Sintered duplex stainless steels from premixes of 316L and 434L powders with Cr3C2 and CrB

被引：0
|
作者：
Datta, P [1 ]
Upadhyaya, GS [1 ]
机构：
[1] Indian Inst Technol, Dept Mat & Met Engn, Kanpur 208016, Uttar Pradesh, India
来源：
TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS | 2000年 / 53卷 / 06期
关键词：
D O I：
暂无
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
Duplex austenite-ferrite stainless steel with 8.6w/o (10 v/o) Cr3C2 and 2 w/o CrB were prepared from the premixes of 316L and 434L stainless steel atomized powders. Pronounced densification was observed after 1508K sintering in hydrogen. Commencement of liquid phase sintering was observed after 1508 K. Variation of hardness was found to be proportionate to densification, whereas coercivity in general decreased with increased sintering temperature. Corrosion resistance was found to depend on sintering temperature.
引用
收藏
页码：605 / 610
页数：6
相关论文
共 50 条
  • [31] Comparative Evaluation of Low Nickel and Nickel Free Lean Duplex Stainless Steels with 316L in a Variety of Corrosive Media
    Singhal, Lokesh Kumar
    Poojary, Prashant Thimmappa
    Kumar, Alok
    TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2013, 66 (01) : 25 - 31
  • [32] Experimental characterization of YAG and SiC added P/M ferritic (434L) stainless steel sintered in hydrogen (H2) atmosphere
    Nirala, Akhileshwar
    Kumar, Navneet
    Sharma, Sanjeev Kumar
    Yadav, Jeetendra Kumar
    Singh, Desh Bandhu
    Shrivastava, Anil Kumar
    MATERIALS TODAY-PROCEEDINGS, 2020, 28 : 2047 - 2052
  • [33] Tribological behaviour of sintered 316L stainless steel impregnated with MoS2 plain bearing
    Raadnui, Surapol
    Mahathanabodee, Sithipong
    Tongsri, Ruangdaj
    WEAR, 2008, 265 (3-4) : 546 - 553
  • [34] Formation of α-Al2O3 on 316L stainless steel
    Lin, Yuebin
    Dong, Yuwei
    Liu, Lei
    EMERGING MATERIALS RESEARCH, 2015, 4 (01) : 71 - 75
  • [35] Dislocation structures and residual stresses in duplex stainless steel fabricated by laser powder bed fusion with 430 and 316L powders
    Nie, Yu Jin
    Yang, Fei
    Meng, Li Xin
    Wang, Ying Zhi
    Yin, Lei
    Shi, Quan Xin
    Ma, Jin Yao
    Liang, Wei
    Zheng, Liu Wei
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2024, 914
  • [36] Dislocation structures in the bands of localised cyclic plastic strain in austenitic 316L and austenitic-ferritic duplex stainless steels
    Kruml, T
    Polak, J
    Obrtlik, K
    Degallaix, S
    ACTA MATERIALIA, 1997, 45 (12) : 5145 - 5151
  • [37] Grain boundary filmlike Fe–Mo–Cr phase in nitrogen-added type 316L stainless steels
    Yong Jun Oh
    Woo Seog Ryu
    Changmo Sung
    Il Hiun Kuk
    Jun Hwa Hong
    Journal of Materials Research, 1999, 14 : 390 - 397
  • [38] Magnetic properties of AISI 316L stainless steel doped with nanocrystalline Ti-B-C powders
    Bodziony, T.
    Kaczmarek, M.
    Tran, V. H.
    Figiel, P.
    Biedunkiewicz, A.
    Leniec, G.
    MATERIALS RESEARCH EXPRESS, 2018, 5 (12):
  • [39] A comparative H2S corrosion study of 304L and 316L stainless steels in acidic media
    Davoodi, A.
    Pakshir, M.
    Babaiee, M.
    Ebrahimi, G. R.
    CORROSION SCIENCE, 2011, 53 (01) : 399 - 408
  • [40] Comparison of grindability of HIPped austenitic 316L, duplex 2205 and super duplex 2507 and as-cast 304 stainless steels using alumina wheels
    Helsinki Univ of Technology, Espoo, Finland
    J Mater Process Technol, 1-3 (1-9):
12345