Sintered duplex stainless steels from premixes of 316L and 434L powders with Cr3C2 and CrB

被引：0

作者：

Datta, P ^{[1
]}

Upadhyaya, GS ^{[1
]}

机构：

[1] Indian Inst Technol, Dept Mat & Met Engn, Kanpur 208016, Uttar Pradesh, India

来源：

TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS | 2000年 / 53卷 / 06期

关键词：

D O I：

暂无

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

Duplex austenite-ferrite stainless steel with 8.6w/o (10 v/o) Cr3C2 and 2 w/o CrB were prepared from the premixes of 316L and 434L stainless steel atomized powders. Pronounced densification was observed after 1508K sintering in hydrogen. Commencement of liquid phase sintering was observed after 1508 K. Variation of hardness was found to be proportionate to densification, whereas coercivity in general decreased with increased sintering temperature. Corrosion resistance was found to depend on sintering temperature.

引用

页码：605 / 610

页数：6

共 50 条

[21] Electrochemical and Passive Layer Characterizations of 304L, 316L, and Duplex 2205 Stainless Steels in Thiosulfate Gold Leaching Solutions
Mohammadi, Maysam
Choudhary, Lokesh
Gadala, Ibrahim M.
Alfantazi, Akram
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2016, 163 (14) : C883 - C894
[22] CORROSION BEHAVIOR OF SINTERED 434L FERRITIC STAINLESS STEEL-AL2O3 COMPOSITES CONTAINING EARLY TRANSITION-METALS
MUKHERJEE, SK
UPADHYAYA, GS
MATERIALS CHEMISTRY AND PHYSICS, 1985, 12 (05) : 419 - 435
[23] Comparison of Hydrogen Embrittlement Resistance between 2205 Duplex Stainless Steels and type 316L Austenitic Stainless Steels Under the Cathodic Applied Potential
Seo, Dong-Il
Lee, Jae-Bong
CORROSION SCIENCE AND TECHNOLOGY-KOREA, 2016, 15 (05): : 237 - 244
[24] Experimental and numerical analysis about the cyclic behavior of the 304L and 316L stainless steels at 350 °C
Taleb, Lakhdar
Cailletaud, Georges
Sai, Kacem
INTERNATIONAL JOURNAL OF PLASTICITY, 2014, 61 : 32 - 48
[25] Microstructure and mechanical behaviour of single pressed and vacuum sintered gas and water atomised 316L stainless steel powders
Lindstedt, U
Karlsson, B
POWDER METALLURGY, 1998, 41 (04) : 261 - 268
[26] Study on the Corrosion Resistance Mechanism of Nitric Acid Passivation on 316L and SUS329J3L Duplex Stainless Steels in a Denitrification Agent
Dong, Yuanneng
Zhang, Jinling
Yu, Yanchong
Yang, Fanxi
Pan, Jie
Wang, Shebin
LANGMUIR, 2025, 41 (11) : 7669 - 7683
[27] SINTERING OF 434L FERRITIC STAINLESS-STEEL CONTAINING AL2O3 PARTICLES
MUKHERJEE, SK
UPADHYAYA, GS
INTERNATIONAL JOURNAL OF POWDER METALLURGY, 1983, 19 (04): : 289 - 298
[28] SINTERING OF 434L FERRITIC STAINLESS STEEL CONTAINING Al2O3 PARTICLES.
Mukherjee, S.K.
Upadhyaya, G.S.
The International journal of powder metallurgy & powder technology, 1983, 19 (04): : 289 - 298
[29] Cr3C2对激光选区熔化316L合金组织及力学性能的影响
斯松华
郑孟勤
徐震霖
雷进
严敏容
表面技术, 2024, 53 (03) : 191 - 199
[30] Comparative Evaluation of Low Nickel and Nickel Free Lean Duplex Stainless Steels with 316L in a Variety of Corrosive Media
Lokesh Kumar Singhal
Prashant Thimmappa Poojary
Alok Kumar
Transactions of the Indian Institute of Metals, 2013, 66 : 25 - 31

← 1 2 3 4 5 →