Fracture process zone of alumina WL-DCB specimen under cyclic loading

被引：0
|
作者：
Kokaly, MT [1 ]
Kobayashi, AS [1 ]
White, KW [1 ]
机构：
[1] Univ Washington, Dept Mech Engn, Seattle, WA 98195 USA
来源：
PROCEEDINGS OF THE SEM IX INTERNATIONAL CONGRESS ON EXPERIMENTAL MECHANICS | 2000年
关键词：
D O I：
暂无
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
The trailing fracture process zone (FPZ) of an alumina WL-DCB specimen subjected to cyclic loading was analyzed by a hybrid experimental-numerical procedure involving phase-shifting moire interferometry and finite element analysis. The residual crack opening profile at unloading continued to increase with cyclic loading until it matched the crack opening profile at maximum load. This anomaly is attributed to the increasing interference of the pulled out grains and provides a mechanistic explanation for the common notion that monolithic ceramics do not fatigue.
引用
收藏
页码：294 / 297
页数：4
相关论文
共 50 条
  • [31] Fracture of Parallel Strand Bamboo Composite under Mode I Loading: DCB Test Investigation
    Shen, Yurong
    Huang, Dongsheng
    Chui, Ying Hei
    Dai, Chunping
    ADVANCES IN MATERIALS SCIENCE AND ENGINEERING, 2019, 2019
  • [32] Damage accumulation in the pre-fracture zone under low-cyclic loading of specimens with the edge crack
    Kornev, Vladimir
    Karpov, Evgeniy
    Demeshkin, Alexander
    FATIGUE 2010, 2010, 2 (01): : 465 - 474
  • [33] Confinement Hoops of Compression Zone in Beam under Cyclic Loading
    Priastiwi, Yulita Arni
    Imran, Iswandi
    Nuroji
    Hidayat, Arif
    3RD INTERNATIONAL CONFERENCE ON CONSTRUCTION AND BUILDING ENGINEERING (ICONBUILD 2017), 2017, 1903
  • [34] Experimental and numerical investigations on fracture behaviours of cracked chevron notched Brazilian disc (CCNBD) sandstone specimen under cyclic loading
    Ma, Gang
    Li, Jiangteng
    Zhou, Xiang
    Chen, Jinci
    Zhang, Yan
    Qiu, Peitao
    ENGINEERING FRACTURE MECHANICS, 2022, 271
  • [35] EFFECT OF COMPRESSIVE STRESS ON FATIGUE OF ALUMINA UNDER UNIAXIAL CYCLIC LOADING
    KIM, KT
    SUH, J
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1993, 76 (01) : 229 - 231
  • [36] Experimental Study on Characteristics of Fatigue Damage of Coal Specimen under Cyclic Loading
    Yang Yongjie
    Xie Hongbing
    He Yanxin
    Hu Yongcan
    3RD INTERNATIONAL WORKSHOP ON MINE HAZARDS PREVENTION AND CONTROL, 2013, 94 : 432 - 437
  • [37] Experimental and Numerical Investigation on the Size of Damage Process Zone of a Concrete Specimen under Mixed-Mode Loading Conditions
    Shen, X. P.
    Feng, J. L.
    CMC-COMPUTERS MATERIALS & CONTINUA, 2010, 20 (02): : 185 - 203
  • [38] Prediction of brittle fracture in notched specimens under cyclic loading
    Iwashita, Tsutomu
    Azuma, Koji
    JOURNAL OF CONSTRUCTIONAL STEEL RESEARCH, 2019, 162
  • [39] Experimental Measurements of Shale Fracture Conductivity Under Cyclic Loading
    Honglian Li
    Jiren Tang
    Yiyu Lu
    Lei Zhou
    Shuaibin Han
    Rui Dai
    Arabian Journal for Science and Engineering, 2018, 43 : 6315 - 6324
  • [40] DEFORMATION AND TRANSVERSE FRACTURE OF RAILS UNDER CYCLIC FATIGUE LOADING
    TSVIGUN, VN
    CHELYSHEV, NA
    STEEL IN THE USSR, 1980, 10 (10): : 541 - 542
12345