Stress assisted oxide cracking of Zr-2.5Nb pressure tube material

被引：0
|
作者：
Gopalan, Avinash [1 ]
Sunil, Saurav [1 ]
Murty, T. N. [1 ]
Bind, A. K. [1 ]
Kumawat, B. K. [1 ]
Chandanshive, S. A. [1 ]
Singh, R. N. [1 ]
机构：
[1] Bhabha Atom Res Ctr BARC, Mech Met Div MMD, Mumbai 400085, Maharashtra, India
来源：
JOURNAL OF NUCLEAR MATERIALS | 2020年 / 536卷 / 536期
关键词：
DELAYED HYDRIDE CRACKING; DYNAMIC EMBRITTLEMENT; FRACTURE-TOUGHNESS; ALLOY; OXIDATION; ZIRCONIUM; GROWTH; NB; BEHAVIOR; TIP;
D O I：
10.1016/j.jnucmat.2020.152187
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The crack growth rates of un-irradiated and un-hydrided Zr-2.5Nb pressure tube material has been investigated in both air and in vacuum. Pre-cracked CCT samples made from pressure tube were tested in air atmosphere at 300 °C and 350 °C at different stress intensity factors. It was observed that till a particular stress intensity factor there is no crack growth and after which the crack growth rate increases with increase in stress intensity factor. For the test carried out in vacuum, it was observed that the crack growth rates for air is an order of magnitude higher than that of the crack growth obtained in the vacuum ambience. © 2020 Elsevier B.V.
引用
收藏
页数：9
相关论文
共 50 条
  • [21] Comparison of the measured and predicted crack propagation behaviour of Zr-2.5Nb pressure tube material
    Williams, B. W.
    St Lawrence, S.
    Leitch, B. W.
    ENGINEERING FRACTURE MECHANICS, 2011, 78 (18) : 3135 - 3152
  • [22] Analysis of steady-state thermal creep of Zr-2.5Nb pressure tube material
    N. Christodoulou
    C. K. Chow
    P. A. Turner
    C. N. Tomé
    R. J. Klassen
    Metallurgical and Materials Transactions A, 2002, 33 : 1103 - 1115
  • [23] The radial delayed hydride cracking behavior of Zr-2.5Nb alloy pressure tube at different temperatures
    Pan, Chunting
    Ming, Hongliang
    Shi, Xiuqiang
    Zhao, Guannan
    Bao, Yichen
    Meng, Fanjiang
    Wang, Jianqiu
    Han, En-Hou
    JOURNAL OF NUCLEAR MATERIALS, 2024, 601
  • [24] Effect of hydrogen isotopes on tensile and fracture properties of Zr-2.5Nb pressure tube material
    Bind, A. K.
    Singh, R. N.
    INTERNATIONAL JOURNAL OF FRACTURE, 2021, 227 (02) : 193 - 204
  • [25] Microstructural evolution in and flow properties of Zr-2.5Nb pressure tube material at elevated temperature
    Nene, S. S.
    Sharma, G.
    Singh, R. N.
    Kashyap, B. P.
    JOURNAL OF NUCLEAR MATERIALS, 2014, 449 (1-3) : 62 - 68
  • [26] Effect of specimen thickness on DHC velocity for Zr-2.5Nb alloy pressure tube material
    Sunil, S.
    Bind, A.K.
    Khandelwal, H.K.
    Singh, R.N.
    Chakravartty, J.K.
    Journal of Nuclear Materials, 2015, 467 : 373 - 382
  • [27] Neutron diffraction study of the precipitation and dissolution of hydrides in Zr-2.5Nb pressure tube material
    Root, JH
    Fong, RWL
    JOURNAL OF NUCLEAR MATERIALS, 1996, 232 (01) : 75 - 85
  • [28] Variations in nanomechanical properties of back-end Zr-2.5Nb pressure tube material
    Gallaugher, Matthew
    Peykov, Daniel
    Brodusch, Nicolas
    Chromik, Richard R.
    Rodrigue, Lisa
    Trudeau, Michel L.
    Gauvin, Raynald
    JOURNAL OF NUCLEAR MATERIALS, 2013, 442 (1-3) : 116 - 123
  • [29] Hydrogen ingress through EDM surfaces of Zr-2.5Nb pressure-tube material
    Chow, CK
    Brady, GR
    Urbanic, VF
    Coleman, CE
    JOURNAL OF NUCLEAR MATERIALS, 1998, 257 (01) : 35 - 43
  • [30] Analysis of steady-state thermal creep of Zr-2.5Nb pressure tube material
    Christodoulou, N
    Turner, PA
    Tomé, CN
    Chow, CK
    Klassen, RJ
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2002, 33 (04): : 1103 - 1115
12345