：
ECF 12: FRACTURE FROM DEFECTS, VOLS. I-III | 1998年
关键词：
D O I：
暂无
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
The fracture behaviour of thick plates of Ti-6Al-4V alloy joined by means of plasma are welding (PAW) and two different electron beam welding (EBW) procedures. In the whole temperature range PAW weld metal specimens exhibited higher toughness than base material. This behaviour has been attributed to the acicular microstructure of the weld metal compared to the equiaxic of parent alloy. EBW welded metals also showed higher toughness than base material although no so high as PAW ones. These results could be associated with the presence of a small volume fraction of brittle alpha prime martensite due to the higher cooling rate.
引用
收藏
页码：895 / 900
页数：6
相关论文
共 50 条
  • [31] Impact toughness and fracture analysis of linear friction welded Ti-6Al-4V alloy joints
    Ma, T. J.
    Li, W. -Y.
    Yang, S. Y.
    MATERIALS & DESIGN, 2009, 30 (06) : 2128 - 2132
  • [32] Effect of the Lattice Curvature of Ti-6Al-4V Titanium Alloy on Their Fatigue Life and Fracture Toughness
    Panin, V. E.
    Ovechkin, B. B.
    Khayrullin, R. R.
    Lider, A. M.
    Bordulev, Yu. S.
    Panin, A. V.
    Perevalova, O. B.
    Vlasov, I. V.
    PHYSICAL MESOMECHANICS, 2020, 23 (05) : 369 - 375
  • [33] Effect of the Lattice Curvature of Ti-6Al-4V Titanium Alloy on Their Fatigue Life and Fracture Toughness
    V. E. Panin
    B. B. Ovechkin
    R. R. Khayrullin
    A. M. Lider
    Yu. S. Bordulev
    A. V. Panin
    O. B. Perevalova
    I. V. Vlasov
    Physical Mesomechanics, 2020, 23 : 369 - 375
  • [34] HYDROGEN RELATED FATIGUE FRACTURE OF TI-6AL-4V
    KENNEDY, JR
    ADLER, PN
    SCHULTE, RL
    SCRIPTA METALLURGICA, 1980, 14 (03): : 299 - 304
  • [35] Spall fracture in additive manufactured Ti-6Al-4V
    Jones, D. R.
    Fensin, S. J.
    Dippo, O.
    Beal, R. A.
    Livescu, V.
    Martinez, D. T.
    Trujillo, C. P.
    Florando, J. N.
    Kumar, M.
    Gray, G. T., III
    JOURNAL OF APPLIED PHYSICS, 2016, 120 (13)
  • [36] THE EFFECT OF EXPOSURE ON FRACTURE OF TI-6AL-4V ALLOY
    BENDERSKY, L
    ROSEN, A
    ENGINEERING FRACTURE MECHANICS, 1980, 13 (01) : 111 - 118
  • [37] Creep failure mechanisms of a Ti-6Al-4V thick plate
    Seco, FJ
    Irisarri, AM
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2001, 24 (11) : 741 - 750
  • [38] Weld Quality Assessment in Fiber Laser Weldments of Ti-6Al-4V Alloy
    Chandan Kumar
    Manas Das
    C. P. Paul
    K. S. Bindra
    Journal of Materials Engineering and Performance, 2019, 28 : 3048 - 3062
  • [39] Effect of heat treatment on corrosion behavior of Ti-6Al-4V alloy weldments
    Karimzadeh, F.
    Heidarbeigy, M.
    Saatchi, A.
    JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2008, 206 (1-3) : 388 - 394
  • [40] Weld Quality Assessment in Fiber Laser Weldments of Ti-6Al-4V Alloy
    Kumar, Chandan
    Das, Manas
    Paul, C. P.
    Bindra, K. S.
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2019, 28 (05) : 3048 - 3062
12345