Delayed hydride crack growth study on irradiated Zr-2.5Nb pressure tube

被引：3
|
作者：
Shah, Priti Kotak [1 ]
Dubey, J. S. [1 ]
Kumar, Ashwini [1 ]
Shriwastaw, R. S. [1 ]
Rath, B. N. [1 ]
Pandit, K. M. [1 ]
Dhotre, M. P. [1 ]
Mishra, P. [1 ]
Alur, V. D. [1 ]
Anantharaman, S. [1 ]
机构：
[1] Bhabha Atom Res Ctr, Post Irradiat Examinat Div, Bombay 400085, Maharashtra, India
来源：
JOURNAL OF NUCLEAR MATERIALS | 2015年 / 460卷
关键词：
ZIRCALOY-2;
D O I：
10.1016/j.jnucmat.2015.01.046
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Delayed hydride crack (DHC) growth study was carried out on irradiated Indian Zr-2.5Nb pressure tube which had seen around 8 effective full power years of operation. Disc compact tension type specimens were used for the DHC tests at 210 degrees C, 250 degrees C, 265 degrees C and 290 degrees C. This paper discusses the test methodology, results generated and compares it with that obtained on the as-fabricated pressure tube of similar specification. (C) 2015 Elsevier B.V. All rights reserved.
引用
收藏
页码：1 / 4
页数：4
相关论文
共 50 条
  • [21] Anisotropic threshold stress intensity factor, KIH and crack growth rate in delayed hydride cracking of Zr-2.5Nb pressure tubes
    Kim, YS
    Kim, SS
    Kwon, SC
    Im, KS
    Cheong, YM
    [J]. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2002, 33 (03): : 919 - 925
  • [22] Anisotropic threshold stress intensity factor, KIH and crack growth rate in delayed hydride cracking of Zr-2.5Nb pressure tubes
    Young Suk Kim
    Sung Soo Kim
    Sang Chul Kwon
    Yong Moo Cheong
    Kyung Soo Im
    [J]. Metallurgical and Materials Transactions A, 2002, 33 : 919 - 925
  • [23] Anisotropic delayed hydride cracking velocity of CANDU Zr-2.5Nb pressure tubes
    Kim, Young Suk
    Cheong, Yong Moo
    [J]. JOURNAL OF NUCLEAR MATERIALS, 2008, 373 (1-3) : 179 - 185
  • [24] Crack tip stress effect on delayed hydride cracking velocity of Zr-2.5Nb tubes
    Kim, Young Suk
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 490 (1-2): : 146 - 150
  • [25] Delayed hydride cracking in Zr-2.5Nb tube with the cooling rate and the notch tip shape
    Kim, YS
    Kim, SJ
    Im, KS
    [J]. JOURNAL OF NUCLEAR MATERIALS, 2004, 335 (03) : 387 - 396
  • [26] Fracture toughness of irradiated Zr-2.5Nb pressure tube from Indian PHWR
    Shah, Priti Kotak
    Dubey, J. S.
    Shriwastaw, R. S.
    Dhotre, M. P.
    Bhandekar, A.
    Pandit, K. M.
    Anantharaman, S.
    Singh, R. N.
    Chakravartty, J. K.
    [J]. JOURNAL OF NUCLEAR MATERIALS, 2015, 458 : 319 - 325
  • [27] Initiation and Arrest of Delayed Hydride Cracking in Zr-2.5Nb Tubes
    Kim, Young S.
    [J]. JOURNAL OF PRESSURE VESSEL TECHNOLOGY-TRANSACTIONS OF THE ASME, 2009, 131 (01):
  • [28] Delayed Hydride Cracking Initiation at Notches in Zr-2.5Nb Alloys
    Cui, Jun
    Shek, Gordon K.
    Scarth, D. A.
    Wang, Zhirui
    [J]. JOURNAL OF PRESSURE VESSEL TECHNOLOGY-TRANSACTIONS OF THE ASME, 2009, 131 (04):
  • [29] The effect of texture on delayed hydride cracking in Zr-2.5Nb alloy
    Levi, MR
    Sagat, S
    [J]. ENVIRONMENTAL DEGRADATION OF MATERIALS AND CORROSION CONTROL IN METALS, 1999, : 323 - 335
  • [30] Effect of temperature on the delayed hydride cracking rate of Zr-2.5Nb alloy pressure tubes
    Pan, Chunting
    Zhao, Guannan
    Bao, Yichen
    Zhang, Zhiming
    Shi, Xiuqiang
    Meng, Fanjiang
    Wang, Jianqiu
    Ming, Hongliang
    [J]. JOURNAL OF NUCLEAR MATERIALS, 2024, 588
12345