Fractographic study of adhesion tested thermal barrier coatings subjected to isothermal and cyclic heat treatments

被引：6
|
作者：
Eriksson, R. [1 ]
Brodin, H. [1 ,2 ]
Johansson, S. [1 ]
Ostergren, L. [3 ]
Li, X. -H. [2 ]
机构：
[1] Linkoping Univ, Div Engn Mat, SE-58183 Linkoping, Sweden
[2] Siemens Ind Turbomachinery AB, SE-61283 Finspang, Sweden
[3] Volvo Aero Corp, SE-46181 Trollhattan, Sweden
来源：
11TH INTERNATIONAL CONFERENCE ON THE MECHANICAL BEHAVIOR OF MATERIALS (ICM11) | 2011年 / 10卷
关键词：
thermal barrier coatings; TBC; adhesion; fractography; thermal cycling fatigue; burner rig test; BOND STRENGTH; MECHANISMS; TOUGHNESS; BEHAVIOR;
D O I：
10.1016/j.proeng.2011.04.035
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Thermal barrier coatings (TBC) are used in gas turbines to protect metallic components from high temperature. In the present study adhesion tests have been conducted on APS TBC coated specimens subjected to different heat treatments. Isothermal and cyclic heat treatments have been conducted at temperatures around 1100 C and the adhesion have been tested using the method described in ASTM C633. The fracture surfaces resulting from the adhesion test have been investigated and the fracture behavior has been characterized. A difference in fracture mechanism between the three heat treatments has been found. The two cyclic heat treatments give fracture in the top coat/bond coat interface while isothermal heat treatment gives fracture in the top coat. (C) 2011 Published by Elsevier Ltd. Selection and peer-review under responsibility of ICM11
引用
收藏
页数：6
相关论文
共 50 条
  • [31] THERMAL BARRIER COATINGS FOR HEAT ENGINE COMPONENTS
    LEVINE, SR
    MILLER, RA
    HODGE, PE
    SAMPE QUARTERLY-SOCIETY FOR THE ADVANCEMENT OF MATERIAL AND PROCESS ENGINEERING, 1980, 12 (01): : 20 - 26
  • [32] Influence of creep and cyclic oxidation in thermal barrier coatings
    Seiler, Philipp
    Baeker, Martin
    Roesler, Joachim
    INTERNATIONAL JOURNAL OF MATERIALS RESEARCH, 2012, 103 (01) : 50 - 56
  • [33] Unsteady Thermal Stresses of Thermal Barrier Coatings under Cyclic Heating
    Suzuki K.
    Toyokawa H.
    Saji C.
    Yamazaki Y.
    Okumura T.
    Zairyo/Journal of the Society of Materials Science, Japan, 2023, 72 : 821 - 827
  • [34] Influence of Cyclic Thermal Loading on Fatigue Behavior of Thermal Barrier Coatings
    Vidyasagar, H. N.
    Prakash, S. Gopal
    Shivrudraiah
    Sharma, K. V.
    PROCEEDINGS OF WORLD ACADEMY OF SCIENCE, ENGINEERING AND TECHNOLOGY, VOL 26, PARTS 1 AND 2, DECEMBER 2007, 2007, 26 : 311 - 313
  • [35] Microstructure and mechanical properties of nanobainitic steel subjected to multiple isothermal heat treatments
    Liu, Ning
    Zhang, Xin
    Ding, Jing
    He, Jun
    Yin, Fu-xing
    JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL, 2018, 25 (10) : 1062 - 1067
  • [36] Microstructure and mechanical properties of nanobainitic steel subjected to multiple isothermal heat treatments
    Ning Liu
    Xin Zhang
    Jing Ding
    Jun He
    Fu-xing Yin
    Journal of Iron and Steel Research International, 2018, 25 : 1062 - 1067
  • [37] Fundamental coating development study to improve the isothermal oxidation resistance and thermal cycle durability of thermal barrier coatings
    Torigoe, Taiji
    Oguma, Hidetaka
    Okada, Ikuo
    Xu, Guochun
    Fujita, Kazuhisa
    Nakayama, Akira
    Maruyama, Toshiro
    Nishio, Kazumasa
    HIGH-TEMPERATURE OXIDATION AND CORROSION 2005, 2006, 522-523 : 247 - 253
  • [38] Effects of isothermal oxidation on microstructure and mechanical properties of thermal barrier coatings
    Liu, Y. Z.
    Hu, X. B.
    Zhu, Y. L.
    Wei, H.
    Dravid, Vinayak P.
    Zhang, W. W.
    CERAMICS INTERNATIONAL, 2019, 45 (07) : 8815 - 8823
  • [39] TEM analysis of the microstructure of thermal barrier coatings after isothermal oxidation
    Poza, P.
    Gomez-Garcia, J.
    Munez, C. J.
    ACTA MATERIALIA, 2012, 60 (20) : 7197 - 7206
  • [40] Influence of water vapor on the isothermal oxidation Behavior of thermal barrier coatings
    Zhou, CG
    Yu, JS
    Gong, SK
    Xu, HB
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2004, 20 (01) : 38 - 40
12345