Fractographic study of adhesion tested thermal barrier coatings subjected to isothermal and cyclic heat treatments

被引：6
|
作者：
Eriksson, R. [1 ]
Brodin, H. [1 ,2 ]
Johansson, S. [1 ]
Ostergren, L. [3 ]
Li, X. -H. [2 ]
机构：
[1] Linkoping Univ, Div Engn Mat, SE-58183 Linkoping, Sweden
[2] Siemens Ind Turbomachinery AB, SE-61283 Finspang, Sweden
[3] Volvo Aero Corp, SE-46181 Trollhattan, Sweden
来源：
11TH INTERNATIONAL CONFERENCE ON THE MECHANICAL BEHAVIOR OF MATERIALS (ICM11) | 2011年 / 10卷
关键词：
thermal barrier coatings; TBC; adhesion; fractography; thermal cycling fatigue; burner rig test; BOND STRENGTH; MECHANISMS; TOUGHNESS; BEHAVIOR;
D O I：
10.1016/j.proeng.2011.04.035
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Thermal barrier coatings (TBC) are used in gas turbines to protect metallic components from high temperature. In the present study adhesion tests have been conducted on APS TBC coated specimens subjected to different heat treatments. Isothermal and cyclic heat treatments have been conducted at temperatures around 1100 C and the adhesion have been tested using the method described in ASTM C633. The fracture surfaces resulting from the adhesion test have been investigated and the fracture behavior has been characterized. A difference in fracture mechanism between the three heat treatments has been found. The two cyclic heat treatments give fracture in the top coat/bond coat interface while isothermal heat treatment gives fracture in the top coat. (C) 2011 Published by Elsevier Ltd. Selection and peer-review under responsibility of ICM11
引用
收藏
页数：6
相关论文
共 50 条
  • [21] THERMAL BARRIER COATINGS FOR HEAT ENGINES
    BRINDLEY, WJ
    MILLER, RA
    JOURNAL OF METALS, 1988, 40 (07): : A64 - A65
  • [22] CYCLIC HOT CORROSION OF THERMAL BARRIER COATINGS AND OVERLAY COATINGS
    Eriksson, Robert
    Brodin, Hakan
    Johansson, Sten
    Ostergren, Lars
    Li, Xin-Hai
    PROCEEDINGS OF THE ASME TURBO EXPO: TURBINE TECHNICAL CONFERENCE AND EXPOSITION, 2013, VOL 4, 2013,
  • [23] Failure of Thermal Barrier Coatings Subjected to CMAS Attack
    Li, L.
    Hitchman, N.
    Knapp, J.
    JOURNAL OF THERMAL SPRAY TECHNOLOGY, 2010, 19 (1-2) : 148 - 155
  • [24] Failure of Thermal Barrier Coatings Subjected to CMAS Attack
    L. Li
    N. Hitchman
    J. Knapp
    Journal of Thermal Spray Technology, 2010, 19 : 148 - 155
  • [25] A comparative study of oxidation kinetics and thermal cyclic performance of thermal barrier coatings (TBCs)
    Karaoglanli, Abdullah Cahit
    Grund, Thomas
    Turk, Ahmet
    Lampke, Thomas
    SURFACE & COATINGS TECHNOLOGY, 2019, 371 : 47 - 67
  • [26] Thermal barrier coatings on aluminium-based alloy 2024 for high temperature protection subjected to thermal cyclic loading
    Kumar, Dipak
    Pandey, K. N.
    Das, Deepak Kumar
    INTERNATIONAL CONFERENCE ON ADVANCES IN MANUFACTURING AND MATERIALS ENGINEERING (ICAMME 2014), 2014, 5 : 1075 - 1080
  • [27] Improved sealing treatments for thick thermal barrier coatings
    Ahmaniemi, S
    Vuoristo, P
    Mäntylä, T
    SURFACE & COATINGS TECHNOLOGY, 2002, 151 : 412 - 417
  • [28] Adhesion strength of ceramic top coat in thermal barrier coatings subjected to thermal cycles: Effects of thermal cycle testing method and environment
    Okazaki, Masakazu
    Yamagishi, Satoshi
    Yamazaki, Yasuhiro
    Ogawa, Kazuhiro
    Waki, Hiroyuki
    Arai, Masayuki
    INTERNATIONAL JOURNAL OF FATIGUE, 2013, 53 : 33 - 39
  • [29] Adhesion of thermal barrier coatings - the development of metastable alumina
    Banks, JP
    Saunders, SRJ
    Chunnilall, CJ
    MATERIALS AT HIGH TEMPERATURES, 2000, 17 (02) : 225 - 229
  • [30] Microstructural evolution of thermal barrier coatings during isothermal oxidation
    Salazar, A.
    Gomez-Garcia, J.
    Poza, P.
    Utrilla, V.
    LAYERED, FUNCTIONAL GRADIENT CERAMICS, AND THERMAL BARRIER COATINGS: DESIGN, FABRICATION AND APPLICATIONS, 2007, 333 : 269 - +
12345