J-integral and plastic limit load of hole-edge crack in plate under biaxial loadings

被引：0
|
作者：
Zhang Yan-qing [1 ]
Wang Zhong-xian [1 ]
Xu Wei [1 ]
机构：
[1] Jiangsu Univ, Fac Civil Engn & Mech, Zhenjiang 212013, Jiangsu, Peoples R China
来源：
CHEMICAL, MATERIAL AND METALLURGICAL ENGINEERING III, PTS 1-3 | 2014年 / 881-883卷
关键词：
Hole-edge crack; elastic-plastic J-integral; Biaxial loading; Plastic limit load; SEMIELLIPTIC SURFACE CRACKS;
D O I：
10.4028/www.scientific.net/AMR.881.883.1412
中图分类号：
TQ [化学工业];
学科分类号：
0817 ;
摘要：
Elastic-plastic J-integral and plastic limit load were described by finite element (FE) analysis for single hole-edge crack in plate under far field biaxial load. In this paper, the effect of biaxial load ratio (from -1 to 1) on elastic-plastic J-integral and plastic limit load was studied, the values of coefficient h(1) for J-integral engineering estimation formulas were given and the effect of material hardening on plastic limit load was discussed. The result obtained from this work provides reference for fracture evaluation, so it can be used in engineering accurately and expediently.
引用
收藏
页码：1412 / 1415
页数：4
相关论文
共 50 条
  • [31] Effect of the accumulated plastic deformation on J-integral for TSV-Cu/SiO2 interface crack under cyclic thermal load
    Zhang, Min
    Qin, Fei
    Dai, Yanwei
    He, Hongwen
    Zheng, Jiantao
    Zhang, Hao
    Chen, Pei
    2020 21ST INTERNATIONAL CONFERENCE ON ELECTRONIC PACKAGING TECHNOLOGY (ICEPT), 2020,
  • [32] The effect of mechanical heterogeneity and limit load of a weld joint with longitudinal weld crack on the J-integral and failure assessment curve
    Welding Research Institute, School of Mechanical Engineering, Xi'an Jiaotong University, Province 710049, Xi'an Shaanxi, China
    不详
    Int. J. Press. Vessels Pip., 8 (625-632):
  • [33] DISTRIBUTION OF CRACK EXTENSION FORCE, THE J-INTEGRAL, ALONG A THROUGH-CRACK-FRONT OF A PLATE
    SAKATA, M
    AOKI, S
    KISHIMOTO, K
    TAKAGI, R
    INTERNATIONAL JOURNAL OF FRACTURE, 1983, 23 (03) : 187 - 200
  • [34] The effect of mechanical heterogeneity and limit load of a weld joint with longitudinal weld crack on the J-integral and failure assessment curve
    Lei, YP
    Shi, YW
    Murakawa, H
    Luo, Y
    INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING, 1998, 75 (08) : 625 - 632
  • [35] Vector J-integral analysis of crack initiation at the edge of complete sliding contact
    Mai, Lifeng
    Korsunsky, Alexander M.
    PROCEEDINGS OF THE ROYAL SOCIETY A-MATHEMATICAL PHYSICAL AND ENGINEERING SCIENCES, 2006, 462 (2070): : 1805 - 1820
  • [36] PIPE FRACTURE SAFETY ANALYSIS USING LIMIT LOAD AND J-INTEGRAL TECHNIQUES
    HAYS, RA
    GUDAS, JP
    VASSILAROS, MG
    NUCLEAR ENGINEERING AND DESIGN, 1986, 96 (2-3) : 225 - 243
  • [37] Numerical calculation of dynamic stress intensity factors for a single hole-edge slant crack in a finite plate
    Wang, Li-Qing
    Gai, Bing-Zheng
    Gongcheng Lixue/Engineering Mechanics, 2009, 26 (03): : 9 - 14
  • [38] Research on hole-edge stress distribution of composite materials plate with complex holes by integral equations method
    School of Mechanical Engineering, Zhengzhou University, Zhengzhou 450002, China
    J. Mech. Strength, 2006, 6 (931-936):
  • [39] Calculation of the energy J-integral in plastic zone ahead of a crack tip by infrared scanning
    Iziumova, A.
    Plekhov, O.
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2014, 37 (12) : 1330 - 1337
  • [40] Using J-integral analysis to predict the failure of HDPE pipes under crack face load and internal pressure
    Gaidi, Laouni
    Ouldyerou, Abdelhak
    Aminallah, Laid
    Merdji, Ali
    Roy, Sandipan
    Houari, Mohammed Sid Ahmed
    PROCEEDINGS OF THE INSTITUTION OF MECHANICAL ENGINEERS PART C-JOURNAL OF MECHANICAL ENGINEERING SCIENCE, 2024, 238 (12) : 5937 - 5944
12345