Microstructural and corrosion behavior of MAO coated 5052 aluminum alloy

被引：9

作者：

Sunilraj, S. ^{[1
]}

Blessto, B. ^{[1
]}

Sivaprasad, K. ^{[1
]}

Muthupandi, V ^{[1
]}

机构：

[1] Natl Inst Technol, Dept Met & Mat Engn, Adv Mat Proc Lab, Tiruchirappalli 620015, Tamil Nadu, India

来源：

MATERIALS TODAY-PROCEEDINGS | 2021年 / 41卷

关键词：

Micro arc oxidation; AA5052; Corrosion morphology; Potentiodynamic polarization; TENSILE PROPERTIES; CERAMIC COATINGS; OXIDATION; RESISTANCE;

D O I：

10.1016/j.matpr.2020.08.755

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

In this paper, the morphology, phase composition and corrosion behavior of micro-arc oxidized 5052 aluminum alloy were analyzed. A uniform micro arc oxidation (MAO) coating was performed on 5052 aluminium alloy in different electrolytes (with and without borax additives) for 30 min. The MAO coating thickness was measured around 17-24 mu m and nanocrystalline gamma-Al2O3 were identified in the MAO coating using XRD analysis. The coating thickness was measured using the eddy current technique and morphology of the coating was analyzed using SEM. The coating formed in the electrolyte with borax showed reduced porosity compared to the sample coated without borax. The corrosion behavior is analyzed by Potentiodynamic polarization. The MAO coated sample offers higher corrosion resistance when compared to the uncoated specimen due to higher corrosion potential. (C) 2019 Elsevier Ltd. All rights reserved.

引用

页码：1120 / 1124

页数：5

共 50 条

[21] Effect of electromagnetic bulging on fatigue behavior of 5052 aluminum alloy
Wang, Du-zhen
Li, Ning
Han, Xiao-tao
Li, Liang
Liu, Lin
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2017, 27 (06) : 1224 - 1232
[22] Influence of surface roughness of substrate on corrosion behavior of MAO coated ZM5 Mg alloy
Li, Jianpeng
Bian, Yimin
Tu, Xiaohui
Li, Wei
Song, Dongdong
JOURNAL OF ELECTROANALYTICAL CHEMISTRY, 2022, 910
[23] Microstructural and Corrosion Properties of Burnished 6060 Aluminum Alloy
Logori, Debora
Pezzato, Luca
Settimi, Alessio Giorgio
Hanoz, Denise
Dabala, Manuele
APPLIED SCIENCES-BASEL, 2021, 11 (10):
[24] Investigating Corrosion Performance and Corrosive Wear Behavior of Sol–gel/MAO-Coated Mg Alloy
Yanhong Gu
Xinhua Zheng
Qi Liu
Huijuan Ma
Lei Zhang
Dawei Yang
Tribology Letters, 2018, 66
[25] Effect of TIG remelting on the microstructure, mechanical properties, and corrosion behavior of 5052 aluminum alloy joints in MIG welding
Wang, Hongduo
Chang, Suteng
Zhou, Zhiyong
Wang, Wen
JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2024, 32 : 2255 - 2267
[26] Microstructure and corrosion performance of zeolite/MAO-coated Al alloy
Xing, Jun
Chen, Yingjie
Yu, Chen-yun
Chen, Ming-an
SURFACE ENGINEERING, 2020, 36 (02) : 167 - 174
[27] Effect of the fluorination of DLC film on the corrosion protection of aluminum alloy (AA 5052)
Rangel, R. C. C.
Souza, M. E. P.
Schreiner, W. H.
Freire, C. M. A.
Rangel, E. C.
Cruz, N. C.
SURFACE & COATINGS TECHNOLOGY, 2010, 204 (18-19): : 3022 - 3028
[28] CORROSION BEHAVIOR OF A WC/C COATED 7075-T6 ALUMINUM ALLOY
Baragetti, S.
Dauru, M.
Gerosa, R.
Rivolta, B.
ADVANCES IN FRACTURE AND DAMAGE MECHANICS XII, 2014, 577-578 : 217 - +
[29] Corrosion behavior of zirconium diboride coated stainless steel in molten 6061 aluminum alloy
Wang, Qian
Wang, Wen Jun
Liu, Hui Jun
Zeng, Chao Liu
SURFACE & COATINGS TECHNOLOGY, 2017, 313 : 129 - 135
[30] Thickening behavior of 1050 aluminum and 5052 aluminum alloy sheets during incremental flattening
Department of Environmental Science and Technology, Faculty of Engineering, Shinshu University, 4-17-1 Wakasato, Nagano-shi, Nagano 380-8553, Japan
Keikinzoku J Jpn Inst Light Met, 2008, 10 (503-508):

← 1 2 3 4 5 →