Electron-beam-induced deposition of copper compound with low resistivity

被引：26
|
作者：
Ochiai, Y
Fujita, J
Matsui, S
机构：
[1] Fundamental Research Laboratories, NEC Corporation, Tsukuba 305
来源：
JOURNAL OF VACUUM SCIENCE & TECHNOLOGY B | 1996年 / 14卷 / 06期
关键词：
D O I：
10.1116/1.588687
中图分类号：
TM [电工技术]; TN [电子技术、通信技术];
学科分类号：
0808 ; 0809 ;
摘要：
Electron-beam-induced deposition of copper was performed using hexafluoro-acetyoacetonate copper vinyl-trimethy-silane (HFA . Cu . VTMS) gas. The deposition was demonstrated by using a 30 keV environmental scanning electron microscope and a 50 keV electron beam Lithography system in an atmosphere of precursor gas: HFA . Cu . VTMS. The deposition rate, composition, and electrical resistivity of the deposited material were measured. The deposition rate was 6.6 nm/(C/cm(2)) at a pressure of 160 Pa. The resistivity was 3.6 mu Omega cm at room temperature deposited at a pressure of 6.7 x 10(-4) Pa. The resistivity is the lowest so far reported. (C) 1996 American Vacuum Society.
引用
收藏
页码：3887 / 3891
页数：5
相关论文
共 50 条
  • [41] Electron-beam-induced deposition of conductive nanostructures with carbon nanotube emitters
    Arai, F
    Liu, P
    Dong, L
    Nakajima, M
    Fukuda, T
    2003 THIRD IEEE CONFERENCE ON NANOTECHNOLOGY, VOLS ONE AND TWO, PROCEEDINGS, 2003, : 811 - 814
  • [42] TIPS FOR SCANNING TUNNELING MICROSCOPY PRODUCED BY ELECTRON-BEAM-INDUCED DEPOSITION
    HUBNER, B
    KOOPS, HWP
    PAGNIA, H
    SOTNIK, N
    URBAN, J
    WEBER, M
    ULTRAMICROSCOPY, 1992, 42 : 1519 - 1525
  • [43] Fabrication and properties of dot array using electron-beam-induced deposition
    Komuro, M.
    Hiroshima, H.
    Denshi Gijutsu Sogo Kenkyusho Iho/Bulletin of the Electrotechnical Laboratory, 1997, 61 (04):
  • [44] Repairing nanoscale devices using electron-beam-induced deposition of platinum
    Peeters, Lucas
    Keller, Andrew J.
    Umansky, Vladimir
    Mahalu, Diana
    Goldhaber-Gordon, David
    JOURNAL OF VACUUM SCIENCE & TECHNOLOGY B, 2015, 33 (05):
  • [45] Conditions for fabrication of highly conductive wires by electron-beam-induced deposition
    Hiroshima, H
    Suzuki, N
    Ogawa, N
    Komuro, M
    JAPANESE JOURNAL OF APPLIED PHYSICS PART 1-REGULAR PAPERS SHORT NOTES & REVIEW PAPERS, 1999, 38 (12B): : 7135 - 7139
  • [46] Fabrication and characterization of nanostructures on insulator substrates by electron-beam-induced deposition
    Song, Minghui
    Furuya, Kazuo
    SCIENCE AND TECHNOLOGY OF ADVANCED MATERIALS, 2008, 9 (02)
  • [47] Fabrication and functionalization of nanochannels by electron-beam-induced silicon oxide deposition
    Danelon, Christophe
    Santschi, Christian
    Brugger, Juergen
    Vogel, Horst
    LANGMUIR, 2006, 22 (25) : 10711 - 10715
  • [48] ELECTRON-BEAM-INDUCED PATTERNED DEPOSITION OF ALLYLCYCLOPENTADIENYL PALLADIUM USING STM
    SAULYS, DS
    ERMAKOV, A
    GARFUNKEL, EL
    DOWBEN, PA
    ABSTRACTS OF PAPERS OF THE AMERICAN CHEMICAL SOCIETY, 1994, 207 : 20 - COLL
  • [49] Purification of platinum and gold structures after electron-beam-induced deposition
    Botman, A.
    Mulders, J. J. L.
    Weemaes, R.
    Mentink, S.
    NANOTECHNOLOGY, 2006, 17 (15) : 3779 - 3785
  • [50] The Direct Writing of Plasmonic Gold Nanostructures by Electron-Beam-Induced Deposition
    Hoeflich, Katja
    Yang, Ren Bin
    Berger, Andreas
    Leuchs, Gerd
    Christiansen, Silke
    ADVANCED MATERIALS, 2011, 23 (22-23) : 2657 - +
12345