Experimental Confirmation of Ni5Al3 Phase in Ni-Al Binary System by Diffusion Couple Technique

被引：0
|
作者：
Li Changfa [1 ]
Ren Yuping [2 ]
Qin Gaowu [2 ]
机构：
[1] Tianjin Univ Technol, Sch Mat Sci & Engn, Tianjin 300384, Peoples R China
[2] Northeastern Univ, Key Lab Anisotropy & Mat MOE, Shenyang 110004, Peoples R China
来源：
MATERIALS AND MANUFACTURING, PTS 1 AND 2 | 2011年 / 299-300卷
关键词：
Ni-Al binary system; Diffusion couple technique; Ni5Al3; Phase diagram; SHAPE-MEMORY ALLOY; INTERMETALLIC COMPOUNDS;
D O I：
10.4028/www.scientific.net/AMR.299-300.224
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The equilibrium phase relationships and compositions of Ni - 51at.%Al/Ni - 26at.%Al diffusion couple heat treated at 650 degrees C for various times have been investigated by means of diffusion couple technique. Experimental results showed that Ni5Al3 phase was not only stable at 650 degrees C, but also had a large solubility range (45.3 similar to 40.6) at.% Al. The obtained relationships of NiAl/Ni5Al3 and Ni5Al3/Ni3Al are in accordance with the current generally accepted Ni-Al binary system phase diagram, but their composition ranges are quite different from the presently accepted one, that is, the the phase boundaries of NiAl / (Ni5Al3 + NiAl), (Ni5Al3 + NiAl) / Ni5Al3 and Ni5Al3 / (Ni3Al + Ni5Al3) significantly shift to the Al-rich side.
引用
收藏
页码：224 / +
页数：2
相关论文
共 50 条
  • [31] Microscopic phase-field simulation for Ni3Al precipitation in Ni-Al alloy
    Lu, Yanli
    Chen, Zheng
    Li, Yongsheng
    Wang, Yongxin
    Jinshu Xuebao/Acta Metallurgica Sinica, 2007, 43 (03): : 291 - 296
  • [32] Microscopic phase-field simulation for Ni3Al pricipitation in Ni-Al alloy
    Lu Yanli
    Chen Zheng
    Li Yongsheng
    Wang Yongxin
    ACTA METALLURGICA SINICA, 2007, 43 (03) : 291 - 296
  • [33] A thermodynamic analysis of the Ni-Al system
    Huang, W
    Chang, YA
    INTERMETALLICS, 1998, 6 (06) : 487 - 498
  • [34] PERITECTIC FORMATION IN THE NI-AL SYSTEM
    LEE, JH
    VERHOEVEN, JD
    JOURNAL OF CRYSTAL GROWTH, 1994, 144 (3-4) : 353 - 366
  • [35] EUTECTIC FORMATION IN THE NI-AL SYSTEM
    LEE, JH
    VERHOEVEN, JD
    JOURNAL OF CRYSTAL GROWTH, 1994, 143 (1-2) : 86 - 102
  • [36] NI-AL AND NI-TA PHASE-DIAGRAMS
    NASH, P
    WEST, DRF
    METAL SCIENCE, 1983, 17 (02): : 99 - 100
  • [37] Effects of Solidification Kinetics on the Phase Composition in Ni-Al System
    SHEN Ning-fu
    LIANG Chang-hao
    LI Jian-qiang
    WANG Xi-ke
    SHI Guang-xin (Research Center for Materials
    Zhengzhou University of Technology
    Zhengzhou 450002
    China)
    郑州工业大学学报 , 2000, (02) : 1 - 8
  • [38] ORDERING AND INSTABILITY OF BETA-PHASE IN NI-AL SYSTEM
    ARKHANGELSKAYA, AA
    LITVINOV, VS
    POLEVA, VV
    FIZIKA METALLOV I METALLOVEDENIE, 1979, 48 (06): : 1256 - 1261
  • [39] Phase Composition and Structure of Multilayered Coatings of Ni-Al System
    Fedorischeva, Marina V.
    Sergeev, Victor P.
    Kalashnikov, Mark P.
    Voronov, Andrei V.
    Bozhko, Irina A.
    INTERNATIONAL CONFERENCE ON PHYSICAL MESOMECHANICS OF MULTILEVEL SYSTEMS 2014, 2014, 1623 : 155 - 158
  • [40] Thermal conductivity mapping of the Ni-Al system and the beta-NiAl phase in the Ni-Al-Cr system
    Zhao, Ji-Cheng
    Zheng, Xuan
    Cahill, David G.
    SCRIPTA MATERIALIA, 2012, 66 (11) : 935 - 938
12345