Enhancement of coercivity for Nd-Fe-B thin films by the infiltration of Nd-Cu alloy cap layer

被引：21
|
作者：
Sato, T. [2 ]
Oka, N. [1 ]
Ohsuna, T. [2 ]
Kaneko, Y. [2 ]
Suzuki, S. [1 ]
Shima, T. [1 ]
机构：
[1] Tohoku Gakuin Univ, Fac Engn, Tagajo, Miyagi 9858537, Japan
[2] Toyota Cent Res & Dev Labs Inc, Nagakute, Aichi 4801192, Japan
来源：
JOURNAL OF APPLIED PHYSICS | 2011年 / 110卷 / 02期
关键词：
PERMANENT-MAGNETS;
D O I：
10.1063/1.3608244
中图分类号：
O59 [应用物理学];
学科分类号：
摘要：
In order to understand the mechanism of coercivity (H-c) of Nd-Fe-B magnets, we have investigated the effect of thermal annealing treatment on Nd-Fe-B thin films with Nd-Cu alloy cap layers. A substantial enhancement of H-c from 19.0 kOe (1512 kAm(-1)) to 26.1 kOe (2078 kAm(-1)) was obtained for the Nd-Fe-B/Nd36Cu64 films after post-annealing at 400 degrees C. Through electron microscope observation, it was revealed that Nd and Cu enrichment is clearly observed in the grain boundary of the Nd-Fe-B layer, whereas the concentration of Fe was decreased there. These results suggest that the exchange coupling between Nd2Fe14B grains is weakened by the infiltration of a non-magnetic element into the grain boundary after the optimum thermal annealing treatment. (C) 2011 American Institute of Physics. [doi: 10.1063/1.3608244]
引用
收藏
页数：4
相关论文
共 50 条
  • [41] Overview of Nd-Fe-B magnets and coercivity
    Fidler, J
    Schrefl, T
    [J]. JOURNAL OF APPLIED PHYSICS, 1996, 79 (08) : 5029 - 5034
  • [42] NOTE ON THE COERCIVITY IN ND-FE-B MAGNETS
    GROSSINGER, R
    KREWENKA, R
    KIRCHMAYR, HR
    NAASTEPAD, P
    BUSCHOW, KHJ
    [J]. JOURNAL OF THE LESS-COMMON METALS, 1987, 134 (02): : L17 - L21
  • [43] Overview of Nd-Fe-B magnets and coercivity
    [J]. J Appl Phys, 8 pt 2A (5029):
  • [44] High-coercivity hot-deformed Nd-Fe-B permanent magnets processed by Nd-Cu eutectic diffusion under expansion constraint
    Akiya, T.
    Liu, J.
    Sepehri-Amin, H.
    Ohkubo, T.
    Hioki, K.
    Hattori, A.
    Hono, K.
    [J]. SCRIPTA MATERIALIA, 2014, 81 : 48 - 51
  • [45] Microstructure and coercivity mechanism of highly textured Nd-Fe-B films
    Hannemann, U
    Melcher, S
    Neu, V
    Fähler, S
    Holzapfel, B
    Schultz, L
    [J]. IEEE TRANSACTIONS ON MAGNETICS, 2003, 39 (05) : 2726 - 2728
  • [46] Reduction of crystallization temperature of the Nd-Fe-B thin films by Cu addition
    Ma, YG
    Yang, Z
    Matsumoto, M
    Morisako, A
    Takei, S
    [J]. MATERIALS SCIENCE AND ENGINEERING B-SOLID STATE MATERIALS FOR ADVANCED TECHNOLOGY, 2004, 110 (02): : 190 - 194
  • [47] Microstructure evolution and coercivity enhancement in Nd-Fe-B thin films diffusion-processed by R-Al alloys (R=Nd, Pr)
    Xie, Yigao
    Yang, Yang
    Zhang, Tongbo
    Fu, Yanqing
    Jiang, Qingzheng
    Ma, Shengcan
    Zhong, Zhenchen
    Cui, Weibin
    Wang, Qiang
    [J]. AIP ADVANCES, 2018, 8 (05)
  • [48] MICRO PATTERNING OF THIN ND-FE-B FILMS
    LEMKE, H
    LANG, T
    GODDENHENRICH, T
    HEIDEN, C
    [J]. JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 1995, 148 (03) : 426 - 432
  • [49] Enhancement of Coercivity in Sintered Nd-Fe-B Magnets by Grain-Boundary Diffusion of Electrodeposited Cu-Nd Alloys
    Lee, Sangjun
    Kwon, Jeehye
    Cha, Hee-Ryoung
    Kim, Kyung Min
    Kwon, Hae-Woong
    Lee, Junggoo
    Lee, Dongyun
    [J]. METALS AND MATERIALS INTERNATIONAL, 2016, 22 (02) : 340 - 344
  • [50] Enhancement of coercivity in sintered Nd-Fe-B magnets by grain-boundary diffusion of electrodeposited Cu-Nd Alloys
    Sangjun Lee
    Jeehye Kwon
    Hee-Ryoung Cha
    Kyung Min Kim
    Hae-Woong Kwon
    Junggoo Lee
    Dongyun Lee
    [J]. Metals and Materials International, 2016, 22 : 340 - 344
12345